Deposition of Stellite 6 alloy on steel substrates using wire and arc additive manufacturing

The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Cite this article

Abstract

Stellite 6 is a cobalt-based superalloy which has a good wear and corrosion resistance and retains these properties at high temperatures. In this study, wire and arc additive manufacturing (WAAM based on the GMAW) was employed to deposit Stellite 6 wire on low alloy high strength steel (S355) and stainless steel (AISI 420) plates. One of the main interests of this study is to produce WAAM Stellite 6 deposits with quality comparable with laser deposition. The advantages of the WAAM process include the high deposition rate, high productivity, high material usage, and energy efficiency with low cost. However, superalloy deposition generally requires maintaining a low dilution level to avoid jeopardizing the integrity of the deposit. As a result, it is important to manage the excess heat input during the WAAM deposition process through a parametric optimization of WAAM deposition of Stellite 6 on S355 steel substrates. In this study, a WAAM process window is established to guide the process optimization. The optimization method used in this study has been applied in our previous laser cladding work. The generated process window also shows some correlations among the heat input, bead geometry, and dilution. The effects of heat input on the resulting microstructure, elemental distribution, and hardness were discussed. Dilution, microstructure, and hardness were considered for comparison from previous studies of laser cladding deposits. In addition, the obtained optimal conditions were adapted to apply WAAM deposition of Stellite 6 layers on AISI 420 stainless steel substrates. The XRD result shows that WAAM deposits contain Co-Cr-Fe solid solution (FCC), Cr7C3 and Cr3C2 carbides, and Co4W2C intermetallic compound. The results obtained through this study lay a foundation for future research on the wear properties of WAAM Stellite 6 deposits. This can contribute to further development of automated deposition of Stellite 6 using WAAM process for industrial applications.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11.
Fig. 12
Fig. 13
Fig. 14
Fig. 15

References

  1. Yangtao X, Tiandong X, Yanling H (2009) Microstructures comparison of Stellite 6 alloy by self-propagating high-temperature synthesis and cast HS111 alloy. Rare Metal Mater Eng 38(8):1333–1337

    Google Scholar 

  2. Derow H., & Bleil HE (1970) Elevated temperature instability of Stellite 6B (Vol. 1590). National Aeronautics and Space Administration.

  3. Zangeneh S, Farhangi H (2010) Influence of service-induced microstructural changes on the failure of a cobalt-based superalloy first stage nozzle. Mater Des 31(7):3504–3511

    Google Scholar 

  4. Marques FP, Scandian C, Bozzi AC, Fukumasu NK, Tschiptschin AP (2017) Formation of a nanocrystalline recrystallized layer during microabrasive wear of a cobalt-chromium based alloy (Co-30Cr-19Fe). Tribol Int 116:105–112

    Google Scholar 

  5. Rebouças Filho PP, da Silveira Cavalcante T, de Albuquerque VHC, Tavares JMR, & Cortez PC (2009) Measurement of welding dilution from images using active contours. In SEECCM 2009-2nd South-East European Conference on Computational Mechanics.

  6. Kuzucu V, Ceylan M, Celik H, Aksoy I (1997) Microstructure and phase analyses of Stellite 6 plus 6 wt.% Mo alloy. J Mater Process Technol 69(1-3):257–263

    Google Scholar 

  7. Ya W, Pathiraj B, Matthews DT, Bright M, Melzer S (2018) Cladding of Tribaloy T400 on steel substrates using a high power Nd: YAG laser. Surf Coat Technol 350:323–333

    Google Scholar 

  8. Gholipour A, Shamanian M, Ashrafizadeh F (2011) Microstructure and wear behavior of stellite 6 cladding on 17-4 PH stainless steel. J Alloys Compd 509(14):4905–4909

    Google Scholar 

  9. Malayoglu U, Neville A, Lovelock H (2005) Assessing the kinetics and mechanisms of corrosion of cast and HIPed Stellite 6 in aqueous saline environments. Corros Sci 47(8):1911–1931

    Google Scholar 

  10. Sidhu TS, Prakash S, Agrawal RD (2006) Studies of the metallurgical and mechanical properties of high velocity oxy-fuel sprayed stellite-6 coatings on Ni-and Fe-based superalloys. Surf Coat Technol 201(1-2):273–281

    Google Scholar 

  11. Opris CD, Liu R, Yao MX, Wu XJ (2007) Development of Stellite alloy composites with sintering/HIPing technique for wear-resistant applications. Mater Des 28(2):581–591

    Google Scholar 

  12. Sidhu BS, Puri D, Prakash S (2005) Mechanical and metallurgical properties of plasma sprayed and laser remelted Ni–20Cr and Stellite-6 coatings. J Mater Process Technol 159(3):347–355

    Google Scholar 

  13. Ya W, Pathiraj B (2018) Residual stresses in Stellite 6 layers cladded on AISI 420 steel plates with a Nd: YAG laser. J Laser Appl 30(3):032007

    Google Scholar 

  14. Ya, W. (2015). Laser materials interactions during cladding: analyses on clad formation, thermal cycles, residual stress and defects.

    Google Scholar 

  15. Heralić A, Christiansson AK, Ottosson M, Lennartson B (2010) Increased stability in laser metal wire deposition through feedback from optical measurements. Opt Lasers Eng 48(4):478–485

    Google Scholar 

  16. Sun S, Durandet Y, Brandt M (2005) Parametric investigation of pulsed Nd: YAG laser cladding of stellite 6 on stainless steel. Surf Coat Technol 194(2-3):225–231

    Google Scholar 

  17. Brandt M, Sun S, Alam N, Bendeich P, Bishop A (2009) Laser cladding repair of turbine blades in power plants: from research to commercialisation. Int Heat Treat Surf Eng 3(3):105–114

    Google Scholar 

  18. Piasecki ADAM, Bartkowski DARIUSZ, Młynarczyk A, Dudziak A, Gościański M, Kasprowiak MONIKA (2013) Laser cladding of Stellite 6 on low carbon steel for repairing components in automotive applications using disk laser. Arch Mech Technol Autom 33(2):25–34

    Google Scholar 

  19. Sarafan S, Wanjara P, Champliaud H, Thibault D (2015) Characteristics of an autogenous single pass electron beam weld in thick gage CA6NM steel. Int J Adv Manuf Technol 78(9-12):1523–1535

    Google Scholar 

  20. Hemmati, I., Ocelík, V., & De Hosson, J. T. M. (2015). Compositional modification of Ni-base alloys for laser-deposition technologies. In Laser Surface Engineering (pp. 137-162). Woodhead Publishing.

  21. Ya W, & Hamilton K (2017) On-demand spare parts for the marine industry with directed energy deposition: propeller use case. In International Conference on Additive Manufacturing in Products and Applications (pp. 70-81). Springer, Cham.

  22. Sarathchandra DT, Davidson MJ, Visvanathan G (2020) Parameters effect on SS304 beads deposited by wire arc additive manufacturing. Mater Manuf Process 35(7):852–858

    Google Scholar 

  23. Li Z, Cui Y, Wang J, Liu C, Wang J, Xu T et al (2019) Characterization of microstructure and mechanical properties of Stellite 6 part fabricated by wire arc additive manufacturing. Metals 9(4):474

    Google Scholar 

  24. Busachi A, Erkoyuncu J, Colegrove P, Martina F, Watts C, Drake R (2017) A review of additive manufacturing technology and cost estimation techniques for the defence sector. CIRP J Manuf Sci Technol 19:117–128

    Google Scholar 

  25. Williams SW, Martina F, Addison AC, Ding J, Pardal G, Colegrove P (2016) Wire+ arc additive manufacturing. Mater Sci Technol 32(7):641–647

    Google Scholar 

  26. Murr LE, Gaytan SM, Ceylan A, Martinez E, Martinez JL, Hernandez DH et al (2010) Characterization of titanium aluminide alloy components fabricated by additive manufacturing using electron beam melting. Acta Mater 58(5):1887–1894

    Google Scholar 

  27. Kim TB, Yue S, Zhang Z, Jones E, Jones JR, Lee PD (2014) Additive manufactured porous titanium structures: through-process quantification of pore and strut networks. J Mater Process Technol 214(11):2706–2715

    Google Scholar 

  28. Gardner L, Kyvelou P, Herbert G, Buchanan C (2020) Testing and initial verification of the world’s first metal 3D printed bridge. J Constr Steel Res 172:106233

    Google Scholar 

  29. Lange J, Feucht T, Erven M (2020) 3D printing with steel: additive Manufacturing for connections and structures. Steel Construction 13(3):144–153

    Google Scholar 

  30. Laghi V, Palermo M, Gasparini G, & Trombetti T (2020) Computational design and manufacturing of a half-scaled 3D-printed stainless steel diagrid column. Addit Manuf, 101505.

  31. Meboldt M, Klahn C. (Eds.). (2017) Industrializing additive manufacturing-proceedings of additive manufacturing in products and applications-AMPA2017. Springer

  32. Bahrin MAK, Othman MF, Azli NHN, & Talib MF (2016) Industry 4.0: a review on industrial automation and robotic. Jurnal Teknologi, 78(6-13).

  33. Martina F, Ding J, Williams S, Caballero A, Pardal G, Quintino L (2019) Tandem metal inert gas process for high productivity wire arc additive manufacturing in stainless steel. Addit Manuf 25:545–550

    Google Scholar 

  34. Pickin CG, Young K, Tuersley I (2007) Joining of lightweight sandwich sheets to aluminium using self-pierce riveting. Mater Des 28(8):2361–2365

    Google Scholar 

  35. Watanabe T, Takayama H, Yanagisawa A (2006) Joining of aluminum alloy to steel by friction stir welding. J Mater Process Technol 178(1-3):342–349

    Google Scholar 

  36. McCaw RL (1979) Plasma ARC welding of high-performance-ship materials. David W Taylor Naval ship research and development center annapolis md ship materials engineering dept.

  37. Muncaster PW (1991) A practical guide to TIG (GTA) welding. Elsevier

  38. Sweet LM (1985) Sensor-based control systems for arc welding robots. Robot Comput Integr Manuf 2(2):125–133

    Google Scholar 

  39. Bhagi LK, Gupta P, Rastogi V (2013) Fractographic investigations of the failure of L-1 low pressure steam turbine blade. case studies in. Eng Fail Anal 1(2):72–78

    Google Scholar 

  40. Ahmad M, Schatz M, Casey MV (2013) Experimental investigation of droplet size influence on low pressure steam turbine blade erosion. Wear 303(1-2):83–86

    Google Scholar 

  41. Ya W, Pathiraj B, Liu S (2016) 2D modelling of clad geometry and resulting thermal cycles during laser cladding. J Mater Process Technol 230:217–232

    Google Scholar 

  42. Ya W, Hernández-Sánchez JF, Pathiraj B, & Veld AHIT (2013) A study on attenuation of a Nd: YAG laser power by co-axial and off-axial nozzle powder stream during cladding. In International Congress on Applications of Lasers & Electro-Optics (Vol. 2013, No. 1, pp. 453-462). Laser Institute of America.

  43. Dinovitzer M, Chen X, Laliberte J, Huang X, Frei H (2019) Effect of wire and arc additive manufacturing (WAAM) process parameters on bead geometry and microstructure. Addit Manuf 26:138–146

    Google Scholar 

  44. Abe T, Sasahara H (2019) Layer geometry control for the fabrication of lattice structures by wire and arc additive manufacturing. Addit Manuf 28:639–648

    Google Scholar 

  45. de Oliveira UOB (2007) Laser treatment of alloys: processing, microstructure and structural properties. University Library Groningen][Host].

  46. Lin Z, Goulas C, Ya W, Hermans MJ (2019) Microstructure and mechanical properties of medium carbon steel deposits obtained via wire and arc additive manufacturing using metal-cored wire. Metals 9(6):673

    Google Scholar 

  47. Hashmi S (2014) Comprehensive materials processing. Newnes

  48. Schneider MF, & Schneider MF (1998) Laser cladding with powder.

    Google Scholar 

  49. Webb CE, & Jones JD (Eds.). (2004) Handbook of laser technology and applications: laser design and laser systems (Vol. 2). CRC Press

  50. DuPont JN, Marder AR (1995) Thermal efficiency of arc welding processes. Welding Journal-Including Welding Research Supplement 74(12):406 s

    Google Scholar 

  51. Kumar S, Shahi AS (2011) Effect of heat input on the microstructure and mechanical properties of gas tungsten arc welded AISI 304 stainless steel joints. Mater Des 32(6):3617–3623

    Google Scholar 

  52. Khromchenko FA, Lappa VA, Fedina IV, Karev AN, Dolzhanskii PR (1999) Technology of repairing working blades of steam turbines. Part 1. Repair by the method of deposition of high-Cr alloys. Weld Int 13(5):405–408

    Google Scholar 

  53. Ferozhkhan MM, Duraiselvam M, Ravibharath R (2016) Plasma transferred arc welding of Stellite 6 alloy on stainless steel for wear resistance. Procedia Technology 25:1305–1311

    Google Scholar 

  54. Kusmoko A, Dunne DP, Li H, & Nolan DJ (2013) Deposition of Stellite 6 on nickel superalloy and mild steel substrates with laser cladding

    Google Scholar 

  55. Yan F, Xiong W, Faierson EJ (2017) Grain structure control of additively manufactured metallic materials. Materials 10(11):1260

    Google Scholar 

  56. Houdková ?árka, Pala Z, Smazalová Eva, Vost?ák, Marek, & ?esánek, Zdeněk. (2016) Microstructure and sliding wear properties of hvof sprayed, laser remelted and laser clad stellite 6 coatings. Surface and Coatings Technology, S0257897216308817.

  57. Xu G, Kutsuna M, Liu Z, Yamada K (2006) Comparison between diode laser and tig cladding of co-based alloys on the sus403 stainless steel. Surf Coat Technol 201(3-4):1138–1144

    Google Scholar 

  58. Silwal B, Walker J, West D (2019) Hot-wire GTAW cladding: inconel 625 on 347 stainless steel. Int J Adv Manuf Technol 102(9-12):3839–3848

    Google Scholar 

  59. Valsecchi B, Previtali B, Gariboldi E (2012) Fibre laser cladding of turbine blade leading edges: the effect of specific energy on clad dilution. Int J Struct Integ 3(4):377–395

    Google Scholar 

Download references

Acknowledgments

The authors would like to express sincere gratitude and thank all researchers from Delft University of Technology, University of Twente and RAMLAB who provided valuable supports and inputs to the project.

Funding

This research was carried out under the master graduation project of the Delft University of Technology in collaboration with the Rotterdam Fieldlab Additive Manufacturing BV. (RAMLAB). Dr. Constantinos Goulas was funded by the Dutch organization for scientific research (NWO-Nederlandse Organisatie voor Wetenschappelijk Onderzoek) in the framework of project GradWAAM, Project Number S16043. A special thanks to Mr. Vincent Wegener, Managing Director, RAMLAB to provide financial support for this project.

Author information

Authors and Affiliations

  1. Rotterdam Additive Manufacture Fieldlab (RAMLAB), Scheepsbouwweg 8 F6, 3089JW, Rotterdam, The Netherlands

    Zidong Lin, Wei Ya, Vignesh Venkata Subramanian, Constantinos Goulas & Benedetto di Castri

  2. Department of Materials Science and Engineering, Delft University of Technology, Mekelweg 2, 2628CD, Delft, The Netherlands

    Zidong Lin, Constantinos Goulas & Marcel J. M. Hermans

  3. Faculty of Engineering Technology, Department of Mechanics of Solids, Surfaces & Systems (MS3), Chair of Laser Processing, University of Twente, P.O. Box 217, 7500AE, Enschede, The Netherlands

    Wei Ya & Belavendram Pathiraj

Authors
  1. Zidong Lin
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Wei Ya
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Vignesh Venkata Subramanian
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Constantinos Goulas
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Benedetto di Castri
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Marcel J. M. Hermans
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Belavendram Pathiraj
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Zidong Lin.

Additional information

Publisher’s note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Lin, Z., Ya, W., Subramanian, V.V. et al. Deposition of Stellite 6 alloy on steel substrates using wire and arc additive manufacturing. Int J Adv Manuf Technol 111, 411–426 (2020). https://doi.org/10.1007/s00170-020-06116-w

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-020-06116-w

Keywords

search

Navigation