Abstract
Cd1−xZnxS/CuInSe2 solar cells having efficiencies in the range of 2·3% were fabricated by spray pyrolysis. The best cell had the following parameters:V oc = 305 mV,J sc = 32 mA/cm2, FF = 0·32 area = 0·4 cm2 and efficiency = 3·149%.V oc versus temperature measurements showed that the electron affinity difference was 0·22 eV. Forward dark current versus voltage curves were plotted and a possible current mechanism occurring in these cells has been proposed.
Similar content being viewed by others
References
Agnihotri O P, Raja Ram P, Thangaraj R and Sharma A K 1983Thin Solid Films 102 291
Chen W S and Mickelsen R A 1980Proceedings of the Society of Photo-optical Instrumentation Engineers, Bellingham, Washington p. 62
Hermann A, Zweibel K and Mitchell R 1984Proceedings of the 17th Photovoltaic Specialists Conference, IEEE, Florida
Ireland P J, Wagner S, Kazmerski L L and Hulstrom R L 1979Science 204 611
Kazmerski L L, White F R and Morgan G K 1976Appl. Phys. Lett. 29 268
Kazmerski L L, White F R, Ayyagari M S, Juang Y L and Patterson R P 1977J. Vac. Sci. Technol. 14 65
Kazmerski L L, Ireland P J, White F R and Cooper R B 1978Proc. 13th IEEE Photovoltaic Specialists Conference, Washington, 184
Mickelsen R A and Chen W S 1982Proc. 16th IEEE PVSC 781
Raja Ram P, Thangaraj R, Sharma A K and Agnihotri O P 1985Solar Cells 14 123
Shay J L, Wagner S, Bachmann K, Buchler E and Kasper H M 1975Proc. 11th IEEE PVSC, Phoenix, 503
Tell B, Shay J L and Kasper H M 1972J. Appl. Phys. 43 1972
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ram, P.R., Thangaraj, R. & Agnihotri, O.P. Thin film CdZnS/CuInSe2 solar cells by spray pyrolysis. Bull. Mater. Sci. 8, 279–284 (1986). https://doi.org/10.1007/BF02744133
Issue Date:
DOI: https://doi.org/10.1007/BF02744133