Abstract
The effects of Fe addition and initial powder size distribution on mechanical properties of Al-20Si-3Cu-lMg alloy, prepared by gas atomization and followed by hot consolidation, were studied by using optical microscopy, transmission electron microscopy, X-ray diffractometry, tensile and wear test. The Al-20Si-xFe-3Cu-lMg (x=0, 5) alloys showed homogeneous and refined microstructure. Addition of Cu and Mg to Al-20Si alloy showed increased tensile property due to precipitation hardening. Addition of Fe to Al-20Si-3Cu-lMg increased tensile strength further due to the formation of spherical Al-Si-Fe compound during hot consolidation and phase transformed from the metastable phase. Alloy bars prepared from powder with wide-size distribution showed low tensile strength and wear resistance.
Similar content being viewed by others
References
T. Hayashi, T. Kaji, Y. Takeda, Y. Odani and K. Akechi,Sumitomo Electric Technical Review 34, 107 (1992).
Z. Zhou, J. Duszczyk and B. M. Korevaar,J. Mater. Sci. 26, 824 (1991).
T. S. Kim, S. J. Hong, W. T. Kim and B. S. Chun,.J. Korean Pow. Metall. Inst. 1, 66 (1994).
M. D. Hanna, S. Lu and A. Hellawell,Metall. Trans. ISA, 459 (1984).
T. S. Kim, S. J. Hong, W. T. Kim and B. S. Chun,Mater. Sci. Eng. A226, 878 (1997).
J. L. Estrada and J. Duszczyk,J. Mater. Sci. 25, 886 (1990).
N. Amano, Y.Odani, Y. Takeda and K. Akechi,MPR, March, 186 (1983).
J. M. Papazian,Metall Trans. 13A, 761 (1982).
J. L. Murray,Int. Met. Rev. 30, 211 (1985).
L. F. Mondolfo,Al Alloys: Structure and Properties, p. 534, Butterworth & Co (publishers) Ltd., Boston, USA (1984).
K. Kondoh and Y. Takeda, inProceedings of 1993 Powder Metallurgy World Congress, p. 231, Japan Society of Powder and Powder Metallurgy, Kyoto (1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kim, T.S., Kim, K.H., Kim, W.T. et al. Microstructure and mechanical properties of rapidly solidified Al-20Si-xFe-3Cu-lMg (x=0 and 5 wt.%) Extradates. Metals and Materials 4, 1163–1169 (1998). https://doi.org/10.1007/BF03025990
Issue Date:
DOI: https://doi.org/10.1007/BF03025990