Crystal structure and resistivity studies on PrBa_{2 −x} Pr _x Cu₃O_{7 −y} oxide system

Abstract

The compound PrBa₂Cu₃O_{7 −y} is not superconducting while most other RBa₂Cu₃O_{7 −y} (R=rare earth) compounds exhibit superconductivity in the 90K range. The system PrBa_{2 −x} Pr _x Cu₃O_{7 −x} has been prepared to study the effect of excess Pr at the Ba site on the structure, resistivity and magnetic behaviour of this system. It is observed that single-phase compounds in the above series form forx=0·8—that is up to the composition Pr_1·8Ba_1·2Cu₃O_{7 −y} . While stoichiometric PrBa₂Cu₃O_{7 −y} is orthorhombic, the compounds with excess Pr show tetragonal structure. Four-probe dc resistivity measurements show that all the single-phase compounds in the above series do not exhibit superconductivity and are semiconducting down to 12 K. Magnetic susceptibility measurements reveal deviation from Curie-Weiss behaviour starting at a characteristic temperature, which is taken to be the ordering temperature (T _N ) of the Pr moments. BothT _N and overall resistivity decrease with increasingx and may have a common origin.