Convergent beam electron diffraction (CBED) is a powerful technique to estimate lattice distortion and lattice strain in crystals. The positions of the higher-order Laue-zone (HOLZ) lines in the transmitted disc of CBED patterns are very sensitive to the lattice parameter, and can therefore be used to estimate changes in the lattice parameter. This offers the possibility to calculate lattice misfit and lattice strain. The positions of the HOLZ lines depend not only on the lattice parameter, but also on the operating voltage of the microscope. It is essential to know the actual voltage of the microscope. In the present work, (1 0 0) GaAs crystal has been used as a standard. Cross-sectional TEM specimens were prepared by argon ion beam thinning technique using a liquid nitrogen cold stage. 〈0 1 2〉 on-zone CBED technique has been used to estimate the actual voltage of the transmission electron microscope (Philips EM430T TEM), when the voltage was set at 250 kV. CBED-HOLZ simulation and analyses have been done, using JEMS software, to correlate with the experimental data. The methodologies adopted for estimating the actual voltage of TEM are discussed in this paper. The studies have also been cross-checked using 〈0 1 2〉 and 〈2 3 3〉 zone axes using (1 0 0) silicon standard. The techniques established are found to be suitable for TEMs operating at a setting voltage of about 250 kV. For the TEM studies, a regular double-tilt specimen holder is required in order to be able to get to the desired zone axes. When the experiments were repeated using a cryogenic double-tilt holder, an improvement in the sharpness of HOLZ lines was observed. Wherever possible, the use of the cryogenic double-tilt holder is recommended. Care must, however, be taken to ensure that effects such as lattice parameter changes (due to temperature changes), phase transformations etc can be properly accounted for.
Similar content being viewed by others
References
Basile G, Bergamin A, Cavagnero G, Mana G, Vittone E and Zosi G 1994Phys. Rev. Lett. 72 3133
Harper Charles A 1970Handbook of materials and processes for electronics (New York: McGraw-Hill) pp 7–50
Jain S C, Harker A H and Cowley R A 1997Philos. Mag. A75 1461
LeGoues F K, Meyerson B S, Morar J F and Kirchner P D 1992J. Appl. Phys. 71 4230
Maher D M, Fraser H L, Humphreys C J, Knoell R V and Bean J C 1987Appl. Phys. Lett. 50 574
Service Manual for Philips EM430T TEM 1987Electronics (Netherlands: Philips) 9432 060 09001 422
Spence J C H and Zuo J M 1992Electron microdiffraction (New York: Plenum Press) p. 126
Sridhara Rao D V, Muraleedharan K and Dey G K 1999Proc. DAE-BRNS workshop on thin film multilayers (Mumbai: BARC) p. 30
Stadelmann P 2001Java Electron Microscopy Software (JEMS) (Switzerland: EPFL) Version 1.0724W2001
Toda Akio, Ikarashi Nobuyuki and Ono Haruhiko 2000J. Cryst. Growth 210 341
Zuo J M 1992Ultramicroscopy 41 211
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Rao, D.V.S., Balamuralikrishnan, R. & Muraleedharan, K. Accurate determination of the voltage of a transmission electron microscope (TEM) by 〈0 1 2〉 CBED-HOLZ analyses using GaAs crystal. Bull Mater Sci 27, 471–482 (2004). https://doi.org/10.1007/BF02708566
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02708566