Abstract
Zinc-aluminum (ZA) alloys are a relatively new family of zinc foundry alloys having superior melting and casting characteristics and attractive mechanical properties. The ZA-8 and ZA-12 alloys are moderate to high strength materials while ZA-27 is a high-strength alloy. All can be sand cast, permanent molded and pressure die cast.
An extensive characterization program is being implemented to develop appropriate and reliable engineering data for designers. Property development in all aspects of ZA metallurgy is welladvanced. The data available on selected physical and mechanical properties of ZA alloys is compared here with the properties of traditional casting alloys.
Similar content being viewed by others
References
E. Gervais, H. Levert and M.L. Bess, “Development of a Family of Zinc Base Foundry Alloys,” Transactions of the American Foundrymen’s Society, Vol. 88, p. 183–194 (1980).
E.A. Anderson, “The Development of Zinc Die Casting Alloys,” Transactions of the 5th SDCE International Die Casting Congress, Detroit, Michigan, U.S.A., Technical Paper No. 115, November 1968.
E. Gervais and C.A. Loong, “New ZA Alloys in Die Casting,” Proceedings of the 11th International Pressure Die Casting Conference, Lyon, France, June 1984.
R.J. Barnhurst, E. Gervais and F.D. Bayles, “Gravity Casting of Zinc-Aluminum Alloys-Solidification Behaviour of ZA-8, ZA-12 and ZA-27,” AFS Transaction, Vol. 91, p. 569–584 (1983).
C.J. Smithells and E.A. Brandes, Metals References Book, 5th ed. p. 1432, Butterworth & Co. (Publishers) Ltd., (1976).
E.A. Anderson and G.L. Werley, “A New Zinc Alloy for Gravity Casting,” ILZRO Research Summary, Project ZM-5, July 1962.
A.C. Street, The Die Casting Book, Portcullis Press, Ltd., p. 197 (1977).
R.I. Stephens, “An Engineer’s Guide to Fracture Mechanics,” Automotive Engineering, Vol. 12, p. 36–42 (1981).
W.R. Tyson, “Fracture Control: Current Issues,” Canadian Metallurgical Quarterly, Vol. 22, p. 219–224 (1983).
CM. Hudson and S. Seward, “A Compendium of Sources of Fracture Toughness and Fatigue-Crack Growth Data for Metallic Alloys,” Parts I and II, International Journal of Fracture, 14, 1978, R151–184 and 20, 1982, R59–117.
P. Dionne, J.I. Dickson and J-P. Bailon, “The Influence of As-Cast Microstructure on the Fracture Toughness of a Zn-Al Foundry Alloy,” AFS Transactions, Vol. 92 (1984).
ASME Boiler and Pressure Vessel Code, Section VIII, Division I-Pressure Vessels, 1977 Edition and Addenda (1979).
R.W. Balliet, “Mechanical Properties of Creep Resistant Die Casting Alloys,” Society of Die Casting Engineers, 8th International Congress, Detroit, Michigan, U.S.A., 1975, Paper No. G-T 75-013.
ILZRO Project ZM-67, British Non-Ferrous Metals Technology Centre, Report A 1458 (1963).
P. Dionne, Personal communication to R.J. Barnhurst, April 1984.
Additional information
E. Gervais received his D.Sc. from Ecole Polytechnique, the engineering school affiliated with the University of Montreal, in 1968. He is currently Head of the Product Engineering Division of the Noranda Research Centre, Pointe Claire, Quebec, Canada. Dr. Gervais is also a member of TMS.
R.J. Barnhurst received his Ph.D. in metallurgy from McGill University, Montreal, in 1983. He is currently Research Scientist in the Physical Metallurgy Department, Noranda Research Centre, Pointe Claire, Quebec, Canada.
C.A. Loong received his Ph.D. in industrial metallurgy from the University of Birmingham, U.K., in 1974. He is currently Senior Research Scientist in the Physical Metallurgy Department, Noranda Research Centre, Pointe Claire, Quebec, Canada.
Rights and permissions
About this article
Cite this article
Gervais, E., Barnhurst, R.J. & Loong, C.A. An Analysis of Selected Properties of ZA Alloys. JOM 37, 43–47 (1985). https://doi.org/10.1007/BF03258743
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF03258743