Investigation on the structure, cross-link, and oxidation index of ultra high molecular weight polyethylene acetabular liners

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

In this work, we proposed a set of techniques and respective methodologies to investigate the physicochemical properties of six models of ultra high molecular weight polyethylene (UHMWPE) acetabular liners commercially available. The correlation between chemical properties, sterilization techniques, and potential performance of material were proposed. Optical microscopy, density, Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), and swell test were employed to evaluate the medical product and manufacturing process safety characteristics. Microscopy demonstrated that all samples went through a satisfactory consolidation process. FTIR revealed that only three models were not exposed to gamma irradiation, and consequently were not cross-linked. On the other hand, three other samples were exposed to gamma irradiation in which on presented an elevated oxidation index. This result was further investigated through the packaging evaluation where it was found that the sample with higher IOX was exposed to an oxygen atmosphere during sterilization and/or shelf life. Samples exposed to sterilization technique in atmosphere with oxygen were observed to have higher oxidation indexes, which are associated with material degradation in vivo. This work demonstrated the relevance of combining specific physicochemical techniques for process mapping and to characterize UHMWPE acetabular liners.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Australian Orthopaedic Association (2016) Annu Rep:2016

  2. Kumar CN, Arora GNC, Datta CB (2014) Bearing surfaces in hip replacement e evolution and likely future. Med J Armed Forces India 70:371–376. https://doi.org/10.1016/j.mjafi.2014.04.015

    Article  Google Scholar 

  3. Bracco P, Oral E (2011) Vitamin E-stabilized UHMWPE for total joint implants: a review. Clin Orthop Relat Res 469:2286–2293. https://doi.org/10.1007/s11999-010-1717-6

    Article  Google Scholar 

  4. Manning DW, Chiang PP, Martell JM, Galante JO, Harris WH (2005) In vivo comparative wear study of traditional and highly cross-linked polyethylene in total hip arthroplasty. J Arthroplast 20:880–886. https://doi.org/10.1016/j.arth.2005.03.033

    Article  Google Scholar 

  5. Sobieraj MC, Rimnac CM (2008) Ultra high molecular weight polyethylene: mechanics, morphology, and clinical behavior. J Mech Behav Biomed Mater 2:433–443. https://doi.org/10.1016/j.jmbbm.2008.12.006

    Article  Google Scholar 

  6. McKellop H, Shen FW, Lu B, Campbell P, Salovey R (2000) Effect of sterilization method and other modifications on the wear resistance of acetabular cups made of ultra-high molecular weight polyethylene. A hip-simulator study. J Bone Joint Surg Am 82–A:1708–1725

    Article  Google Scholar 

  7. Medel FJ, Peña P, Cegoñino J, Gómez-Barrena E, Puértolas JA (2007) Comparative fatigue behavior and toughness of remelted and annealed highly crosslinked polyethylenes. J Biomed Mater Res Part B Appl Biomater 83B:380–390. https://doi.org/10.1002/jbm.b.30807

    Article  Google Scholar 

  8. ASTMs F2759 - Standard guide for assessment of the ultra high molecular weight polyethylene ( UHMWPE ) Used in orthopedic and spinal 2017:1–6. doi:https://doi.org/10.1520/F2759-11.2

  9. Fulin P, Pokorny D, Slouf M, Nevoralova M, Vackova T, Dybal J, Pilar J (2014) Quantification of structural changes of UHMWPE components in total joint replacements. BMC Musculoskelet Disord 15:1–8. https://doi.org/10.1186/1471-2474-15-109

    Article  Google Scholar 

  10. ASTM D792. Standard test methods for density and specific gravity ( relative density ) of plastics 2013:1–6. doi:https://doi.org/10.1520/D0792-13.2

  11. American Society for Testing and Materials (2013) ASTM F2102 - 13 - Standard guide for evaluating the extent of oxidation in polyethylene fabricated forms intended for surgical implants. ASTM Stand:1–4. https://doi.org/10.1520/F2102-13.2

  12. ASTM F2381. ASTM F2381 - Standard test method for evaluating trans-vinylene yield in irradiated ultra-high molecular weight polyethylene fabricated forms intended for surgical implants by infrared spectroscopy 1. Astm 2015;i:1–5. doi:https://doi.org/10.1520/F2381-10.2

  13. American Society for Testing and Materials (2016) ASTM F2625 - 10 - Standard test method for measurement of enthalpy of fusion , percent crystallinity , and melting point of ultra-high-molecular weight polyethylene by means of differential scanning calorimetry. ASTM Stand:7–10. https://doi.org/10.1520/F2625-07.2

  14. D2765 A (2001) ASTM D2765 - standard test methods for determination of gel content and swell ratio of. Test 09:1–10. https://doi.org/10.1520/D2765-01R06

    Google Scholar 

  15. ASTM F648 (2014) F648-14 standard specification for ultra-high-molecular-weight polyethylene powder and fabricated form for surgical implants. ASTM:1096–1102. https://doi.org/10.1520/F0648-14.2

  16. Costa L, Luda MP, Trossarelli L, Brach Del Prever EM, Crova M, Gallinaro P (1998) Oxidation in orthopaedic UHMWPE sterilized by gamma-radiation and ethylene oxide. Biomaterials 19:659–668. https://doi.org/10.1016/S0142-9612(97)00160-9

    Article  Google Scholar 

  17. (2005) Microstructure changes of extruded ultra high molecular weight polyethylene after gamma irradiation and shelf-aging. Polym Degrad Stab 88:435–443. https://doi.org/10.1016/J.POLYMDEGRADSTAB.2004.11.015

  18. Kurtz SM (2004) The UHMWPE handbook, 1st edn. Elsevier, San Diego

    Google Scholar 

  19. Gao P, Cheung K, Leung TY (1996) Effects of compaction pressure on cohesive strength and chain mobility of low- temperature compacted nascent UHMWPE. Po 37:3265–3272

    Google Scholar 

  20. Ansari F, Ries MD, Pruitt L (2016) Effect of processing, sterilization and crosslinking on UHMWPE fatigue fracture and fatigue wear mechanisms in joint arthroplasty. J Mech Behav Biomed Mater 53:329–340. https://doi.org/10.1016/j.jmbbm.2015.08.026

    Article  Google Scholar 

  21. Shen F-W, Yu Y-J, McKellop H (1999) Potential errors in FTIR measurement of oxidation in ultrahigh molecular weight polyethylene implants. J Biomed Mater Res 48:203–210. https://doi.org/10.1002/(SICI)1097-4636(1999)48:3<203::AID-JBM1>3.0.CO;2-R

    Article  Google Scholar 

  22. Costa L, Bracco P. 26 Mechanisms of cross-linking , oxidative degradation , and stabilization of UHMWPE. Third Edition. Elsevier Inc.; n.d. doi:https://doi.org/10.1016/B978-0-323-35401-1/00026-0

  23. (2005) Ionizing radiation and orthopaedic prostheses. Nucl Instruments Methods Phys Res Sect B Beam Interact with Mater Atoms 236:30–37. https://doi.org/10.1016/J.NIMB.2005.03.245

  24. Effects of machining on tribological behavior of ultra high molecular weight polyethylene (UHMWPE) under dry reciprocating sliding. Wear 1999;225–229:716–23. doi:https://doi.org/10.1016/S0043-1648(99)00066-6

  25. Wang A (2001) A unified theory of wear for ultra-high molecular weight polyethylene in multi-directional sliding. Wear 248:38–47. https://doi.org/10.1016/S0043-1648(00)00522-6

    Article  Google Scholar 

Download references

Acknowledgments

The authors also acknowledge the fellowships from CNPQ (GB, GVS and CRMR) and CAPES (IMG).

Funding

This study was financially supported by the Brazilian National Health Fund (FNS) under Grant no. 25000.162216/2013-11TC 116/2013. The study also received additional financial support from FAPESC and CNPq.

Author information

Authors and Affiliations

  1. Biomechanics Engineering Laboratory, University Hospital (HU), Federal University of Santa Catarina, Florianópolis, Santa Catarina, 88040-900, Brazil

    Gabriel Bertoli, Izabelle M. Gindri, Patrícia O. Cubillos, Carlos R. M. Roesler & Gean V. Salmoria

  2. Laboratory of Innovation on Additive Manufacturing and Molding (NIMMA), Federal University of Santa Catarina, Florianópolis, Santa Catarina, 88040-900, Brazil

    Gean V. Salmoria

Authors
  1. Gabriel Bertoli
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Izabelle M. Gindri
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Patrícia O. Cubillos
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Carlos R. M. Roesler
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Gean V. Salmoria
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Gean V. Salmoria.

Ethics declarations

Conflict of interest

The authors declare that they have no conflict of interest.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Bertoli, G., Gindri, I.M., Cubillos, P.O. et al. Investigation on the structure, cross-link, and oxidation index of ultra high molecular weight polyethylene acetabular liners. Int J Adv Manuf Technol 101, 235–241 (2019). https://doi.org/10.1007/s00170-018-2937-2

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-018-2937-2

Keywords

Search

Navigation