Abstract
Silver-clad tapes of highT c Bi-Pb-Sr-Ca-Cu-O superconductors have been fabricated through the powder-in-tube method. The critical current density, J c , of a thick tape was 534 A.cm−2 (77 K, 0 T). Subsequent rolling and sintering of the tapes led to a gradual decrease inJ c, instead of the expected increase. This was caused by the microcracks developed in the core material by a rather drastic reduction during the rolling of the tapes. A modified and well controlled rolling technique, on the other hand, resulted in much improvedJ c values. Repeated rolling and sintering resulted in a good grain alignment and no microcracks were observed. In the present studies, maximumJ c of 1846 A.cm−2 (77 K, 0 T) and 2.43 × 104 A.cm−2 (4.2 K, 0 T) have been obtained Optimization of the processing and sintering parameters are expected to lead to still higherJ c values.
Similar content being viewed by others
References
Asano T, Tanaka Y, Fukotomi M, Jikihara K and Maeda H 1988Jpn. J. Appl. Phys. 28 L595
Green S M, Jiang C, Mei Y, Luo H L and Politis C 1988Phys. Rev. B38 5016
Heine K, Tenbrink J and Thorner M 1989Appl. Phys. Lett. 55 2441
Kase J, Togano K, Kumakura H, Dietderich D R, Irisawa N, Morimoto T and Maeda H 1990Jpn. J. Appl. Phys. 29 L1096
Kawashima M, Nagata M, Hosoda Y, Takano S, Shibuta N, Mukai H and Hikata T 1989IEEE Trans. Mag. 25 2168
Kumakura H, Togano K and Maeda H 1990J. Appl. Phys. 67 3443
Maeda, H, Tanaka Y, Fukotomi M and Asano T 1988Jpn. J. Appl. Phys. 27 L209
Mimura M, Kumakura K, Togano K and Maeda H 1989Appl. Phys. Lett. 54 1582
Okada M, Okayama A, Morimoto T, Mutsumoto T, Aihara K and Matsuda S 1988Jpn. J. Appl. Phys. 27 L185
Rajput R, Reddy Y S, Singh D P, Kundra K D and Sharma R G 1991Solid State Commun. 79 667
Sekine H, Inoue K, Maeda H and Numata K 1988 (Private Communication)
Sharma R G, Reddy Y S, Jha S R, Kundra K D and Suri D K 1988Pramana — J. Phys. 30 L75
Togano K, Kumakura, Maeda H, Yanagisiwa E, Irisawa N, Shimoyama J and Morimoto T 1989Jpn. J. Appl. Phys. 28 L95
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shukla, S.R., Reddy, Y.S., Pandya, D.K. et al. Role of processing in improving the critical current of Ag/BPSCCO tapes. Pramana - J Phys 37, 333–344 (1991). https://doi.org/10.1007/BF02848485
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02848485