Friction stir lap welding of 5456 aluminum alloy with different sheet thickness: process optimization and microstructure evolution

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

The influences of friction stir welding process parameters on microstructure evolution and mechanical properties of lap-welded 5456 aluminum alloy plates with different thickness and temper conditions were investigated. The upper plate was 5 mm thick, cold rolled aluminum alloy 5456-T321 and the lower plate was 2.5-mm annealed sheet (5456-O). Four different pin geometry types (conical thread pin, cylindrical–conical thread pin, stepped conical thread pin, and flared-triflute pin tool) and two rotational speeds (600 and 800 rpm) were used to produce the joints. Microstructures and microhardness values in the weld nugget (WN), thermomechanically affected zone (TMAZ), and the heat-affected zone (HAZ) were examined and correlated with selected processing conditions. Specifically, the influence of tool geometry on the flow of the plasticized material in the nugget zone, extent of hooking defect, and mechanical properties (microhardness) of the FSW joints were documented and quantified. It was found that weld joints made by using the stepped conical thread pin tool produced a homogeneous microstructure with finer grain size (5.4 μm) and higher microhardness levels than the other tools. The optimum processing conditions resulting in sound and defect-free joints with highest mechanical properties were obtained with the stepped conical thread pin and 600-rpm rotational speed. The evolution of the microhardness in each region is characterized and related to processing conditions.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Buffa G, Campanile G, Fratini L, Prisco A (2009) Friction stir welding of lap joints: influence of process parameters on the metallurgical and mechanical properties. Mater Sci Eng A 519:19–26

    Article  Google Scholar 

  2. Zhao YH, Lin SB, Wu L, Qu FX (2005) The influence of pin geometry on bonding and mechanical properties in friction stir weld 2014 Al alloy. Mater Lett 59:2948–2952

    Article  Google Scholar 

  3. Cederqvist L, Reynolds AP (2001) Factors affecting the properties of friction stir welded aluminum lap joints. Weld J Res Suppl 80–12:281–287

    Google Scholar 

  4. Fleming PA, Hendricks CE, Cook GE, Wilkes DM, Strauss AM, Lammlein DH (2010) Seam-tracking for friction stir welded lap joints. ASM Int JMEPEG 19:1128–1132

    Article  Google Scholar 

  5. Chionopoulos SK, Sarafoglou CI, Pantelis DI, Papazoglou VJ (2008) Effect of tool pin and welding parameters on friction stir welded (FSW) marine aluminum alloys. Proceedings of 3rd ICMEN, Chalkidiki :307–316

  6. Chen HB, Yan K, Lin T, Chen SB, Jiang CY, Zhao Y (2006) The investigation of typical welding defects for 5456 aluminum alloy friction stir welds. Mater Sci Eng A 433:64–69

    Article  Google Scholar 

  7. Menzemer C, Srivatsan TS (1999) The effect of environment on fatigue crack growth behavior of aluminum alloy 5456. Mater Sci Eng A 271:188–195

    Article  Google Scholar 

  8. Fonda RW, Pao PS, Jones HN, Feng CR, Connolly BJ, Davenport AJ (2009) Microstructure, mechanical properties, and corrosion of friction stir welded Al 5456. Mater Sci Eng A 519:1–8

    Article  Google Scholar 

  9. Bahemmat P, Rahbari A, Haghpanahi M, Besharati MK (2008) Experimental study on the effect of rotational speed and tool pin profile on AA2024 aluminum friction stir welded but joints. Proceedings of ECTC, ASME technical conference, Miami, Florida, USA: 1.1–1.7

  10. Leal RM, Loureiro A (2008) Effect of overlapping friction stir welding passes in the quality of welds of aluminum alloys. Mater Design 29:982–991

    Article  Google Scholar 

  11. Scialpi A, De Filippis LAC, Cavaliere P (2007) Influence of shoulder geometry on microstructure and mechanical properties of friction stir welded 6082 aluminum alloy. Mater Design 28:1124–1129

    Article  Google Scholar 

  12. Fujii H, Cui L, Maeda M, Nogi K (2006) Effect of tool shape on mechanical properties and microstructure of friction stir welded aluminum alloys. Mater Sci Eng A 419:25–31

    Article  Google Scholar 

  13. Elangovan K, Balasubramanian V (2007) Influences of pin profile and rotational speed of the tool on the formation of friction stir processing zone in AA2219 aluminum alloy. Mater Sci Eng A 459:7–18

    Article  Google Scholar 

  14. Boz M, Kurt A (2004) The influence of stirrer geometry on bonding and mechanical properties in friction stirs welding process. Mater Design 25:343–347

    Article  Google Scholar 

  15. Elangovan K, Balasubramanian V (2008) Influences of tool pin profile and tool shoulder diameter on the formation of friction stir processing zone in AA6061 aluminium alloy. Mater Design 29:362–373

    Article  Google Scholar 

  16. Oosterkamp A, Oosterkamp LD, Nordeide A (2004) ‘Kissing bond’ phenomena in solid-state welds of aluminum alloys. Weld J 83:225S–231S

    Google Scholar 

  17. Zhou C, Yang X, Luan G (2006) Effect of kissing bond on fatigue behavior of friction stir welds on Al 5083 alloy. J Mater Sci 41:2771–2777

    Article  Google Scholar 

  18. Salari E, Jahazi M, Khodabandeh A, Ghasemi-Nanesa H (2014) Influence of tool geometry and rotational speed on mechanical properties and defect formation in friction stir lap welded 5456 aluminum alloy sheets. Mater Design 58:381–389

    Article  Google Scholar 

  19. Kallee S (2000) Application of friction stir welding in the shipbuilding industry. Paper presented at the Lightweight construction. The Royal Institution of Naval Architects, TWI, Cambridge, UK, 25–25 February 2000

  20. Dubourg L, Merati A, Jahazi M (2010) Process optimization and mechanical properties of friction stir lap welds of 7075-T6 stringers on 2024-T3 skin. Mater Design 31–7:3324–3330

    Article  Google Scholar 

  21. Afrin N, Chen DL, Cao X, Jahazi M (2008) Microstructure and tensile properties of friction stir welded AZ31B magnesium alloy. Mater Sci Eng A 472(1–2):179–186

    Article  Google Scholar 

  22. Cavaliere P, De Santis A, Panella F, Squillace A (2009) Effect of welding parameters on mechanical and microstructural properties of dissimilar AA6082–AA2024 joints produced by friction stir welding. Mater Design 30(3):609–616

    Article  Google Scholar 

  23. Liu HJ, Fujii H, Nogi K (2004) Microstructure and mechanical properties of friction stir welded joints of AC4A cast aluminium alloy. Mater Sci Tech 20(3):399–402

    Article  Google Scholar 

  24. Chen YC, Feng JC, Liu HJ (2009) Precipitate evolution in friction stir welding of 2219-T6 aluminum alloys. Mater Charact 60:476–481

    Article  Google Scholar 

  25. Sukedai E, Yokoyama T, Song M (2014) Microstructure and tensile properties of a friction stir welded Al–Mg–Si alloy. Int J Mater Res 105(9):883–893

    Article  Google Scholar 

  26. Gemme F, Verreman Y, Dubourg L, Jahazi M (2010) Numerical analysis of the dwell phase in friction stir welding and comparison with experimental data. Mater Sci Eng A 527(16–17):4152–4160

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Science and Research Branch, Islamic Azad University, 1477893855, Tehran, Iran

    Emad Salari & Alireza Khodabandeh

  2. Department of Mechanical Engineering, École de Technologie Supérieure, 1100 rue Notre-Dame Ouest, Montréal, QC, H3C1K3, Canada

    Mohammad Jahazi & Hadi Ghasemi Nanesa

Authors
  1. Emad Salari
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Mohammad Jahazi
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Alireza Khodabandeh
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Hadi Ghasemi Nanesa
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Hadi Ghasemi Nanesa.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Salari, E., Jahazi, M., Khodabandeh, A. et al. Friction stir lap welding of 5456 aluminum alloy with different sheet thickness: process optimization and microstructure evolution. Int J Adv Manuf Technol 82, 39–48 (2016). https://doi.org/10.1007/s00170-015-7342-5

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-015-7342-5

Keywords

Search

Navigation