The effect of an external electric field on solid-state phase transition of (P(VDF/TrFE)(72/28)

Abstract

The copolymers of vinylidene fluoride and trifluoroethylene (P(VDF/TrFE)) with VDF content of 50–80 mole % can be applied to the field of nonvolatile ferroelectric polymeric random access memory (FePoRAM) devices, since they exhibit stable ferroelectricβ-phase at room temperature with spontaneous polarization of the C-F dipoles towards an external electric field greater than the coercive field. Many researchers have already reported the molecular structures and dynamics of the ferroelectric (F) crystalline phase and the unique change in chain conformation between polarF phase and non-polar paraelectric (P) phase near their Curie transition temperature (T c) which is dependent on factors such as VDF content and annealing treatment conditions. The effect of external electric field strength on theFP crystalline phase transition in P(VDF/TrFE)(72/28) random copolymer samples of nanometer thickness was investigated. Capacitance of 250 nm thick sample measured as a function of heating-cooling under varying external electric field strength exhibited increasingT c’s during heating (T c ) and cooling (T c ) under an applied electric field of more than 0.03 MV/cm. Applying cyclic bias electric field (+1 to −1 MV/cm) for samples kept isothermally at just above theirT c(T c ) during cooling, we were able to observe the field-inducedPF phase transition. With increasing cycles of the applied electric field for sample maintained just above (T c ), the bistableC-E hysteresis was observed and the phase change fromPF is irreversible even after the electric field is removed. However, for samples kept well above (T c ) and nearT m (100 °C and 120°C respectively) during cooling, theF-phase initially formed through the field-induced phase transition is reversibly transformed to theP-phase when the applied electric field is removed. Drastic changes were observed in both coercive field (E c) and remanent polarization (P r) values during heating and cooling near theT c range due to theFP phase transition and the results are reported in detail here.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    T. Furukawa, M. Date, E. Fukada, Y. Tajitsu, and A. Chiba,Jpn. J. Appl. Phys.,19(2), L109 (1980).

    Google Scholar 

  2. 2.

    A. J. Lovinger,Macromolecules,16, 1529 (1983).

    Article  CAS  Google Scholar 

  3. 3.

    K. J. Kim, N. M. Reynold, and S. L. Hsu,J. Polym. Sci. Poly. Phys.,31, 1555 (1993).

    CAS  Article  Google Scholar 

  4. 4.

    R. Tanaka, K. Tashiro, and M. Kobayashi,Polymer,40, 3855 (1999).

    Article  CAS  Google Scholar 

  5. 5.

    K. Urayama, M. Tsuji, and D. Neher,Macromolecules,33, 8269 (2000).

    Article  CAS  Google Scholar 

  6. 6.

    Q. M. Zhang, H. Xu, F. Fang, Z.-Y. Cheng, F. Xia, and H. You,J. Appl. Phys.,89, 2613 (2001).

    Article  CAS  Google Scholar 

  7. 7.

    F. Xia, H. S. Xu, B. Razavi, Z.-Y. Cheng, and Q. M. Zhang,Ferroelectrics,273, 377 (2002).

    CAS  Google Scholar 

  8. 8.

    T. Yamada, T. Ueda, and T. Kitayama,J. Appl. Phys.,52(2), 948 (1981).

    Article  CAS  Google Scholar 

  9. 9.

    T. Yamada and T. Kitayama,J. Appl. Phys.,52(11), 6859 (1981).

    Article  CAS  Google Scholar 

  10. 10.

    A. J. Lovinger,Science,220(4602), 1115 (1983).

    Article  CAS  Google Scholar 

  11. 11.

    K. Kimura and H. Ohigashi,Appl. Phys. Lett.,43(9), 834 (1983).

    Article  CAS  Google Scholar 

  12. 12.

    K. Kimura and H. Ohigashi,Jpn. J. Appl. Phys.,25, 383 (1986).

    Article  CAS  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Kap Jin Kim.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Lee, J.S., Prabu, A.A., Kim, K.J. et al. The effect of an external electric field on solid-state phase transition of (P(VDF/TrFE)(72/28). Fibers Polym 8, 456 (2007). https://doi.org/10.1007/BF02875865

Download citation

Keywords

  • P(VDF/TrFE)
  • Nonvolatile memory
  • FePoRAM
  • Ferroelectric crystalline phase
  • Paraelectric crystalline phase
  • Field-induced phase transition