Abstract
Magnesium zinc ferrites with the general formula Mg x Zn(1 −x)Fe2O4 were prepared by the standard ceramic technology route involving double sintering. X-ray analysis was carried out to confirm the single-phase formation as well as to calculate the lattice parameters. Two sets of samples were prepared by sintering the samples at 1100°C for 15 and 30 h respectively. The high-field loop tracer was used to measure the hysteresis parameters. It is observed that the sintering conditions effectively modify the magnetization characteristics of these ferrites.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Broese van Groenou A, Bongers P F and Stuijts A L 1968/69Mater. Sci. Engg. 3 317
Evans B J and Hafnes S S 1969J. Phys. Chem. Solids 29 1573
Gorter E W 1954Philips Res. Rep. 9 321
Igarasi H and Okazaki K 1977J. Am. Ceram. Soc. (USA) 60 51
Jain G C, Das B K, Khanduja R S and Gupta G C 1976J. Mater. Sci. 11 4335
Jain G C, Das B K, Tripathi R B and Narayan R 1983J. Mater. Sci. 18 1583
Jonker G H and Stuijts A L 1971Philips Tech. Rev. 32 79
Josyulu O S, Sobhanadri J, Narayanaswamy A and Nagarajan T 1982Indian J. Pure Appl. Phys. 20 404
Kulkarni R G and Joshi H H 1985Solid State Commun. 53 1005
Kulkarni R G and Patil V U 1972J. Mater. Sci. 17 843
Likhite S D, Murthy C R K and Sahsrabudhe P W 1965Rev. Sci. Instrum. 36 1558
Naik A B and Powar J I 1985Indian J. Pure and Appl. Phys. 23 436
Patil S R 1988Studies on the physical properties of some magnesium-zinc ferrites, M. Phil. Thesis, Shivaji University, Kolhapur, 149
Patil V U and Kulkarni R G 1979Solid State Commun. 31 551
Rezlescu N 1970C. R. Acad. Sci. Ser. B (France) 270 18, 1134
Rezlescu N and Cuciureanu 1969C. R. Acad. Sci. B (France),269 19, 952
Rikukawa H 1982IEEE Trans. Magn. (USA) 18 1535
Rodrigue G P 1977 inTreatise on materials science (ed.) R K MacCrown (New York: Academic Press)
Sawant S R and Patil R N 1981Solid State Commun. 40 391
Smith W F 1986 inPrinciples of materials science and engineering, (New York: MacGraw-Hill) pp. 527
Smith J and Wijn H P J 1959Ferrites: Philips Technical Reports 144
Yafet Y and Kittle C 1954Phys. Rev. 9 295
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Patil, S.H., Patil, S.I., Kadam, S.M. et al. Effect of sintering on the magnetization behaviour of Mg x Zn(1 −x)Fe2O4 system. Bull. Mater. Sci. 14, 1225–1230 (1991). https://doi.org/10.1007/BF02744616
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02744616