Abstract
Small crack size accelerates corrosion fatigue propagation through high strength 4130 steel in aqueous 3 pct NaCl. The size effect is attributed to crack geometry dependent mass transport and electrochemical reaction processes which govern embrittlement. For vacuum or moist air, growth rates are defined by stress intensity range independent of crack size (0.1 to 40 mm) and applied maximum stress (0.10 to 0.95 Φys). In contrast small (0.1 to 2 mm) surface elliptical and edge cracks in saltwater grow up to 500 times faster than long (15 to 40 mm) cracks at constant δK. Small cracks grow along prior austenite grain boundaries, while long cracks propagate by a brittle transgranular mode associated with tempered martensite. The small crack acceleration is maximum at low δK levels and decreases with increasing crack length at constant stress, or with increasing stress at constant small crack size. Reductions in corrosion fatigue growth rate correlate with increased brittle transgranular cracking. Crack mouth opening, proportional to the crack solution volume to surface area ratio, determines the environmental enhancement of growth rate and the proportions of inter- and transgranular cracking. Small cracks grow at rapid rates because of enhanced hydrogen production, traceable to increased hydrolytic acidification and reduced oxygen inhibition within the occluded cell.
Similar content being viewed by others
References
A.J. McEvily and R. P. Wei:Corrosion Fatigue: Chemistry, Me- chanics and Microstructure, O. Devereaux, A. J. McEvily, and R.W. Staehle, eds., NACE, Houston, TX, 1973, pp. 381–95.
R. P. Wei and Gunchoo Shim:Corrosion Fatigue Mechanics: Metal- lurgy, Electrochemistry and Engineering, ASTM STP 801,T. W. Crooker and B.N. Leis, eds., ASTM, Philadelphia, PA, 1983, pp. 5–25.
P. M. Scott:Corrosion Fatigue Mechanics: Metallurgy, Electro- chemistry and Engineering, ASTM STP 801, T. W. Crooker and B.N. Leis, eds., ASTM, Philadelphia, PA, 1983, pp. 110–43.
R.N. Parkins:Metal Sci., 1979, vol. 13, pp. 381–86.
T. W. Crooker, S.J. Gill, G.R. Yoder, and F.D. Bogar:Environment-Sensitive Fracture: Evaluation and Comparison of Test Methods, ASTM STP 821, T. Dean, E. N. Pugh, and G.M. Ugiansky, eds., ASTM, Philadelphia, PA, 1984.
C. E. Jaske, D. Broek, J. E. Slater, and W. E. Anderson:Corrosion Fatigue Technology, ASTM STP 642, H. L. Craig, Jr., T. W. Crooker, and D.W. Hoeppner, eds., ASTM, Philadelphia, PA, 1978, pp. 1–47.
R. P. Wei:Fatigue Mechanisms, ASTM STP 675, J.T. Fong, ed., ASTM, Philadelphia, PA, 1979, pp. 816–31.
C.E. Jaske, J.H. Payer, and V. S. Balint: MCIC Report 81-42, Battelle, Columbus, OH, 1981.
R.P. Wei and G.W. Simmons:Int. J. Frac, 1981, vol. 17, pp. 235–47.
R.W. Hertzberg:Deformation and Fracture Mechanics of Engineer- ing Materials, 2nd ed., John Wiley and Sons, New York, NY, 1983, pp. 519–618.
B.F. Brown:Met. Rev., 1968, Review 129, pp. 171–83.
S. R. Novak and S. T. Rolfe:Corrosion, 1970, vol. 26, pp. 121–30.
S.R. Novak: Ph.D. Dissertation, University of Pittsburgh, Pitts- burgh, PA, 1977.
P. Shahinian and R. W. Judy, Jr.:Stress Corrosion— New Approaches, ASTM STP 610, H.L. Craig, Jr., ed., ASTM, Phila- delphia, PA, 1982, pp. 128–42.
O. Vosikovsky and R. J. Cooke:Int. J. Pres. Ves. Piping, 1978, vol. 6, pp. 113–29.
R.P. Gangloff:Advances in Crack Length Measurement, C.J. Beevers, ed., EMAS, London, 1982, pp. 175–230.
S. J. Hudak, Jr.:J. Engr. Math. Tech., 1981, vol. 103, pp. 26–35.
M.H. El Haddad, T.J. Topper, and B. Mukherjee:J. Test. Eval., 1981, vol. 9, pp. 65–81.
J.C. Newman, Jr.:Behavior of Short Cracks in Airframe Components, Conf. Proc. No. 328, AGARD, France, 1983, pp. 6.1–6.26.
R.O. Ritchie and S. Suresh:Matl. Sci. and Engr., 1983, vol. 57, pp. 27–30.
K.S. Chan and J. Lankford:Scripta Met., 1983, vol. 17, pp. 529–32.
J.F. McCarver and R.O. Ritchie:Matl. Sci. and Engr., 1982, vol. 55, pp. 63–67.
S. Suresh and R.O. Ritchie:Metall. Trans. A, 1982, vol. 13A, pp. 1627–31.
D. L. Davidson:Fat. Eng. Matl. Struc, 1981, vol. 3, pp. 229–36.
A. Rezrek, M.R. James, and W.L. Morris:Metall. Trans. A, 1983, vol. 14A, pp. 1697–705.
R. P. Gangloff and R. O. Ritchie:Fundamentals of Deformation and Fracture, K. J. Miller, ed., Cambridge University Press, Cambridge, in press, 1984.
R.P. Gangloff:Res. Mech. Let., 1981, vol. 1, pp. 299–306.
W.G. Clark, Jr.:Cracks and Fracture, ASTM STP 601, ASTM, Philadelphia, PA, 1976, pp. 138–53.
P. Doig and P. E. J. Flewitt:Metall. Trans. A, 1983, vol. 14A, pp. 978–83.
S. Usami and S. Shida:Fat. Engr. Matl. Struc, 1979, vol. 1, pp. 471–81.
D. Taylor and J.F. Knott:Fat. Eng. Matl. Struc., 1981, vol. 4, pp. 147–55.
R. J. Taunt and W. Charnock:Matl. Sci. and Engr., 1978, vol. 35, pp. 219–28.
F J. Bradshaw:Scripla Met., 1967, vol. 1, pp. 41–43.
B.R. Lawn:Mat. Sci. and Engr., 1974, vol. 13, pp. 277–83.
T. W. Weir, G. W. Simmons, R. G. Hart, and R. P. Wei:ScriptaMet., 1980, vol. 14, pp. 357–64.
A. Turnbull and J.G.N. Thomas:J. Electrochem. Soc., 1982, vol. 129, pp. 1412–22.
A. Turnbull:Br. Corros. J., 1980, vol. 15, pp. 162–71.
A. Turnbull:Corr. Sci., 1982, vol. 22, pp. 877–93.
W. H. Hartt, J. S. Tennant, and W. C. Hooper:Corrosion Fatigue Technology, ASTM STP 642, H. L. Craig, Jr., T. W. Crooker, and D.W. Hoeppner, eds., ASTM, Philadelphia, PA, 1978, pp. 5–18.
R. Alkire and D. Sutari:J. Electrochem Soc., 1979, vol. 26, pp. 15–22.
P. Doig and P. E. J. Flewitt:Corrosion, 1981, vol. 37, pp. 378–83.
B. Tompkins:Proc Conf. Influence of Environment on Fatigue, Inst. Mech. Engr., London, 1977, pp. 111–16.
J.M. Barsom:Int. J. Frac. Mech., 1971, vol. 7, pp. 163–82.
J.A. Smith, M.H. Peterson, and B.F. Brown:Corrosion, 1970, vol. 26, pp. 255–58.
G. Sandoz, C. T. Fujii, and B. F. Brown:Corr. Sci., 1970, vol. 10, pp. 839–45.
P. A. Parrish, K. B. Das, C. M. Chen, and E. D. Verink, Jr.:Effect of Hydrogen on Behavior of Materials, A. W. Thompson and I. M. Bernstein, eds., TMS-AIME, Warrendale, PA, 1976, pp. 169–81.
B.F. Brown:Stress Corrosion Cracking and Hydrogen Em- brittlement of Iron Base Alloys, J. Hockmann, J. Slater, R. D. McCright, and R. W. Staehle, eds., NACE, Houston, TX, 1976, pp. 747–50.
S. Suresh and R.O. Ritchie:Scripta Met., 1983, vol. 17, pp. 575–80.
R. van der Velden, H. L. Ewalds, and W. A. Schultze:Corrosion Fatigue: Mechanics, Metallurgy, Electrochemistry and Engineering, ASTM STP 801, T. W. Crooker and B. N. Leis, eds., ASTM, Phila- delphia, PA, 1983, pp. 64–80.
E. Bardai, J. M. SΦndenfor, and P. O. Gartland:Proc. Conf. Euro- pean Offshore Steel Research, Welding Institute, London, 1978, pp. 415–38.
B.F. Jones:J. Matl. Sci., 1982, vol. 17, pp. 499–507.
R.P. Gangloff:Fatigue Crack Growth Measurement and Data Analysis, ASTM STP 738, S. J. Hudak, Jr. and R. J. Bucci, eds., ASTM, Philadelphia, PA, 1981, pp. 120–38.
W. C. Hooper and W. H. Hartt:Corrosion, 1978, vol. 34, pp. 320–23.
W. H. Hartt and S.S. Rajpathak: Corrosion 83, Paper No. 62, NACE, Houston, TX, 1983.
M. Müller:Metall. Trans. A, 1982, vol. 13A, pp. 649–55.
D. W. Hoeppner:Fatigue Mechanisms, ASTM STP 675, J. T. Fong, ed., ASTM, Philadelphia, PA, 1979, pp. 841–70.
H.H. Lee and H.H. Uhlig:Metall. Trans., 1972, vol. 3, pp. 2949–57.
B.D. Craig and G. Krauss:Metall. Trans. A, 1980, vol. 11A, pp. 1799–807.
D.L. Williamson, R.G. Shupmann, J.P. Materkowski, and G. Krauss:Metall. Trans. A, 1979, vol. 10A, pp. 379–82.
F. Zia-Ebrahimi and G. Krauss:Metall. Trans. A, 1983, vol. 14A, pp. 1109–19.
1980 Annual Book of ASTM Standards, Part 10, E647-78T, ASTM, Philadelphia, PA, 1980, pp. 749–67.
G.R. Yoder, L. A. Cooley, and T. W. Crooker:Fatigue Crack Growth Measurement and Data Analysis, ASTM STP 738, S. J. Hudak, Jr. and R.J. Bucci, eds., ASTM, Philadelphia, PA, 1981, pp. 85–102.
R.P. Gangloff:Fat. Engr. Matl. Struc., 1981, vol. 4, pp. 15–31.
R. H. Van Stone, D. D. Krueger, and L. T. Duvelius:Fracture Me- chanics: I4th Symposium, ASTM STP 791, J.C. Lewis and G. Sines, eds., ASTM Philadelphia, PA, 1984, vol. II, pp. 553–78.
H. Tacta, P. C. Paris, and G. R. Irwin:The Stress Analysis of Cracks Handbook, Del Research Corp., St. Louis, MO, 1973, p. 2.10.
M. O. Speidel:High Temperature Materials in Gas Turbines, Am Elsevier Publ. Co., New York, NY, 1974, pp. 207–55.
E. J. Imhof and J. M. Barsom:Progress in Flaw Growth and Frac- ture Toughness Testing, ASTM STP 536, ASTM, Philadelphia, PA, 1973, pp. 182–205.
J.M. Barsom, E.J. Imhof, and S.T. Rolfe:J. Eng. Frac Mech., 1971, vol. 2, pp. 301–21.
R.J. Bucci:Fatigue Crack Growth Measurement and Data Analysis, ASTM STP 738, S.J. Hudak, Jr. and R.J. Bucci, eds., ASTM, Philadelphia, PA, 1981, pp. 5–28.
J. M. Barsom:Corrosion Fatigue, O. F. Devereux, A. J. McEvily, and R.W. Staehle, eds., NACE, Houston, TX, 1972, pp. 424–36.
S.J. Hidak, Jr. and R. P. Wei:Int. J. Pressure Vessels and Piping, 1981, vol. 9, pp. 63–74.
C. S. Carter: “Stress Corrosion Cracking and Corrosion Fatigue of Medium and High Strength Steels,” Boeing Company Report, Seattle, WA, 1977.
G. Sandoz: “High Strength Steels,” inStress Corrosion Cracking in High Strength Steels and in Titanium and Aluminum Alloys, B.F. Brown, ed., Naval Research Laboratory Report, Washington, DC, 1972.
H. E. Townsend, Jr.:Metall. Trans. A, 1975, vol. 6A, pp. 877–89.
P. N. Thielen and M. E. Fine:Metall. Trans. A, 1975, vol. 6A, pp. 2133–44.
O. Vosikovsky:Trans. ASME, 1975, vol. 97, pp. 298–304.
I. M. Austen and E. F. Walker:Proc Conf. Influence of Environment on Fatigue, Inst. Mech. Engr., London, 1977, pp. 1–10.
R. P. Gangloff: Exxon Research and Engineering Report CR.26BV.84, Annandale, NJ, 1984.
R. P. Gangloff:Embrittlement by the Localized Crack Environment, R. P. Gangloff, ed., TMS-AIME, Warrendale, PA, 1984, pp. 265–90.
C.L. Briant and S.K. Banerji:Met. Rev., Review 232, 1978, pp. 164–99.
R.P. Gangloff and R.P. Wei:Fractography in Failure Analysis, ASTM STP 645, B. M. Strauss and W. H. Cullen, Jr., eds., ASTM, Philadelphia, PA, 1978, pp. 87–106.
B.D. Craig:Metall. Trans. A, 1982, vol. 13A, pp. 907–12.
R.P. Wei and G.W. Simmons:Scripta Met., 1976, vol. 10, pp. 153–58.
P. M. Scott and D. R. V. Silvester: Tech Rep. UKOSRP 3/02, Harwell Corrosion Service, UKAEA, Harwell, 1977.
J. Congleton, I.H. Craig, B.K. Denton, and R.N. Parkins:Metal Sci., 1979, vol. 13, pp. 436–43.
R. Holder:Proc. Conf. Influence of Environment on Fatigue, Inst. Mech. Engr., London, 1977, pp. 37–41.
A. Turnbull: National Physical Laboratory Report, NPL DMA(D) 363, Teddington, 1983.
H. G. Nelson and D. P. Williams:Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Based Alloys, J. Hochmann, J. Slater, R. D. McCright, and R.W. Staehle, eds., NACE, Houston, TX, 1976, pp. 390–404.
P. M. Scott, T. W. Thorpe, and D. R. V. Silvester:Corr. Sci., 1983, vol. 23, pp. 559–75.
D. Tromans: Metall. Trans. A, 1981, vol. 12A, pp. 1445–53.
J. McBreen and M. A. Genshaw:Proc. Conf. Fundamental Aspects of Stress Corrosion Cracking, R.W. Staehle, A.J. Forty, and D. Van Rooyen, eds., NACE, Houston, TX, 1969, pp. 51–63.
W. W. Gerberich and A.G. Wright:Environmental DegrAadation of Engineering Materials in Hydrogen, M. R. Louthan, R.P. McNitt, and R. D. Sisson, eds., VPI Press, Blacksburg, VA, 1981, pp. 183–206.
R.P. Wei and Ming Gao:Scripta Met., 1983, vol. 17, pp. 959–62.
R. P. Gangloff: unpublished research, Exxon Research and Engineer- ing Company, Annandale, NJ, 1984.
S. Lynch:Advances in the Mechanics and Physics of Surfaces, R. M. Latanision and T. E. Fischer, eds., Harwood Academic Publishers, New York, NY, 1983, pp. 265–364.
J. Lankford:Fat. Engr. Math. Struc., 1983, vol. 6, pp. 15–31.
J. Lankford ;Fat. Engr. Math. Struc., 1982, vol. 5, pp. 233–48.
S. Suresh and R. O. Ritchie:Int. Met. Rev., 1984, in press.
P. Chauhan and B.W. Roberts:Metall. Matl. Tech., 1979, pp. 131–36.
S.J. Hudak, Jr., O. H. Burnside, and K.S. Chan: Offshore Tech- nology Conference Paper, OTC 4771, Houston, TX, 1984.
S.J. Maddox:Weld. Res. Suppl., 1974, vol. 53, pp. 401s-09s.
J. M. Hyzak and I. M. Bernstein:Metall. Trans. A, 1982, vol. 13A, pp. 34–43.
M. Kesten and K. F. Windgassen:Hydrogen Effects in Metals, I. M. Bernstein and A. W. Thompson, eds., TMS-AIME, Warrendale, PA, 1981, pp. 1017–25.
H. G. Nelson:Effect of Hydrogen on the Behavior of Materials, A.W. Thompson and I.M. Bernstein, eds., TMS-AIME, War- rendale, PA, 1977, pp. 602–11.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Gangloff, R.P. Crack size effects on the chemical driving force for aqueous corrosion fatigue. Metall Trans A 16, 953–969 (1985). https://doi.org/10.1007/BF02814848
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02814848