Abstract
The thermal conductivity of several wet and dry processed industrial soft fibreboards was determined at temperatures between 10°C and 30°C. Additionally, the thermal conductivity was tested relative to the moisture content ranging from an oven-dry sample to a moisture content of 85% relative humidity. Furthermore, the water vapour diffusion was investigated to determine the resistance factor and the diffusion coefficient under ‘dry cup’ and ‘wet cup’ conditions and the sorptions were tested by means of the sorption isotherms.
The thermal conductivity increases with increasing temperature at about 0.45% per Kelvin and with increasing moisture at about 0.17×10−2 W/mK per percent volumetric moisture content. Furthermore, the thermal conductivity depends on the manufacture (dry or wet process) and is influenced by density. The water vapour resistance factor increases and the diffusion coefficient decreases with increasing density. Both factors decrease with increasing moisture content and they are dependant on board thickness, composition and manufacturing. The sorption isotherm is similar to solid wood below about 80% relative humidity but strongly increases for soft fibreboards with binding fibres and additives of ammonium phosphate or sodium borate and boric acid when above 80% relative humidity.
Zusammenfassung
An verschiedenen, nach dem Nass- oder nach dem Trockenverfahren, industriell hergestellten Holzfaserdämmplatten wurde die Wärmeleitfähigkeit in Abhängigkeit von der Temperatur zwischen 10°C und 30°C geprüft. An einem Teil der Platten wurde die Wärmeleitfähigkeit zusätzlich in Abhängigkeit von der Feuchte, von darrtrocken bis zu einer Feuchte bei 85 % relativer Luftfeuchte, bestimmt. Weiterhin wurden die Wasserdampfdiffusion unter Ermittlung der Diffusionswiderstandszahlen und der Diffusionskoeffizienten im Trocken- und im Feuchtbereich sowie das Sorptionsverhalten anhand der Sorptionsisothermen untersucht.
Die Wärmeleitfähigkeit steigt mit zunehmender Temperatur um 0,45 % pro Kelvin und mit zunehmender Feuchte um 0,17×10−2 W/mK pro Prozent volumenbezogenen Feuchtegehalts. Zusätzlich besteht eine Abhängigkeit von der Dichte sowie vom Herstellungsverfahren (Nass- oder Trockenverfahren). Während mit zunehmender Dichte die Wasserdampfdiffusionswiderstandszahl steigt, verringert sich der Diffusionskoeffizient. Beide Kenngrößen nehmen mit zunehmender Feuchte ab und sind abhängig von der Probendicke, der Zusammensetzung und dem Herstellungsverfahren. Bis ca. 80 % relativer Luftfeuchte verhält sich die Sorptionsisotherme ähnlich wie diejenige von Vollholz, oberhalb davon steigt sie jedoch bei den Holzfaserdämmplatten mit Bindefasern sowie Zusätzen von Ammoniumphosphat oder Borsäure und Borax steil an.
Similar content being viewed by others
References
Albrecht W (1997) Anwendungsgebiete, Eigenschaften und Klassifizierung von „alternativen“ Wärmedämmstoffen. Bauphysik 19(4):121–125
Alix S, Philippe E, Bessadok A, Lebrun L, Morvan C, Marais S (2009) Effect of chemical treatments on water sorption and mechanical properties of flax fibres. Bioresour Technol 100:4742–4749
Bessadok A, Langevin D, Gouanvé F, Chappey C, Roudesli S, Marais S (2009) Study of water sorption on modified Agave fibres. Carbohydr Polym 76:74–85
Cammerer WF (1987) Der Feuchtigkeitseinfluss auf die Wärmeleitfähigkeit von Bau- und Wärmedämmstoffen. Bauphysik 9(6):259–266
Frandsen HL, Damkilde L, Svensson S (2007) A revised multi-Fickian moisture transport model to describe non-Fickian effects in wood. Holzforschung 61(5):563–572
Grohe B (2004) Heat conductivities of insulation mats based on water glass bonded non-textile hemp or flax fibres. Holz Roh- Werkst 62(5):352–357
Häupl P (2008) Bauphysik. Ernst & Sohn, Berlin, p 66
Hill CAS, Norton A, Newman G (2009) The water vapor sorption behavior of natural fibers. J Appl Polym Sci 112:1524–1537
ISO 8302 (1991) Thermal insulation—determination of steady-state thermal resistance and related properties—guarded hot plate apparatus. Geneva
ISO 12572 (2001) Hygrothermal performance of building materials and products—determination of water vapour transmission properties. Geneva
Kehrer M, Künzel HM, Sedlbauer K (2001) Dämmstoffe aus nachwachsenden Rohstoffen—ist der Feuchtezuschlag für die Wärmeleitfähigkeit gerechtfertigt? IBP-Mitteilung 390, Stuttgart, p 2
Kollmann F (1951) Technologie des Holzes und der Holzwerkstoffe, 2nd edn. Anatomie und Pathologie, Chemie, Physik, Elastizität und Festigkeit, vol 1. Springer, Berlin
Kollmann F, Côté WA Jr (1968) Principles of wood science and technology. Solid wood, vol I. Springer, Berlin
Kollmann F, Malmquist L (1956) Über die Wärmeleitzahl von Holz und Holzwerkstoffen. Holz Roh- Werkst 14(6):201–204
Kollmann F, Schneider A (1959) Sorptionsmessungen an mit Salzen imprägnierten Hölzern. Holz Roh- Werkst 17(5):212–218
Künzel H (1986) Bestimmt der volumen- oder der massebezogene Feuchtegehalt die Wärmeleitfähigkeit von Baustoffen? Bauphysik 8(2):33–39
Lesar B, Gorisek Z, Humar M (2009) Sorption properties of wood impregnated with boron compounds, sodium chloride and glucose. Dry Technol 27(1):94–102
Martin JR, Lamb GER (1987) Measurement of thermal conductivity of nonwovens using a dynamic method. Text Res J 57:721–727
Müller M (1998) Möglichkeiten der Herstellung stärkegebundener lignocelluloser Formkörper als Variante dämmender, biologisch abbaubarer Werkstoffe. Dissertation, Technische Universität Dresden
Niemz P (1993) Physik des Holzes und der Holzwerkstoffe. DRW-Verlag, Leinfelden-Echterdingen
Popper R, Niemz P (2009) Wasserdampfsorptionsverhalten ausgewählter heimischer und überseeischer Holzarten. Bauphysik 31(2):117–121
Reyer E, Schild K, Völkner S (2002) Kompendium der Dämmstoffe, 3rd edn. Fraunhofer IRB Verlag, Stuttgart
Schardt G, Mägel M, Gulich B (1993) Untersuchungen zum Wärmeisolationsverhalten von Nadelvliesstoffen. Tech Text 36(2):114–119
Scheiding W (1998) Entwicklung, Herstellung und Untersuchung wesentlicher Eigenschaften wasserglasgebundener Holzfaserdämmplatten aus Fichtenholz. Dissertation, Technische Universität Dresden
Schulz T, Tobisch S (2006) Untersuchungen zur Herstellung mehrlagiger Massivholzplatten unter Einsatz von Holzfaserdämmplatten als Mittellagen. Teil 2: Weiterführende Untersuchungen und Industrieversuche. Holztechnologie 47(3):5–12
Schunk C, Treml S, Tröger F (2009) Lose Dämmstoffe aus Holz – Wärmeleitfähigkeit von speziell hergestellten Frässspänen ausgewählter Holzarten. Eur J Wood Prod 67(4):487–488
Seifert J (1972) Zur Sorption und Quellung von Holz und Holzwerkstoffen. Erste Mitteilung: Einflüsse auf das Sorptionsverhalten der Holzwerkstoffe. Holz Roh- Werkst 30(3):99–111
Siau JF (1995) Wood: influence of moisture on physical properties. Department of Wood Science and Forest Products, Virginia Polytechnic Institute and State University, Keene, NY
Skaar C (1988) Wood-water relations. Springer, Berlin
Sonderegger W, Niemz P (2006) Untersuchungen zur Quellung und Wärmedehnung von Faser-, Span- und Sperrholzplatten. Holz Roh- Werkst 64(1):11–20
Sonderegger W, Niemz P (2009) Thermal conductivity and water vapour transmission properties of wood-based materials. Eur J Wood Prod 67(3):313–321
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Sonderegger, W., Niemz, P. Thermal and moisture flux in soft fibreboards. Eur. J. Wood Prod. 70, 25–35 (2012). https://doi.org/10.1007/s00107-010-0498-7
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00107-010-0498-7