Optical constants ofε-GaSe

Summary

The optical constants for both polarizations of light (E‖C andE⊥C) in ε-GaSe have been studied between 30 cm⁻¹ and 22000 cm⁻¹, at room temperature. In the region of the band gap absorption edge, data are given down to 2 K. Infra-red data forE⊥C andE‖C in the (200÷300) cm⁻¹ range have been obtained by reflectivity measurements and Kramers-Krönig analysis. TheE⊥C polarization has been compared with interferometric measurements between 30 cm⁻¹ and 600 cm⁻¹. Verification for the high-frequency range (σ>300 cm⁻¹) has been done by comparison with interference patterns, analysed by the same method as for the visible region.

Riassunto

Si sono studiate fra 30 e 22000 cm⁻¹ a temperatura ambiente le costanti ottiche per entrambe le polarizzazioni della luce (E‖C edE⊥C) nel ε-GaSe. Si considerano i dati fino a 2 K nella regione di assorbimento fondamentale. Si sono ottenuti dati nell’infrarosso perE⊥C edE‖C nel campo (200÷300) cm⁻¹ per mezzo di misure di riflessione e di analisi di Kramers-Krönig. Si è confrontata la polarizzazioneE⊥C con misure interferometriche fra 30 e 600 cm⁻¹. Si è fatta una verifica per la regione di alte frequenze (σ>300 cm⁻¹) dal confronto con le figure di interferenza analizzate con un metodo uguale a quello usato per la regione visibile.

Резюме

Исследуются оптические постоянные для поляризации света (E‖C иE⊥C) в ε-GaSe в области от 30 до 22000 см⁻¹ при комнатной температуре. В области края полосы поглощения приводятся резуьтаты до 2 К. Получены инфракрасные данные дляE⊥C иE‖C в области (200÷300) см⁻¹ с помощью измерений козффициента отражения и анализа Крамерса-Кронига. ПоляризацияE⊥C сравнивается с интерферометрическими измерениями между 30 и 600 см⁻¹. Проведена проверка для области высоких частот (σ>300 см⁻¹) посредством сравнения с системой полос интерференции, применяя тот же метод анализа, что и с видимой области.