Abstract
Surface treatment of wood was carried out using acryl-silicon type resin including didecyl dimethyl ammonium tetrafluoroborate (DBF), boron-containing quaternary ammonia compound. Surface-treated wood specimens were exposed laboratory decay resistance tests after completing a 10-cyle severe weathering process. In laboratory decay resistance tests, one brown-rot decay fungus, Fomitopsis palustris and one white-rot decay fungus, Trametes versicolor were used. The specimens were also subjected to laboratory termite resistance tests using subterranean termites, Coptotermes formosanus. Wood specimens treated with 2% DBF and resin containing preservative solution showed improved decay and termite resistance suggesting that the preservative solution at 2% DBF concentration provides lasting protection against wood degradation owing to the amount of DBF remaining in the wood after severe weathering process. However field tests are needed to determine the performance of surface-treated wood with DBF and the acryl-silicon type resin in more realistic conditions.
Zusammenfassung
Oberflächenbehandlung von Holz wurde mit einem Acryl-Silikon Harz einschließlich Didecyl – Dimethyl – Ammonium – Tetrafluorborat (DBF) vorgenommen, eine borhaltige quaternäre Ammonium - Komponente. Oberflächenbehandelte Holzproben wurden nach dem Durchlaufen 10 vollständiger strenger Witterungszyklen im Labor Fäulnisresistenztests unterzogen. Dabei wurden ein Braunfäulepilz Domitopsis palustris und ein Weißfäulepilz, Trametes versicolor benutzt. Mit denselben Proben wurden im Labor auch Termitenresistenzversuchen mit der unterirdischen Termitenart Coptotermes formosanus durchgeführt. Proben, die mit 2% DBF und einem konservierungsmittelhaltigem Harz behandelt waren, zeigten verbesserte Fäulnis- und Termitenresistenz, was nahe legte, dass die Konservierungslösung mit 2%iger DBF - Konzentration dauerhaften Schutz gegen Holzabbau liefert, auf Grund der Menge an DBF, die nach dem strengen Witterungsprozess im Holz verbleibt. Um die Dauerhaftigkeit der Resistenz von Holz, dessen Oberfläche mit DBF und Acryl-Silicon - Harz behandelt wurde, festzustellen, sind allerdings Freilandversuche unter wirklichkeitsnahen Bedingungen erforderlich.
Similar content being viewed by others
References
AWPA (1999) Book of standards. Woodstock, MD: American Wood Preservers’ Association
Carretti E, Dei L (2004) Physicochemical characterization of acrylic polymeric resin coating porous materials of artistic interest. Progress in Organic Coatings 49(3): 282–289
Jin L, Archer K (1991) Copper based wood preservatives: Observations on fixation, distribution and performance. In: Proceedings, American Wood Preservers’ Association 7: 169–184
JIS (1991) Qualitative standards and testing methods of wood preservatives. Japanese Industrial Standards (JIS) JIS A 9201. Japanese Standards Association, Tokyo
JWPA (2001) Laboratory test method to evaluate effectiveness of termiticides for pressure treatment and performance requirements of the treated materials. JWPS-TW-P.1. Japanese Wood Preserving Association (JWPA), Tokyo
Kartal SN, Hwang WJ, Shinoda K, Imamura Y (in press) Laboratory evaluation of boron-containing quaternary ammonia compound, didecyl dimethyl ammonium tetrafluoroborate (DBF) for control of decay and termite attack and fungal staining of wood. Holz Roh- Werkstoff
Kartal SN, Shinoda K, Imamura Y (2005) Laboratory evaluation of boron-containing quaternary ammonia compound, didecyl dimethyl ammonium tetrafluoroborate (DBF) for inhibition of mold and stain fungi. Holz Roh- Werkstoff 63:73–77
Lebow ST (1996) Leaching of wood preservative components and their mobility in the environment. Summary of pertinent literature. Gen. Tech. Rpt. FPL–GTR–93. U.S. Dept. Agriculture, Forest Service, Forest Products Laboratory, Madison
Loubinoux B, Malek H, Joly JP, Kilbertus G (1992) Interaction of quartenary ammonium salts with wood: influence of cation and anion structure on fixation and leaching. Forest Products Journal 42(10): 55–58
Preston AF, Walcheski PJ, McKaig PA, Nicholas DD (1987) Recent research on alkylammonium compounds in the U.S. In: Proceedings, American Wood Preservers’ Association 83: 331–348
Vinden P, Romero J (1997) Developments in the application of organic boron compounds. In: Proceedings of the Second International Conference on Wood Protection with Diffusible Preservatives and Pesticides. Forest Products Society, Madison, WI, USA. Proceedings No. 7284, pp. 119–126
Wood Handbook (1999) Wood Handbook- Wood as an engineering material. U.S. Department of Agriculture, Forest Service, Forest Products Laboratory, Madison, WI, USA. Gen. Tech. Rep. FPL-GTR-113, 463 p
Wu CS, Liu YL, Chiu YS (2002) Epoxy resins possessing flame retardant elements from silicon incorporated epoxy compounds cured with phosphorus or nitrogen containing curing agents. Polymer 43:4277–4284
Acknowledgements
The authors gratefully acknowledge the support of Japan Society for the Promotion of Science (JSPS).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hwang, W.J., Kartal, S.N., Shinoda, K. et al. Surface treatment for preventing decay and termite attack in wood using didecyl dimethyl ammonium tetrafluoroborate (DBF) incorporated with acryl-silicon type resin. Holz Roh Werkst 63, 204–208 (2005). https://doi.org/10.1007/s00107-004-0558-y
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00107-004-0558-y