Abstract
The cyclic bending reliability of printed conductors fabricated with different polymer thick film pastes is studied in this article. Three silver pastes with different properties, Asahi SW1400, Asahi LS411AW, and DuPont 5064H, were utilized to deposit test specimens on a 125-μm thick polyethylene terephthalate foil, Melinex ST506, and to investigate the paste characteristics affecting the mechanical durability of the test specimens. The main fabrication method for the traces was roll-to-roll printing with a rotary screen, but also a sheet-based screen printing process was used to compare the results between the two manufacturing techniques. The electrical behavior of the test components was monitored by measuring the DC resistance of the test samples in situ under cyclic bending in both compression and tension with about a 6 mm bending radius. The reliability of the studied test populations was assessed with the statistical Weibull analysis as the failure criterion was a 20 % increase in resistance. It was found that the conductors fabricated with the paste with the smallest silver particle size, Asahi SW1400, had the highest lifetimes. This was due to the more flexible micro-scale structure with a lower volume fraction of silver in the paste. In addition, heat-treatment during the printing process was observed to be a crucial factor from the both electrical and mechanical perspectives of the printed conductors.
Similar content being viewed by others
References
Søndergaard RR, Hösel M, Krebs FC (2013) Roll-to-roll fabrication of large area functional organic materials. J Polym Sci Polym Phys 51:16–34
Kololuoma T, Tuomikoski M, Mäkelä T, Heilmann J, Haring T, Kallioinen J, Hagberg J, Kettunen I, Kopola H (2004) Towards roll-to-roll fabrication of electronics, optics and optoelectronics for smart and intelligent packaging. Proc SPIE 77–85 doi:10.1117/12.535456
Kim CH, Jo J, Lee S (2012) Design of roll-to-roll printing equipment with multiple printing methods for multi-layer printing. Rev Sci Instrum 83:065001
Noh J, Yeom D, Lim C, Cha H, Han J, Kim J, Park Y, Subramanian V (2010) Scalability of roll-to-roll gravure-printed electrodes on plastic foils. IEEE Trans Electron Packag Manuf 33:275–283
Yakimets I, MacKerron D, Giesen P, Kilmartin KJ, Goorhuis M, Meinders E, MacDonald WA (2009) Polymer substrates for flexible electronics: achievements and challenges. Proc FuSeM 5–8
Tobjörk D, Österbacka D (2011) Paper electronics. Adv Mater 23:1935–1961
Lacerda Silva N, Goncalves LM, Carvalho H (2013) Deposition of conductive materials on textile and polymeric substrates. J Mater Sci 24:635–643
Pudas M, Halonen N, Granat P, Vähäkangas J (2005) Gravure printing of conductive particulate polymer inks on flexible substrates. Prog Org Coat 54:310–316
Janeczek K, Jakubowska M, Koziot G, Mlozniak A, Arazna A (2012) Investigation of ultra-high-frequency antennas printed with polymer paste on flexible substrates. IET Microw Antennas Propag 6:549–554
Voutilainen JV, Happonen T, Fabritius T, Häkkinen J (2015) All silk-screen printed polymer-based remotely readable temperature sensor. IEEE Sensors J 15:723–733
van den Brand J, de Baets J, van Mol T, Dietzel A (2008) Systems-in-foil—devices, fabrication processes and reliability issues. Microelectron Reliab 48:1123–1128
Keränen K, Korhonen P, Rekilä J, Tapaninen O, Happonen T, Makkonen P, Rönkä K (2015) Roll-to-roll printed and assembled large area LED lighting element. Int J Adv Manuf Technol. doi:10.1007/s00170-015-7244-6
Happonen T, Voutilainen JV, Fabritius T (2014) Reliability study on adhesive interconnections in flex-to-flex printed electronics applications under environmental stresses. IEEE Trans Device Mater Reliab 14:1005–1012
Janeczek K, Koziol G, Jakubowska M, Arazna A, Mlozniak A, Futera K (2013) Assessment of electromechanical properties of screen printed polymer nanopastes. Mater Sci Eng B Solid 178:511–519
Merilampi S, Laine-Ma T, Ruuskanen P (2009) The characterization of electrically conductive silver ink patterns on flexible substrates. Microelectron Reliab 49:782–790
Merilampi S, Björninen T, Haukka V, Ruuskanen P, Ukkonen L, Sydänheimo L (2010) Analysis of electrically conductive silver ink on stretchable substrates under tensile load. Microelectron Reliab 50:2001–2011
Suo Z, Ma EY, Gleskova H, Wagner A (1999) Mechanics of rollable and foldable film-on-foil electronics. Appl Phys Lett 74:1177–1179
Sevkat E, Li J, Liaw B, Delale F (2008) A statistical model of electrical resistance of carbon fiber reinforced composites under tensile loading. Compos Sci Technol 68:2214–2219
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Happonen, T., Ritvonen, T., Korhonen, P. et al. Bending reliability of printed conductors deposited on plastic foil with various silver pastes. Int J Adv Manuf Technol 82, 1663–1673 (2016). https://doi.org/10.1007/s00170-015-7403-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-015-7403-9