Abstract
Magnetic hysteresis studies were carried out on Metglas 2605 Co(Fe67Co18B14Si1) samples, cut parallel and perpendicular to the ribbon axis and annealed at different temperatures. The samples annealed at 450°C for 2 hr show a coercive force of 8·75 Oe and 0·60 Oe in the parallel and perpendicular directions respectively. Electron probe micro analysis studies revealed the onset of primary crystallization at 400°C and a gradual displacement of B and Si from the lattice as the annealing temperature was increased to 450°C. The observed large coercive force is due to an increase in anisotropy resulting from an intergrowth pattern of the type Fe x Co1 −x , 0·3<x<1·0, including boron containing phases such as (FeCo)B, (FeCo)2B, (FeCo)3B, developed by the displacement of and Si from the original amorphous lattice.
Similar content being viewed by others
References
Allied Corporation 1981 Bulletin No. 15M-10/81 on Metglas electromagnetic alloys p 16
Baburaj E C, Dey G K, Patni M J and Krishnan R 1985Scr. Metall. 19 305
Beaman D R and Isasi J A 1972 Electron probe micro analysis: The fundamentals and applications, ASTM STP 506, Am. Soc. Test Mater. pp 23–28
Bhatnagar A K, Bhanuprasad B and Jagannathan R 1985J. Appl. Phys. 57 3514
Chaughule R S, Radhakrishnamurthy C, Sampathkumaran E V, Mallik S K and Vijayaraghavan R 1983Mater. Res. Bull. 18 817
Finney J L and Wallace J 1981Proc. Fourth Int. Conf. Rapidly Quenched Metals, (ed) T Masumoto and K Suzuki Sendai Japan p 253
Gray D E (ed.) 1963AIP Handbook (2nd edition) (New York: McGraw-Hill) Chapter 5 p 190
Haregawa R 1976AIP Conf. Proc. 29 216
Harold V and Koster U 1978Proc. Third Int. Conf. Rapidly Quenched Metals Brighton (ed) B Cantor1 281
Heinrich K F J 1981Electron beam micro analysis (New York: Van Nostrand) p 355
Mohri K 1984IEEE Trans. Mag. 20 942
Radhakrishnamurthy C, Lkhite S D and Sahasrabudhe P W 1978Proc. Indian Acad. Sci. (Earth Planet. Sci.) 87A 245
Rao C N R 1985Bull. Mater. Sci. 7 155
Sasada I, Hiroike A and Harada K 1984IEEE Trans. Mag. 20 951
Suja N T, Arai K I, Shiirija Y and Masumoto T 1975Phys. Lett. A51 121
Takacs L, Caderille M C and Vincze I 1975J. Phys. F5 800
Takahashi M, Ikeda N O and Miyazaki T 1976Jpn. J. Appl. Phys. 15 1821
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Varaprasad, A.M., Radhakrishnamurthy, C. Magnetic hysteresis and crystallization studies on metallic glass alloy Fe67Co18B14Si1 . Bull. Mater. Sci. 8, 567–575 (1986). https://doi.org/10.1007/BF02744356
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02744356