Abstract
6063-T4 aluminum alloy plates were friction stir butt and lap welded using three different backing plate materials: mild steel, stainless steel, and asbestos. Effects of backing plate material on macrostructure, peak mid-section temperatures in heat affected and weld nugget zones, and weld mechanical properties were obtained for each of the cases. Effect of backing plate material was seen to be more significant in lap than butt welding. While lap welds obtained even at a low welding speed, for mild steel and stainless steel backing plates, contained multiple weld defects leading to failure in lap shear tests from weld nugget zone, corresponding welds obtained with asbestos backing plate were defect free resulting in failure from base metal region. In butt as well as lap configuration, asbestos backing plate which had the lowest thermal diffusivity was observed to provide the largest process window within which defect free welds could be obtained.
Similar content being viewed by others
References
Mistikoglu CG (2014) Recent developments in friction stir welding of Al-alloys. J Mater Eng Performance 23:1936–1953
Threadgill PL, Leonard AJ, Shercliff HR, Withers PJ (2009) Friction stir welding of aluminium alloys. Int Mater Rev 54(2):49–93
Mishra RS, MA ZY (2005) Friction stir welding and processing. Mater Sci Eng R 50:1–78
Nandan R, Debroy T, Bhadeshia H KDH (2008) Recent advances in friction-stir welding-process, weldment structure and properties. Prog Mater Sci 53:980–1023
He X, Gu F, Ball A (2014) A review of numerical analysis of friction stir welding. Prog Mater Sci 65:1–66
Hui-jie L, Fujii H, Maeda M, Nogi K (2003) Tensile properties and fracture locations of friction-stir welded joints of 6061-T6 aluminum alloy. J Mater Sci Lett 22:1061–1063
Imam M, Racherla V, Biswas K (2014) Effect of post-weld natural aging on mechanical and microstructural properties of friction stir welded 6063-T4 aluminium alloy. Mater Des 64:675–686
Ren SR, Ma ZY, Chen LQ (2007) Effect of welding parameters on tensile properties and fracture behavior of friction stir welded Al-Mg-Si alloy. Scrip Mater 56:69–72
Lim S, Kim S, Lee CG, Kim S (2004) Tensile behavior of friction stir welded Al 6061-T651. Metal Mater Trans A 35A:2829–2835
Sato YS, Kokawa H, Enomoto M, Shigetoshi J (Unknown Month 2429) Microstructural evolution of 6063 aluminium alloy during friction stir welding. Metall Mater Trans A :30A
Heinz B, Skrotzki B (2002) Characterization of a friction-stir-welded aluminum alloy 6013. Metall Mater Trans A 33B:489–498
Imam M, Biswas K, Racherla V (2013) On use of weld zone temperatures for online monitoring of weld quality, in friction stir welding of naturally aged aluminium alloys. Mater Des 52:730–739
Rajakumar S, Muralidharan C, Balasubramanian V (2010) Establishing empirical relationships to predict grain size and tensile strength of friction stir welded AA 6061-T6 aluminium alloy joints. Trans Nonferrous Met Soc China 20:1863–1872
Yadava MK, Mishra RS, Chen YL, Carlson B, Grant GJ (2010) Study of friction stir welding joining of thin aluminium sheets in lap joint configuration. Sci Tech Weld join 15:70–75
Rosales MJC, Alcantara NG, Satos J, Zettler R (2010) The backing bar role in heat transfer on aluminium alloys friction stir welding. Mater Sci Forum 636–637:459–464
Upadhyay p, Reynolds AP (2012) Effects of forge axis force and backing plate thermal diffusivity on FSW of AA6056. Mater Sci Eng A 558:94–402
Zhang Z, Li W, Shen J, Chao YJ, Li J, Ma YE (2013) Effect of backplate diffusivity on microstructure and mechanical properties of friction stir welded joints. Mater Des 50:551–557
Soundararajan v, Yarrapareddy E, Kovacevic R (2007) Investigation of the friction stir lap welding of aluminum alloys AA 5182 and AA 6022. J Mater Eng Perform 16(4):477–484
Buffa G, Campanile G, Fratini L, Prisco A (2009) Friction stir welding of lap joints: Influence of process parameters on the metallurgical and mechnical properties. Mater Sci Eng A 519:19–26
Yazdanian S, Chen ZW, Littlefair G (2012) Effects of friction stir lap welding parameters on weld features on advancing side and fracture strength of AA6060-T5 welds. J Mater Sci 47:1251–1261
Edwards GA, Stiller K, Dunlop GL, Couper MJ (1998) The precipitation sequence in Al-Mg-Si alloys. Acta Mater 46:3893–3904
Simar A, Brechet Y, De Meester B, Denquin A, Gallais C, pardoen T (2012) Integrated modeling of friction stir welding of 6xxx series Al alloys: Process, microstructure and properties. Prog Mater Sci 57:95–183
Elangovan K, Balasubramanian V (2008) Influences of tool pin profile and tool shoulder diameter on the formation of friction stir processing zone in AA6061 aluminium alloy. Mater Des 29:362–373
Imam M, Biswas K, Racherla V (2013) Effect of weld morphology on mechanical response and failure of friction stir welds in a naturally aged aluminum alloy. Mater Des 44:23–34
Kumzerov YA, Parfen’eva LS, Smirnov IA, Krivchikov AI, Zvyagina GA, Fil VD, Misiorek H, Mucha J, Jezowski A (2005) Thermal and acoustic properties of chrysotile asbestos. Phy Solid State 47(2):370–373
Kusiorowski R, Zarimba T, Piotrowski J, Adamek J (2014) Thermal decomposition of different types of asbestos. J Therm Ana Calorim 109:693–704
Charde N, Yusof F, Rajkumar R (2014) Materials characterization of mild steels, stainless steels, and both steel mixed joints under resistance spot welding (2-mm sheets). Int J Adv Manuf Tech
Sato YS, Urata M, Kokawa H (2002) Parameters controlling microstructure and hardness during friction-stir welding of precipitation-hardenable aluminum alloy 6063. Metall Mater Trans A 33A:625–635
Su JQ, Nelson TW, Stirling CJ (2005) Microstructure evolution during FSW/FSP of high strength aluminium alloys. Mater Sci Eng A 405:277–286
Shastry CR, Judd G (1971) A study of grain boundary precipitate-free zone formation in an Al-Zn-Mg alloy. Metal Trans 2:3283–3287
Zhang HJ, Liu HJ, Yu L (2012) Effect of water cooling on the performances of friction stir welding heat-affected-zone. J Mater Eng Perform 21:118–227
Lee WB, Yeon YM, Jung SB (2003) Evaluation of the microstructure and mechanical properties of friction stir welded 6005 aluminum alloy. Mater Sci Tech 19:1513–1518
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Imam, M., Racherla, V. & Biswas, K. Effect of backing plate material in friction stir butt and lap welding of 6063-T4 aluminium alloy. Int J Adv Manuf Technol 77, 2181–2195 (2015). https://doi.org/10.1007/s00170-014-6617-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-014-6617-6