Abstract
Different laser heat inputs were applied on the gray-colored acrylonitrile butadiene styrene (ABS) plastic using fixed laser power and variable scanning speeds to join ABS- and polycarbonate (PC)-based polymers. Experiments with a laser power between 6 and 8 W and a scanning speed of 1,500, 3,000, and 4,500 mm/min were used for the joining. Heat-affected zone (HAZ) and melt zone measurements were performed to find the joining energy threshold, and the mechanical properties of welds were evaluated. At the low scanning speed, the total heat input at the given area resulted in carbonization damage on the surface. However, energy distributed laser beam joining process by galvanometers resulted in secure and sound weld joining quality. Damage threshold was calculated as 127 J/cm2 with relatively less sensitivity of scanning speed. However, the ablation threshold was measured to be 215, 281, and 424 J/cm2 for the scanning speed of 4,500, 3,000 and 1,500 mm/min, respectively.
Similar content being viewed by others
References
Acherjee B, Kuar A, Mitra S, Misra D (2012) Effect of carbon black on temperature field and weld profile during laser transmission welding of polymers: a FEM study. Opt Laser Technol 44:514–521
Wei M, Yang H (2003) Cumulative heat effects in excimer laser ablation of polymer PC and ABS. Int J Adv Manuf Technol 21(12):1029–1034
Hadriche I, Ghorbel E, Masmoudi N, Casalino G (2010) Investigation on the effects of laser power and scanning speed on polypropylene diode transmission welds. Int J Adv Manuf Technol 50(1):217–226
Ussing T, Petersen L, Nielsen C, Helbo B, Hojslet L (2007) Micro laser welding of polymer microstructures using low power laser diode. Int J Adv Manuf Technol 33(1):198–205
Mingareev I, Weirauch F, Olowinsky A, Shah L, Kadwani P, Richardson M (2012) Welding of polymers using a 2 μm thulium fiber laser. Opt Laser Technol 4:2095–2099
Illie M, Cicala E, Grevey D, Mattei S, Stoica V (2009) Diode laser welding of ABS: experiments and process modeling. Opt Laser Technol 41:608–614
Amanat N, Chaminade C, Grace J, James N, McKenzie D (2011) Optimal process parameters for thermoplastic polyetheretherketone joints fabricated using transmission laser welding and Lumogen IR absorptive pigment. J Laser Appl 23:012003
Thorlabs catalogue (Small Beam Diameter Scanning Galvo Mirror Systems), www.thorlabs.com
Han S, Choi H (2013) Dual laser beam joining process for polymers in automotive applications to reduce weights. J Korean Weld Join Soc 31(4):23–27
Hansen J-P, McDonald IR (2007) Theory of simple liquids. Elsevier, pp 250–254. ISBN 0123705355
Choi H, Farson D, Bovatsek J, Arai A, Ashkenasi D (2007) Direct-write patterning of indium-tin-oxide film by high pulse repetition frequency femtosecond laser ablation. Appl Optics 46(23):5792–5799
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shin, H.M., Choi, H.W. Design of energy optimization for laser polymer joining process. Int J Adv Manuf Technol 75, 1569–1576 (2014). https://doi.org/10.1007/s00170-014-6241-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-014-6241-5