Abstract
Aluminum was carefully anodized, then palladium salts were supported on its A12O3 surface layer by ion-exchange. CO 3.76 vol% contained in the air can be eliminated at around 200 °C. Both anodization conditions and the nature of the precursor solutions affect catalyst nature, particularly the pH value of the precursor solutions. The pH value of the solution suitable for supporting active components is 5–6. Palladium, which is present as Pd2+ and Pd4+ after calcination,distributes uniformly on the support surface which had a honeycomb structure.
References
Cybuski, A. and Monlijn, J. A., “Monoliths in Heterogeneous Catalysis”,Catal. Rev. Sci. Eng.,36(2), 279 (1994).
Diggle, J. W., Downie, T. C. and Goulding, C. W., “Anodic Oxide Films on Aluminum”,Chem. Rev.,69(3), 365 (1969).
Hönicke, D., “Formation of an Al2O3-coated Catalyst with a Metallic Core by Anodic Oxidation of Aluminum”,Applied Catal.,5, 179 (1983).
Hönicke, D., “Partial Oxidation of 1,3-Butadiene on V2O5/Al2O3/ Al-coated Catalysts: Effects of Pore Lengths on Product Selectivities”,J. Catal.,105, 19 (1987).
Irandust, S. and Anderson, B., “Monolithic Catalysts”,Catal. Rev. Sci. Eng.,30(3), 341 (1988).
Masuda, H. and Fukuda, K., “Ordered Metal Nanohole Arrays Made by a Two Step Replication of Honeycomb Structures of Anodic Alumina”,Science,268(9), 1466 (1995).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, XH., An, LD. Preparation of Pd/Al2O3/Al catalysts for CO removal. Korean J. Chem. Eng. 15, 563–565 (1998). https://doi.org/10.1007/BF02707111
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02707111