Abstract
A novel high-pressure (water pump pressure up to 250 MPa) abrasive slurry micro-machining (HASJM) system was introduced. By feeding a premixed slurry into the mixing chamber of a water jet machine with a micro-nozzle (mixing tube diameter of 254 μm), premature erosion of system components was avoided. An optimum erosion rate of 2.7 mg/g was reached when machining Al6061-T6 with a slurry of 25 μm aluminum oxide particles under conditions (slurry flow rate = 200 g/min and water pump pressure = 235 MPa) near to those which theoretically maximized momentum transfer between the inlet slurry and the water jet entering the mixing chamber from the orifice. It was found that when the standoff distance increased tenfold, the erosion rate almost doubled in glass, but decreased by 50 % in Al6061-T6, due to differences in the erosion at the jet periphery for the two materials. For aspect ratios greater than 0.9, high-quality symmetric channels with a centerline waviness below 6.9 μm and a centerline roughness below 1.1 μm could be produced using a single pass at a low traverse velocity of 40 mm/min. The use of multiple machining passes at a relatively high traverse speed (~1000 mm/min) was found to produce asymmetric channels when the aspect ratio was greater than 0.9, owing to jet deflection from steps formed on the cutting front. Channels produced by micro-milling Al6061-T6 and glass had a 50 % lower centerline waviness and 16 % lower centerline roughness than those made with the conventional abrasive water jet in which air and abrasive entered the mixing chamber.
Similar content being viewed by others
References
Nguyen N, Wereley S (2002) Fundamentals and applications of microfluidics. Artech House, Norwood
Guruparan GK, Sathish M, Subramaniam NS, Kumar TS (2006) Design and fabrication of micro-channels for MEMS applications. J Synth React Inorg Met-Org Nano-Met Chem 36(2):185–191
Nguyen T, Pang K, Wang J (2009) A preliminary study of the erosion process in micro-machining of glasses with a low pressure slurry jet. Key Eng Mater 389:375–380
Wang J, Nguyan T, Pang KL (2009) Mechanism of microhole formation on glasses by an abrasive slurry jet. J Appl Sci 105(4):044906
Pang KL, Nguyen T, Fan JM, Wang J (2010) Machining of micro-channels on brittle glass using an abrasive slurry jet. Key Eng Mater 443:639–644
Nouraei H, Wodoslawsky A, Papini M, Spelt JK (2013) Characteristics of abrasive slurry jet micro-machining: a comparison with abrasive air jet micro-machining. J Mater Process Technol 213(10):1711–1724
Kowsari K, Nourei H, James DF, Spelt JK, Papini M (2014) Abrasive slurry jet micro-machining of holes in brittle and ductile materials. J Mater Process Technol 214:1909–1920
Hashish M (1993) Performance of high-pressure abrasive suspension jet system. Am Soc Mech Eng Prod Eng Div Pub 67:199–207
Liu HT (1998) Near-net shaping of optical surfaces with abrasive suspension jets. 14th Int. Conference on Jetting Technology, Brugge, pp 285–294
Miller DS (2004) Micromachining with abrasive water jets. J Mater Process Technol 149:37–42
Haghbin N, Ahmadzadeh F, Spelt JK, Papini M (2015) Micro-machining of channels using a high pressure abrasive slurry jet machine (HASJM). The 4M/ICOMM2015 Conference on Micro Manufacturing, Milan 459–462
Pua LM, Rumbold SO (2003) Industrial micro-channel devices where are we today. The first international conference on micro-channels and mini-channels, ICMM2003-1101, New York 773–780
Zhang S, Li X, Gu Y (2009) Optimum abrasive flow rate modelling for titanium alloy cutting using abrasive water jet. Int J Abras Technol 2(4):400–419
Momber AW, Kovacevic R (1998) Principles of abrasive water jet machining. Duisburg
Haghbin N, Spelt JK, Papini M (2015) Abrasive waterjet micro-machining of channels in metals: comparison between machining in air and submerged in water. Int J Mach Tools Manuf 88:108–117
Tazibt A, Parsy F, Abriak N (1996) Theoretical analysis of the particle acceleration process in abrasive water jet cutting. Comput Mater Sci 5:243–254
Momber AW, Kovacevic R (1995) Energy dissipative processes in high speed water-solid particle erosion. ASME Publ HTD 321:555–564
Hashish M (1987) Milling with abrasive-waterjets: a preliminary investigation. The 4th U.S. water jet conference, California 1–20
Dadkhahipour K, Nguyen T, Wang J (2012) Mechanisms of channel formation on glasses by abrasive waterjet milling. Wear 292–293:1–10
Aich U, Banerjee S, Bandyopadhyay A (2014) Multi-objective optimization of abrasive water jet machining responses by simulated annealing and particle swarm. Int J Mech Manuf Syst 7(1):38–59
Fan JM, Wang CY, Wang J (2009) Modelling the erosion rate in micro abrasive air jet machining of glass. Wear 266:968–974
Ciampini D, Spelt JK, Papini M (2003) Simulation of interference effects in particle stream following impact with a flat surface part I. Theory and analysis. Wear 254:237–249
Kovacevic R (1991) Surface texture in abrasive waterjet cutting. J Manuf Syst 10(1):32–40
Monno M, Ravasio C (2005) The effect of heading vibrations on the surfaces generated by waterjet cutting. Int J Mach Tools Manuf 45:355–363
Hashish M (1988) Visualization of the abrasive-waterjet cutting process. Exp Mech 28(2):159–169
Wang J (1999) Abrasive waterjet machining of polymer matrix composites cutting performance, erosive process and predictive model. Int J Adv Manuf Technol 15:757–768
Guo NS, Louis H, Meier G (1993) Surface structure and kerf Geometry in abrasive water jet cutting: formation and optimization. 7th American Water Jet Conference, Seattle 1–25
Orbanic H, Junkar M (2008) Analysis of striation formation mechanism in abrasive water jet cutting. Wear 265(5):821–830
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Haghbin, N., Ahmadzadeh, F., Spelt, J.K. et al. High pressure abrasive slurry jet micro-machining using slurry entrainment. Int J Adv Manuf Technol 84, 1031–1043 (2016). https://doi.org/10.1007/s00170-015-7769-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-015-7769-8