The solid solubility of iron in 2 to 10 pct cupro-nickels increases with temperature and nickel content. Property changes accompanying various heat treatments indicate typical precipitation hardening behavior. Iron content also affects softening temperature and subscale formation. These factors, as well as impingement corrosion resistance, influence the optimum iron content of commercial alloys.
Similar content being viewed by others
References
A. W. Tracy and R. L. Hungerford: Proc. A.S.T.M. (1945) 45, p. 591.
J. R. Freeman, Jr. and A. W. Tracy: Corrosion (1949) 5, p. 245.
G. Tammann and W. Oelsen: Ztsch. anorg. allgem. Chem. (1930) 186, p. 257.
A. J. Bradley, W. F. Cox, and H. J. Goldschmidt: Journal Inst. Metals (1941) 67, p. 189.
G. Chaudron: Journal Inst. Metals (1949) 76, p. 1.
R. B. Gordon and M. Cohen: Symposium on Precipitation Hardening. A.S.M., Chicago (October 1949).
P. J. E. Forsyth, G. J. Metcalfe, R. King, and B. Chalmers: Nature (London) (1946) 158, p. 875.
G. L. Bailey: Journal Inst. Metals (1951) 79, p. 243.
Author information
Authors and Affiliations
Additional information
Discussion on this paper, TP 3203E, may be sent, 2 copies, to AIME by April 1, 1952. Manuscript, Aug. 23, 1951. New York Meeting, February 1952.
Rights and permissions
About this article
Cite this article
Palmer, E.W., Wilson, F.H. Constitution and Properties of Some Iron-Bearing Cupro-Nickels. JOM 4, 55–64 (1952). https://doi.org/10.1007/BF03397649
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF03397649