Abstract
Ferritic stainless steel X2CrNi12 (EN 10088) is generally appreciated for its relatively low cost and good resistance to wet abrasion and mild environments, but unfortunately its weldability is restricted. Typical applications up to now include railway wagons for coal and iron ore, mining and mineral process and transport equipment, bus frames and chassis, silos, etc. This steel grade nowadays can be fabricated cost effectively with low carbon and impurity levels appreciably improving both the weldability and mechanical properties. In this case, long-term maintenance costs of assemblies produced using this ‘clean’ X2CrNi12 stainless steel will be low, with a suitable coating providing sufficient protection for several decades. For other applications, the use of weldable X2CrNi12 is also more economical than higher alloyed stainless steels. Moreover, joining the steel by laser welding without filler metal should be considered. The present paper provides an overview of results of a research project initiated by the Belgian Welding Institute investigating the possibilities of this modified low carbon ferritic stainless steel. The main objective of this work was to demonstrate that it offers great application ranges for constructing purposes which should expand its application field substantially. In the near future broadening this steel family with even higher mechanical properties allowing further reduction of plate or wall thickness and of production costs will be explored.
Similar content being viewed by others
References
du Toit M., van Rooyen G.T., Smith D.: An overview of the heat-affected zone sensitization and stress corrosion cracking behaviour of 12% chromium type 1.4003 ferritic stainless steel, Doc. IIW-1814-07 (ex-doc IX-2213-06/IX-H-640–06), Welding in the World, 2007, vol. 51, no. 9/10, pp. 41–50.
Topic M., Allen C., Tait R.: The effect of cold work and heat treatment on the fatigue behaviour of 3Cr12 corrosion resistant steel wire, International Journal of Fatigue, 2007, vol. 29, issue 1, pp. 49–56.
Ball A., Chauvan Y., Schaffer G.B.: Microstructure, phase equilibria and transformations in corrosion resistant dual phase steel designated 3Cr12, Material Science and Technology, 1987, 3, pp. 189–196.
Pagani S.M., Robinson F.P.A.: Microstructure and mechanical and electrochemical properties of martensitic weld deposits developed for welding of a 12% chromium duplex stainless steel, Material Science and Technology, 1998, 4, pp. 554–559.
Knutsen R.D., Hutchings R.: The influence of inclusions on the corrosion behaviour of a 12 wt percent chromium steel, Corrosion, Materials Science and Technology, 1988, 4, pp. 127–135.
van Lelyveld C., van Bennekom A.: Autogeneously welded 3Cr12 tubing for use in the sugar industry, Stainless Steel, 1995, September-October, pp. 16–18.
Bennet P.: The Weldability of 12% chromium ferritic corrosion-resisting steels, Material Australia, 1991, June, pp. 15–17.
Moore P.: 3Cr12-Welding the 12% Chromium utility stainless steel, Australian Welding Journal, 1997, vol. 42, Third Quarter, pp. 22–24.
NIROSTA 4003: Thyssen Krupp Nirosta, Germany. www.nirosta.de
Columbus Stainless Technical Data 3Cr12. Columbus Stainless Pty. Ltd. 2002, www.columbusstainless.co.za
Deleu E., Dhooge A.: Ferritic stainless steel XCrNi12 with improved weldability for structural applications, Proceedings Stainless Steel World 2005, pp. 160–166.
Deleu E., Dhooge A.: 12Cr ferritisch roestvast staal voor primaire constructies (12Cr ferritic stainless steel for primary structures), Proceedings BIL/NIL Lassymposium, November 2005, Session 7 (in Dutch).
Taban E., Deleu E., Dhooge A., Kaluc E.: Gas metal arc welding of modified X2CrNi12 ferritic stainless steel, Kokove materially, Metallic Materials, 2007, vol. 45, issue 2, pp. 67–73.
Gooch T.G., Ginn B.J.: Welding Institute Members Report 373/1988: 6–7.
Greef M.L., du Toit M.: Looking at the sensitization of 11–12% chromium EN 14003 stainless steels during welding, Welding Journal, 2006, vol. 85, no. 11, pp. 234s–251s.
Marshall A.W., Farrar J.C.M.: Welding of ferritic and martensitic 11–14% Cr steels, Doc. IIW-1499-00 (ex-doc IX-1975–00), Welding in the World, 2001, vol. 45, no. 5/6, pp. 32–55.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Deleu, E., Dhooge, A., Taban, E. et al. Possibilities and Limitations to Improve the Weldability of Low Carbon 12Cr Ferritic Stainless Steel for Expanded Industrial Applications. Weld World 53, R198–R208 (2009). https://doi.org/10.1007/BF03321131
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF03321131