Evaluation on some finishing properties of oil palm plywood

Bewertung der Oberflächeneigenschaften von unterschiedlich behandeltem Ölpalmen-Sperrholz

Abstract

Oil palm is the largest and most important plantation crop in Malaysia. The oil palm generally lasts for 25–30 years before the next replantation is done. Substantial amount of biomass in the form of palm trunk results from plantation cycle. This resource is simply left on the ground to decay and is not used as raw material to manufacture any kind of value-added products. The objective of this study was to investigate the possibility of manufacturing plywood from oil palm trunks and to evaluate some of the finishing properties of such experimental panels in comparison to those from Shorea sp as control samples. Three-ply plywood samples were produced from 5 mm thick veneers of oil palm using urea formaldehyde adhesive. Three types of chemicals, namely nitrocellulose, pre-catalyzed lacquer and polyurethane were used to finish experimental panels. The surface finished with nitrocellulose had the lowest contact angle on raw surface of oil palm plywood and wood. The average cross cut tape index of oil palm plywood was comparable to Shorea sp. All finishing materials of oil palm plywood produced impact rating of 4 except for surface finished with nitrocellulose while finishing on wood indicated an impact rating of 3. Oil palm plywood had higher weight loss compared to Shorea sp. Based on results from contact angle, cross cut tape index, impact rate test, weathering, and soil burial test methods it appears that the samples showed acceptable finishing properties comparable to those of solid wood.

Zusammenfassung

Die Ölpalme ist das mengenmäßig größte und wichtigste Erzeugnis der Plantagen in Malaysia. Der Bestand wird in der Regel nach 25–30 Jahren erneuert und neu angepflanzt. Aufgrund dieses Zyklus fällt eine beachtliche Menge an Biomasse in Form von Palmenstämmen an. Diese Ressource bleibt liegen und verfault und wird nicht als Rohmaterial zur Herstellung irgendwelcher Erzeugnisse genutzt. Ziel dieser Studie war es, die Möglichkeiten der Sperrholzherstellung aus Ölpalmenstämmen zu untersuchen und die Oberflächeneigenschaften solcher Versuchsplatten mit Kontrollproben aus Shorea sp. zu vergleichen. Aus 5 mm dicken Ölpalmen-Furnieren wurden unter Verwendung von Harnstoff-Formaldehydharz dreilagige Sperrholzproben hergestellt. Die Oberflächen der Versuchsplatten wurden mit den drei Chemikalien Nitrocellulose, vorkatalysiertes Beschichtungsmaterial sowie Polyurethan behandelt. Die mit Nitrocellulose behandelte, nicht weiter bearbeitete Oberfläche hatte den kleinsten Kontaktwinkel. Der durchschnittliche Abhebefestigkeitsindex von Ölpalmen-Sperrholz war mit demjenigen von Shorea sp. vergleichbar. Bis auf die mit Nitrocellulose behandelten Oberflächen wurden alle Materialen zur Oberflächenbehandlung von Ölpalmen-Sperrholz bei der Stoßprüfung mit 4 bewertet, wohingegen Holz durchschnittlich als 3 eingestuft wurde. Der Masseverlust bei Ölpalmen-Sperrholz war größer als bei Shorea sp. Basierend auf den Ergebnissen der Kontaktwinkel-, Abhebefestigkeits-, Stoßprüfungs-, Bewitterungs- und Erdeingrabeversuchsverfahren wies das Sperrholz im Vergleich zu Massivholz tendenziell akzeptable Oberflächeneigenschaften auf.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    ASTM D3359 (1997) Standard test method for measuring adhesion by tape test

  2. 2.

    ASTM E308-01 (2006) Standard practice for computing the colors of objects by using the CIE system

  3. 3.

    ASTM1413 D (1979) Standard test method for wood preservative by laboratory soil-block cultures

  4. 4.

    Basiron Y, Weng CK (2004) The role of research and development strategies in Food Safety and Good Agricultural, Manufacturing and distribution practices in the Malaysian Palm oil industry. Oil Palm Ind Econ J 5(1):1–16

    Google Scholar 

  5. 5.

    BS3962: Part 6 (1975) Finishes for wooden furniture: Assessment of resistance to mechanical damage

  6. 6.

    Feist WC (1982) Weathering characteristics of finished wood-based panel products. J Coat Technol 54(686):43–50

    Google Scholar 

  7. 7.

    Feist WC (1988) Weathering performance of finished southern pine plywood siding. For Prod J 38(3):22–28

    CAS  Google Scholar 

  8. 8.

    Kalnins MA, Feist WC (1993) Increase in wettability of wood with weathering. For Prod J 43(2):55–57

    CAS  Google Scholar 

  9. 9.

    Leonard LS, Bouldin DL, Martz JA (1983) Transparent film forming coatings. In: Proceedings of Forest Products Research Society 7318, USA

  10. 10.

    Mahmud SZ, Ahmad M (2005) Contact angles of liquid adhesives on oil palm trunk veneer surfaces. Japanese International Research Center for Agricultural Science (JIRCAS) Working Report No. 39 pp. 153–156

  11. 11.

    Meincken M, Klash A, Seboa S, Sanderson RD (2006) Influence of the viscosity and the substrate on the surface hydrophobicity of polyurethane coatings. Appl Surf Sci 253(2):805–809

    Article  CAS  Google Scholar 

  12. 12.

    MTC (2005) Malaysian Timber Council. http://mtc.com.my/news/pr164.htm

  13. 13.

    Ramli R, Shaler S, Jamaludin MA (2002) Properties of medium density fibreboard from oil palm empty fruit bunch fibre. J Oil Palm Res 14(2):34–40

    Google Scholar 

  14. 14.

    Wicks ZW, Jones FN, Pappas SP (1999) Organic Coatings Science and Technology 2nd edn. Wiley Interscience Publication, New York

    Google Scholar 

  15. 15.

    Yamamoto K, Simatupang MH, Hashim R (1988) Caoutchouc in teak wood (Tectona grandis L.f.): formation, location, influence on sunlight irradiation, hydrophobicity and decay resistance. Holz Roh- Werkst 56(3):201–209

    Article  Google Scholar 

  16. 16.

    Yusof MN (1997) High yield pulping of oil palm frond fibers in Malaysia. In: Proceedings of the Nanjing International Symposium on High Yield Pulping, Nanjing, China

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Othman Sulaiman.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Sulaiman, O., Hashim, R., Wahab, R. et al. Evaluation on some finishing properties of oil palm plywood . Holz Roh Werkst 66, 5–10 (2008). https://doi.org/10.1007/s00107-007-0194-4

Download citation

Keywords

  • Contact Angle
  • Polyurethane
  • Malaysia
  • Empty Fruit Bunch
  • Laminate Veneer Lumber