Abstract
Ag, Fe undCu, Fe alloys of high concentration (up to 20 at %), which cannot be produced as solid solution in bulk, are produced by the simultaneous condensation of both the components on a substrate at a temperature of 4.2 or 78 K. By cooling the two alloys show a minimum and a maximum of the electric resistance, both dependent on concentration and annealing temperature. In contrast toAg, Fe theCu, Fe alloys with more than 3,5 at % show an additional minimum at temperatures between 10 and 1 K, which disappears if the samples are annealed at 380 K.
Similar content being viewed by others
Literatur
Meißner, W., Voigt, G.: Ann. Phys.7, 761 (1930)
van den Berg, G.J.: Progress in LTP, Vol. IV. Amsterdam: North-Holland Publ. Co. 1964
Kondo, J.: Prog. Theoret. Phys.32, 37 (1964)
Fischer, K.H.: Phys. Stat. Sol.46, 11 (1971)
Hauser, J.J.: Phys. Rev. B, Vol. 5, Nr. 1, 110 (1972)
Hauser, J.J., Lim, C.S., Leslie, J.D.: Phys. Rev. B, Vol. 3, Nr. 7, 2211 (1971)
Knorr, K., Hamann, D.R., Kammlott, G.W.: Sol. State Commun.10, 637 (1972)
Tholence, J.L., Tournier, R.: Phys. Rev. Letters, Vol. 25, Nr. 13, 867 (1970)
Hansen, M., Anderko, K.: Const. of binary alloys, 2nd ed. New York 1958
Buckel, W., Hilsch, R.: Z. Physik132, 420 (1952)
Wassermann, E.: Z. Physik187, 369 (1965)
Tolansky, S.: Multiple-beam interferometry. Oxford: University Press 1948
v. Bassewitz, A., v. Minnigerode, G.: Z. Physik181, 368 (1964)
Korringa, J., Gerritsen, A.N.: Physica19, 457 (1953)
Yosida, K.: Phys. Rev.107, 396 (1957)
van Dam, J.E., van den Berg, G.J.: Phys. Stat. Sol. A3, 11 (1970)
Gerritsen, A.N., Linde, J.O.: Physica17, 573 (1951)
Linde, J.O.: Proc. 5th Int. Conf. Low Temp. Phys. Chem. Madison 1957, 402
Korn, D.: Z. Physik238, 275 (1970)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kaufmann, K. Elektrischer Widerstand von metastabilenAg, Fe- undCu, Fe-Legierungen bei tiefen Temperaturen. Z Physik B 22, 117–120 (1975). https://doi.org/10.1007/PL00020763
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/PL00020763