Summary
The reaction of the carboxymethyl cellulose sodium salt (Na-CMC) (degrees of substitution (DS) = 1.2) with N-hydroxysuccinimide (Su-OH) in the presence of 1-hydroxybenzotriazole and 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC) was carried out in water to obtain the Su-OH ester of carboxymethyl cellulose, Su-CMC, with the DS values of 0.19 – 1.04. N-Allylcarbamoylmethyl cellulose (Allyl-CMC), which was prepared from the reaction of Su-CMC with an excess amount of allylamine, was crosslinked by UV-irradiation. In addition, the photocrosslinked Allyl-CMC film was swollen with water to form a hydrogel having a relatively high water-swelling property, e.g., the degree of swelling (ds) was ca. 360% for Allyl-CMC with the DS of 0.93.
Similar content being viewed by others
References
Wagenknecht W, Nehls I, Philipp B (1992) Carbohydr Res 237:211.
Edgar KJ, Buchanan CM, Debenham JS, Rundquist PA, Seiler BD, Shelton MC, Tindall D (2001) Prog Polym Sci 26:1605.
McCormick CL, Dawsey TR (1990) Macromolecules 23:3606.
McCormick CL, Callais PA (1987) Polymer 28:2317.
Isogai A, Ishizu A, Nakano J, Eda S, Kato K (1985) Carbohydr Res 138:99.
Isogai A, Ishizu A, Nakano J (1986) J Appl Polym Sci 31:341.
Isogai A, Ishizu A, Nakano J (1984) J Appl Polym Sci 29:2097.
Mornann W, Michel U (2002) Carbohydr Polym 50:201.
Hearon WM, Hiatt GD, Fordyce CR (1943) J Am Chem Soc 65:829.
Heinze T, Liebert T (2001) Prog Polym Sci 26:1689.
Olaru N, Olaru L, Stoleriu A, Timpu D (1998) J Appl Polym Sci 67:481.
Barbucci R, Leone G, Vecchiullo A (2004) J Biomater Sci Polymer Edn 15:607.
Carrigan SD, Scott G, Tabrizian M (2005) Langmuir 21:5966.
Hara K, Iida M, Yano K, Nishida T (2004) Colloid Surf B: Biointerfaces 38:227.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shen, X., Kitajyo, Y., Duan, Q. et al. Synthesis and Photocrosslinking Reaction of N-Allylcarbamoylmethyl Cellulose Leading to Hydrogel. Polym. Bull. 56, 137–143 (2006). https://doi.org/10.1007/s00289-005-0482-2
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00289-005-0482-2