Abstract
Solute diffusion occurs in the solid state through interactions between lattice defects and specific solute species. This article describes calculations and measurements of major solute diffusion parameters in irradiated austenitic stainless steels at temperatures below 500 °C. Calculated diffusivity parameters are shown to be in accord with high-temperature, thermal-diffusion experiments. The predictions are used to understand irradiation-assisted stress corrosion cracking as it relates to chromium depletion at irradiated grain boundaries.
Similar content being viewed by others
References
P.L. Andersen, “Irradiation-Assisted Stress Corrosion Cracking,” Stress Corrosion Cracking, ed. R. Jones (Materials Park, OH: ASM, 1992).
P. Scott, J. Nucl. Mater., 211 (1994), p. 101.
J.O. Stiegler, ed. “Workshop on Solute Segregation and Phase Stability During Irradiation,” J. Nucl. Mater., 83 (1979).
A.D. Marwick, J. Phys. F. Metals Phys., 8 (1978), p. 1849.
J.M. Perks and S.M. Murphy, “Modeling the Major Element Radiation-Induced Segregation in Concentrated Fe-Cr-Ni Alloys,” Proc. Materials for Nuclear Reactor Core Applications, vol. 1 (London: BNES, 1987), p. 119.
K.P. Simonen, L.A. Charlot, and S.M. Bruemmer, J. Nucl. Mater., 225 (1995), p. 117.
S.M. Bruemmer et al., “Radiation-Induced Grain Boundary Segregation in Austenitic Stainless Steels,” Microstructure of Irradiated Materials, vol. 373, ed. L.M. Robertson et al. (Pittsburgh, PA: MRS, 1995), p. 119.
A.C. Hindmarsh, GEAR: Ordinary Differential Equation System Solver, Report UCID-3000l, rev. 3, Lawrence Livermore Laboratory, Livermore, CA (1974).
S.M. Bruemmer, M.D. Merz and L.A. Charlot, J. Nucl. Mater., 186 (1991), p. 13.
D.L. Damcott, T.R. Allen, and G.S. Was, J. Nucl. Mater., 225 (1995), p. 97.
D.L.R. Norris, C. Baker, and J.M. Titchmarsh, “CompOSitional Profiles at Grain Boundaries in 20%Cr/25%Ni/Nb Stainless Steel,” Proceedings of Symposium on Radiation-Induced Sensitization of Stainless Steels (Held at Berkeley Nuclear Laboratories, September 1986, CEGB, INIS-GB-90), p. 86.
S.J. Rothman, L.J. Norwicki, and G.E. Murch, J. Phys. F. Metal Phys., 10 (1980), p. 383.
K.P. Simonen and S.M. Bruemmer, “Radiation-Induced Segregation: A Microchemical Gauge to Quantify Fundamental Defect Parameters,” Microstructure of Irradiated Materials, ed. L.M. Robertson et al. (Pittsburgh, PA: MRS, 1995), p. 95.
D.L. Damcott, G.S. Was, and S.M. Bruemmer, “Proton Irradiation Induced Grain Boundary Segregation in Austenitic Stainless Steels,” Microstructure of Irradiated Materials, vol. 373, ed. L.M. Robertson et al. (Pittsburgh, PA: MRS, 1995), p. 131.
C. Dimitrov and O. Dimitrov, J. Nucl. Mater., 152 (1988), p. 21.
S.M. Bruemmer, “Quantitative Modeling of Sensitization Development in Austenitic Stainless Steel” (Paper presented at Corrosion 89, National Association of Corrosion Engineers, 1989).
S.M. Bruemmer, L.A. Chariot, and K.P. Simonen, “Measurement and Modeling of Radiation-Induced Grain Boundary Segregation in Austenitic Stainless Steet,” Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Houston, TX: NACE, 1995), p. 971.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Simonen, E.P. Diffusivities from the calculation and measurement of radiation kinetics. JOM 48, 34–37 (1996). https://doi.org/10.1007/BF03223264
Issue Date:
DOI: https://doi.org/10.1007/BF03223264