Abstract
Electron paramagnetic resonance has been used to study the structure and thermostability of oxygen hole centers produced in KTiOPO4 (KTP) crystals X-irradiated at 77 K. During the annealing of KTP crystals above 160 K the redistribution of charges took place. Four hole centers were observed at 40 K after the heating of the X-irradiated KTP crystal at different temperatures. The intensity of the hole center 1 decreased and new hole configurations (center 2 and center 3) appeared in the crystals. Theg-matrices were obtained from the angular dependencies of EPR spectra. The principalg-values for center 1 were 2.0040, 2.0209, and 2.0437. The principalg-values for centers 2 and 3 were 2.0053, 2.0204, 2.0431 and 2.0035, 2.0183, 2.0628, respectively. The transformation of Ti3+ spectra indicated that the trivalent titanium ions were involved into the recombination process. Subsequent annealing at temperatures above 220 K led to the formation of a new hole center 4 (g a =2.0213,g b =2.0236,g c =2.0370).
Similar content being viewed by others
References
Ouvrand M.L.: Comp. Rend. Acad. Sci.111(3), 117–119 (1890)
Masse R.J., Clenler G.: Bull. Soc. Franc. Mineral. Crist.94, 437–439 (1971)
Zumsteg F.C., Bierlein J.D., Gier T.E.: J. Appl. Phys.47(11), 4980–4985 (1976)
Bierlein J.D., Gier T.E.: US Patent 3, 949, 323. April 6 (1976)
Driscoll T.A., Hoffman H.J., Stone R.E., Perkins P.E.: J. Opt. Soc. Am.3, 683 (1986)
Roelofs M.G.: J. Appl. Phys.65, 4976–4982 (1989)
Scripsick M.P., Edwards G.J., Halliburton L.E., Belt R.F.: J. Appl. Phys76(6) 2991–2994 (1991)
Nizamutdinov N.M., Khasanova N.M., Bulka G.R., Vinokurov V.M., Rez I.S., Garmash V.M., Pavlova N.I.: Sov. Phys.-Crystallogr.32, 408–413 (1987)
Bulka G.R., Belonogova E.K., Ermakov G.A., Nizamutdinov N.M., Pavlova N.I.: Laser Technics and Optoelectronics, part 11, issue 12(1587). Moscow: Electronica Press 1990. (in Russian)
Martin M.J., Bravo D., Sole R., Diaz F., Lopez F.J., Zaldo C.: J. Appl. Phys.76(11), 7510–7517 (1994)
Andreev B.V., Efimov V.N.: Mod. Phys. Lett. B6, 177–181 (1992)
Yu J.T., Lee C.H., Ziu K.T., Ziu C.L., Huang Y., Payne D.A., Zii K.H.: J. Phys. Chem. Solids56(2), 233–240 (1995)
Scripsick M.P., Lolacono D.N., Rottenberg J., Goellner S.H., Halliburton L.E., Hopkins F.K.: Appl. Phys. Lett.66(25), 3428–3430 (1995)
Tordjman I., Masse R., Guitel J.C.: Z. Kristalogr.139, 103 (1974)
Edwards G.J., Scripsick M.P., Halliburton L.E., Belt R.F.: Phys. Rev. B48(10), 6884–6891 (1993-II)
Mangin J., Jeandel G., Marnier G.: Phys. Status Solidi A117(1), 319–323 (1990)
Pisarev R.V., Kizhaev S.A., Jamet J.P., Ferre J.: Solid State Commun.72(2), 155–158 (1989)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Laruhin, M.A., Efimov, V.N. & Nazarova, V.A. New hole configurations in X-irradiated KTiOPO4 Crystals. Appl. Magn. Reson. 12, 517–527 (1997). https://doi.org/10.1007/BF03164132
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF03164132