, Volume 2, Issue 4, pp 71–75 | Cite as

Rolling contact fatigue behavior of sintered and hardened steels

  • R. Gnanamoorthy
  • N. Rajiv
  • K. Gopinath
  • Y. Miyahsita
  • Y. Mutoh
Peer Reviewed Articles

Abstract

Powder-metal-processed bearings and gears are finding increasing application because of their economical and technical advantages. The residual pores from the sintering operatives act as lubricant pockets and dampen sound and vibration. However, porosity also decreases the mechanical strength and reduces the life of components fabricated by powder processing relative to similar wrought components. The rolling contact fatigue behavior of sintered and heat treated steel rollers was investigated using a fatigue test machine designed and fabricated for that purpose. The powder-metal-processed and the wrought steel rollers that were tested had similar composition and hardness and were mated against wrought steel rollers of high hardness. The contact stress versus number of cycles to failure data showed that the wrought steel had a very high endurance limit under rolling contact fatigue compared to the sintered steels investigated. Rolling contact fatigue behavior was found to depend on the porosity present in the material. Large surface peeling failures and pitting type fatigue failures were observed in the sintered and hardened steels, while only pitting type failures were observed in the wrought steels

Keywords

density failure analysis powder metallurgy steels rolling contact fatigue sintered and hardened 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    G.F. Bocchini: “The Influence of Porosity on the Characteristics of Sintered Materials,”Int. J. Powder Metall., 1986,22(3), pp. 185–200.Google Scholar
  2. 2.
    J. Holmes and R.A. Queeney: “Fatigue Crack Initiation in a Porous Steel,”Powder Metall., 1985,28(4), pp. 231–35.Google Scholar
  3. 3.
    P. Beiss and M. Dalgic: “Effects of Pore Structure on Bending Fatigue Strength of Sintered Steel,”Metal Powder Report, 1997,51(1), pp. 38–40.CrossRefGoogle Scholar
  4. 4.
    Y.T. Chen: “Fracture Toughness Testing of PM Materials,”Metal Powder Report, 1989,39, pp. 425–28.Google Scholar
  5. 5.
    W. Pompe, G. Leitner, K. Wetzig, G. Zies, and W. Grabner: “Crack Propagation and Processes Near Crack Tip of Metallic Sintered Materials,”Powder Metall., 1984,27, pp. 45–52.Google Scholar
  6. 6.
    R.C. Juvinall and K.M. Marshek:Fundamentals in Machine Design, John Wiley & Sons, New York, 1991, p. 331.Google Scholar
  7. 7.
    S. Way: “Pitting Due to Rolling Contact,” ASME,J. Appl. Mech., 1935,2, pp. A49–58.Google Scholar
  8. 8.
    W. Cheng, H.S. Cheng, L. M. Keet, and X. Li: “Surface Crack Initiation Under Contact Fatigue: Experimental Observation and Contact Analysis,”T. ASME J. Tribol., 1993,115, pp. 658–65.CrossRefGoogle Scholar
  9. 9.
    H. Salehinzadeh and N. Saka: “Crack Propagation in Rolling Line Contacts,”T. ASME J. Tribol., 1992,114, pp. 690–95.Google Scholar
  10. 10.
    C.A. Stickels: “Rolling Contact Fatigue Tests of 52100 Bearing Steel Using a Modified NASA Ball Test Rig,”Wear, 1984,98, pp. 199–210.CrossRefGoogle Scholar
  11. 11.
    L. Xiaogan, C. Quing, and S. Eryu: “Initiation and Propagation of Case Crushing Cracks in Rolling Contact Fatigue,”Wear, 1988,122, pp. 33–43.CrossRefGoogle Scholar
  12. 12.
    P.H. Dawson: “Effect of Metallic Contact on the Pitting of Lubricated Rolling Surfaces,”J. Mech. Eng. Sci., 1962,4(1), pp. 16–20.CrossRefGoogle Scholar
  13. 13.
    S. Marcela and A. Salak: “Durability and Failure of Powder Forged Rolling Bearing Rings,”Wear, 1999,236, pp. 47–54.CrossRefGoogle Scholar
  14. 14.
    A.W. Julia, P.D. Nurthen, and P.R. Brewin: “Rolling Contact Fatigue Testing of P/M High Speed Steels,”Int. J. Powder Metall., 1990,26, pp. 345–51.Google Scholar
  15. 15.
    K.L. Johnson:Contact Mechanics, Cambridge University Press, Cambridge, 1985.Google Scholar

Copyright information

© ASM International - The Materials Information Society 2002

Authors and Affiliations

  • R. Gnanamoorthy
    • 1
  • N. Rajiv
    • 1
  • K. Gopinath
    • 1
  • Y. Miyahsita
    • 2
  • Y. Mutoh
    • 2
  1. 1.Department of Mechanical EngineeringIndian Institute of Technology MadrasChennaiIndia
  2. 2.Department of Mechanical EngineeringNagaoka University of TechnologyNagaoka-shiJapan

Personalised recommendations