Abstract
Specimens of a nickel base superalloy were exposed to air at 1423 K to study the effect of gamma prime depletion in the near-surface region on the creep behaviour of the alloy. The results showed that the gamma prime depletion in the air-exposed specimens caused a weakening effect, leading to enhanced creep rate. Kachanov’s damage parameterf was determined and was found to be 0·5 indicating that the near-surface region, comprising of surface oxide, grain boundary oxide and gamma prime depleted region, carried a small fraction of the applied stress. It is further shown that the damaging effect is more pronounced in thinner specimens.
Similar content being viewed by others
References
Chang W H 1972Superalloys — Processing Sect. V AMIE MCIC-72-10
Dyson B F and Osgerby S 1987Mater. Sci. & Tech. 3 545
Kachanov L M 1958IZV Akad. Nauk SSSR 8 26
Pandey M C, Sharma K K and Satyanarayana D V V 1992Mater. at High Temp. 10 261
Pandey M C, Dyson B F and Taplin D M R 1984Proc. R. Soc. London A393 117
Pandey M C, Taplin D M R, Ashby M F and Dyson B F 1986Acta Metall. 34 2025
Pandey M C, Satyanarayana D V V and Rama Rao P 1991Mater. at High Temp. 9 167
Pandey M C 1996Trans. Indian Inst. Metals, Special Volume (in press)
Pandey M C and Taplin D M R 1984Proc. of the sixth international conference on fracture (eds) S R Valluri, D M R Taplin, P Rama Rao, J F Knott and R Dubey (Oxford UK: Permagon Press) p. 2287
Sundararajan G, Pandey M C and Rama Rao P 1992Mater. at High Temp. 10 227
Woodford D A and Bricknell R H 1983Treatize on mater. sci. and tech. (eds) C L Briant and S K Banerjee25 p. 157
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pandey, M.C., Satyanarayana, D.V.V. Effect of gamma prime depletion on creep behaviour of a nickel base superalloy (Inconel alloy X-750). Bull. Mater. Sci. 19, 1009–1015 (1996). https://doi.org/10.1007/BF02744633
Issue Date:
DOI: https://doi.org/10.1007/BF02744633