Abstract
Experiments have been conducted to examine the effects of binder composition on the mechanical properties of injection-molded, carbonyl iron sintered products. A solvent extraction debinding technique was used to quickly remove the binder and carefully control the carbon content. A high content of high molecular weight backbone binder component gives rise to a higher flow viscosity, but does not significantly enhance the green strength. The addition of a small amount of stearic acid can improve moldability by reducing the flow viscosity. A variance in sintered properties is related to the difference in carbon content and final grain size.
Similar content being viewed by others
References
D. Poniatowski and G. Will, “Injection Molding of Tungsten Carbide Base Hard Metals,” Metal Powder Report, 43(12) (1988), pp. 812–815.
B.K. Lograsso et al., “Baseline System for Powder Injection Molding: Iron-Polyethylene,” paper presented at 1989 TMS Annual Meeting, Las Vegas, NV (Feb. 1989).
B.J. Carpenter, “Melt Rheology of Iron Powder/Wax Mixtures,” M.S. thesis, Rensselaer Polytechnic Institute, 1988.
R.E. Wiech, Jr., “Method for Rapidly Removing Binder from Green Body,” U.S. patent no. 4,661,315 (April 28, 1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hens, K.F., Lin, S.T., German, R.M. et al. The effects of binder on the mechanical properties of carbonyl iron products. JOM 41, 17–21 (1989). https://doi.org/10.1007/BF03220296
Issue Date:
DOI: https://doi.org/10.1007/BF03220296