Synthesis of dense MoSi2 by high-frequency induction heated combustion and its mechanical properties

  • Published:
Metals and Materials International Aims and scope Submit manuscript


Dense MoSi2 compound was synthesized with the high-frequency induction heated combustion synthesis method in one step from elemental powders of Mo and Si within 2 min. Simultaneous combustion synthesis and densification were carried out under the combined effects of induced current and mechanical pressure. A highly dense MoSi2 with a relative density of up to 98% was produced with simultaneous application of 60 MPa pressure and induced current. The percentages of the total shrinkage occurring before and during the synthesis reaction were 16% and 53%, respectively. The average grain size was about 15 μm and a slight amount of Mo5Si3 was observed at the boundaries of the MoSi2 grains. The fracture toughness and hardness values obtained were 3.5 MPa·m1/2 and 1050 kg/mm2, respectively. These values were similar to those of commercial ones.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Subscribe and save

Springer+ Basic
EUR 32.99 /Month
  • Get 10 units per month
  • Download Article/Chapter or Ebook
  • 1 Unit = 1 Article or 1 Chapter
  • Cancel anytime
Subscribe now

Buy Now

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others


  1. A. K. Vasudevan and J. J. Petrovic,Mater. Sci. Eng. A 155, 1 (1992).

    Article  Google Scholar 

  2. J. Milne,Instant Heat, Kinetic Metals Inc., Derby, CT (1985).

    Google Scholar 

  3. Y. S. Touloukian, R. W. Powell, C. Y. Ho, and P. G. Klemens,Thermal Conductivity, p. 1324, P.G. IFI/Plenum, New York (1970).

    Google Scholar 

  4. J. D. Cotton, Y. S. Kim, and M. J. Kaufman,Mater. Sci. Eng. A 144, 287 (1991).

    Article  Google Scholar 

  5. B. Aronsson, T. Lundstrom, and S. Rundquist,Borides, Silicides, and Phosphides, p. 1, Wiley, New York (1965).

    Google Scholar 

  6. R. Wenrman,High-Materials and Technology (eds., I. E. Campbell and E. M. Sherwood), p. 399, Wiley, New York (1967).

    Google Scholar 

  7. Z. A. Munir, I. J. Shon, and K. Yamazaki,U. S. Patent, No. 5,794,113 (1998).

  8. I. J. Shon, Z. A. Munir, K. Yamazaki, and K. Shoda,J. Am. Ceram. Soc. 79, 1875 (1996).

    Article  CAS  Google Scholar 

  9. I. J. Shon, H. C. Kim, D. H. Rho, and Z. A. Munir,Mater. Sci. Eng. A 269, 129 (1999).

    Article  Google Scholar 

  10. I. J. Shon, D. H. Rho, H. C. Kim, and Z. A. Munir,J. Alloys & Compounds 322, 120 (2001).

    Article  CAS  Google Scholar 

  11. I. J. Shon, D. H. Rho, and H. C. Kim,Metals and Materials 6, 533 (2000).

    Article  CAS  Google Scholar 

  12. C. D. Park, H. C. Kim, and I. J. Shon,Metals and Materials Int. 8, 253 (2002).

    Article  CAS  Google Scholar 

  13. Z. A. Munir,J. Mater. Synth. Process 1, 387 (1993).

    CAS  Google Scholar 

  14. S. C. Deevi,J. Mater. Sci. 26, 3343 (1991).

    Article  ADS  CAS  Google Scholar 

  15. S. W. Jo, G. W. Lee, J. T. Moon, and Y. S. Kim,Acta metall. 44, 4316 (1996).

    Google Scholar 

  16. G. R. Anstis, P. Chantikul, B. R. Lawn, and D. B. Marshall,J. Am. Ceram. Soc. 64, 533 (1981).

    Article  CAS  Google Scholar 

  17. T. E. Mitchell, R. G. Castro, and H. H. Charwick,Philos. Mag. A 65, 1339 (1992).

    Article  ADS  CAS  Google Scholar 

  18. J. B. Beukowitz-Mattuck, M. Rossett, and D. W. Lee,Metall. Trans. 1, 1479 (1970).

    Google Scholar 

  19. A. K. Bhattacharya and J. J. Petrovic,J. Am. Ceram. Soc. 74, 2700 (1991).

    Article  CAS  Google Scholar 

  20. R. K. Wade and J. J. Petrovic,J. Am. Ceram. Soc. 75, 1682 (1992).

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations


Corresponding author

Correspondence to In Jin Shon.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Kim, H.C., Park, C.D., Jeong, J.W. et al. Synthesis of dense MoSi2 by high-frequency induction heated combustion and its mechanical properties. Met. Mater. Int. 9, 173–178 (2003).

Download citation

  • Issue Date:

  • DOI: