Abstract
Lead magnesium niobate (PMN) based binary with lead titanate (PT), lead iron niobate (PFN) and lead zinc niobate (PZN) and ternary with PZN-PT and PFN-PT solid solutions have been synthesized. In depth characterization using X-ray diffraction and SEM techniques have revealed the major perovskite phase formation. Amongst all the solid solutions, PMN-PZN-PT has given the highest values of permittivity as 19,740 and 23,700 withT c as 34°C when sintered at 1080°C and 1180°C respectively on the one hand and on the other, PFN containing solid solutions exhibited distinct deviation from the relaxor behaviour.
Similar content being viewed by others
References
Bokov V A and Mylnikova I E 1961Sov. Phys. Solid State 2 2428
Bouquin O and Lejeune M 1991J. Am. Ceram. Soc. 74 1152
Desgardin G, Bali H and Raveau B 1983Mater. Chem. & Phys. 8 469
Goldschmidt V M 1926Shrifter Norske Videnskaps-Akad. Oslo: Matemot. Naturuid. Klasse, No 2
Ichionse K and Kato N 1994J. Appl. Phys. 33 5423
Landin S M and Schulze W A 1990J. Am. Ceram. Soc. 73 913
Lejeune M and Boilot J P 1985Mater. Res. Bull. 20 493
Ravindranathan P, Komarneni S, Bhalla A and Roy R 1991J. Am. Ceram. Soc. 74 2996
Shrout T R and Halliyal A 1987Am. Ceram. Soc. Bull. 66 704
Singh K and Band S A 1996Ferroelectrics 175 193
Smolenskii G A and Agranovskaya A I 1959Sov. Phys. Solid State 1 1429
Swartz S L and Shrout T R 1982Mater. Res. Bull. 17 1245
Swartz S L, Shrout T R, Schulze W A and Cross L E 1984J. Am. Ceram. Soc. 167 311
Voss D J, Swartz S L and Shrout T R 1983Ferroelectrics 50 203
Wang H C and Schulze W A 1990J. Am. Ceram. Soc. 73 825
Yan M F, Ling H C and Rhodes W 1989J. Mater. Res. 4 930
Yokosuka M 1995Jpn J. Appl. Phys. 34 5338
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Singh, K., Band, S. A comparative study on the processing, dielectric and electrical properties of PMN based solid solutions. Bull Mater Sci 20, 265–277 (1997). https://doi.org/10.1007/BF02744897
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02744897