Recovery of quenched-in resistivity in doped gold

Summary

Changes in electrical resistivity of quenched gold wires, to which small amounts of silver, nickel, and antimony were added, have been studied in detail at annealing temperatures in the range (20÷170) ‡C. Some results with Ag-doped specimens were explained in a previous paper by assuming the formation of vacancy-impurity complexes whose binding energy is about 0.3 eV. The results with Ni-doped specimens are qualitatively similar but suggest a very small binding energy of the vacancy-Ni atom complex. Evidence of motion of defects is also obtained at low temperature. In the case of Sb-doped specimens different features are noticed, the deviations from the kinetics of vacancies in pure gold being more apparent for specimens containing small amounts of impurities than for more heavily doped specimens.

Riassunto

Le variazioni di resistività elettrioa dovute alla tempra di fili di oro, a cui erano state aggiunte piccole quantità di argento, nichel e antimonio, sono state studiate a temperature di rinvenimento comprese tra 20÷170 ‡C. Alcuni risultati ottenuti con campioni di oro contenenti argento vennero spiegati in un precedente lavoro ammettendo la formazione di complessi vacanza-atomo di impurità caratterizzati da una. energia di legame di circa 0.3 eV. I risultati relativi a campioni contenenti nichel sono qualitativamente simili ma suggeriscono una energia di legame molto piccola per il complesso vacanza-atomo di nichel. Anche a bassa temperatura è osservabile il moto dei difetti dovuti alla tempra. Nel caso di campioni contenenti impurità di antimoniosi notano caratteristiche diverse, le deviazioni dalla cinetica delle vacanze in oro puro essendo più evidenti per campioni contenenti piccole quantità di impurità che non. per i campioni contenenti maggiori concentrazioni di antimonio.