Vapor phase equilibria in the Cd_1−xZn_xTe alloy system

Abstract

Cd_1−xZn_xTe compounds of different compositions have been prepared at temperatures ranging from 400 to 1000°C by annealing elemental Te in sealed quartz ampoules, in an atmosphere comprising vapors of Cd and Zn whose partial pressures were varied by varying the composition of the binary Cd_1−yZn_y alloys which provided the Cd and Zn vapors in these annealing experiments. The chemical compositions of the resulting Cd_1−xZn_xTe compounds have been analyzed using electron probe microanalytical techniques. Results indicate that presence of a 0.5%Zn along with Cd in a closed or semi-closed system may prove to be beneficial in preventing decomposition and/or formation of a metal/non metal phase during annealing of Cd_0.96Zn_0.04 Te substrates. Using the thermodynamic data in the literature for the binary Cd_1−yZn_y alloys and with the assumption that the activities of the Cd and Zn components are weakly dependent on temperature, the partial pressures of Cd and Zn in equilibrium with the Cd_1−xZn_xTe compounds at various temperatures have been evaluated.