Pervaporation (PV) of water from HIx solution (HI-H2O-I2 mixture) using Nafion-117 was evaluated aiming at the application to dehydrate the azeotropic composition in HI decomposition reaction of thermochemical IS process. PV experiment was carried out by using HI solutions of 40–65 wt% and an I2/HI molar ratio of 0–3 in the feed at the room temperature. The permeation flux decreased with increasing HI weight fraction in the feed. The permeation flux is dependent on the I2 concentration in the feed having an I2/HI molar ratio. A long time PV experiment was carried out using I2/HI molar ratio of 1 (in HI solution of 55.9%) in the feed at room temperature. It is expected that the permeation component in the permeate zone using the PV process was mainly H2O, and H2O permeation was constant with increasing operation time.
Similar content being viewed by others
References
Hwang, G.-J., Onuki, K., Nomura, M., Kasahara, S. and Kim, J.-W., “Improvement of the thermochemical water-splitting IS (iodine-sulfur) process by electro-electrodialysis,”J. Membr. Sci.,220, 129 (2003).
Jonquieres, A., Clement, R., Lochon, P., Neel, J., Dresch, M. and Chretien, B., “Industrial state-of-the-art of pervaporation and vapour permeation in the western countries,”J. Membr. Sci.,206, 87 (2002).
Kang, M. S., Choi, Y J. and Moon, S. H., “Effect of charge density on water splitting at cation-exchange membrane surface in the over-limiting current region,”Korean J. Chem. Eng.,21, 221 (2004).
Kang, M. S., Tanioka, A. and Moon, S. H., “Effect of interface hydrophilicity and metallic compounds on water-splitting efficiency in bipolar membranes,”Korean J. Chem. Eng.,19, 99 (2002).
Nakajima, H., Ikenoya, K., Onuki, K. and Shimizu, S., “Closed cycle continuous hydrogen production test by thermochemical IS process,”Kagaku Kougaku Ronbunshu,24, 352 (1998).
Neel, J.,Introduction to pervaporation, in R. Y M. Huang (Ed.), Pervaporation Membrane Separations Process, Amsterdam (1991).
Norman, J. H., Besenbruch, G E. and O’keefe, D. R.,Thermochemical water-splittingfor hydrogen production, GRI-80/0105, March (1981).
Onuki, K., Hwang, G.-J., Arifal, Shimizu, S., “Electro-electrodialysis of hydriodic acid in the presence of iodine at elevated temperature,”J. Membr. Sci.,192, 193 (2001).
Onuki, K., Nakajima, H., Futakawa, M., Ioka, I. and Shimizu, S.,Thermochemical water-splittingfor hydrogen production, Proc. 8* Int. Topical Meeting on Nuclear Reactor Thermal-Hydraulics, Kyoto, Japan, Sep. 30 Oct. 4,1803 (1997).
Sakurai, M., Aihara, M., Miyake, N., Tsutusmi, A. and Yoshida, K., “Test of one-loop flow scheme for the UT-3 thermochemical hydrogen production process,”Int. J. Hydrogen Energy,17, 587 (1992).
Sakurai, M., Nakajima, H., Onuki, K. and Shimizu, S., “Investigation of 2-liquid phase separation characteristics on the iodine-sulfur thermochemical hydrogen production process,”Int. J. Hydrogen Energy,25, 605 (2000).
Song, K. H. and Lee, K. R., “Pervaporation of flavors with hydrophobic membrane,”Korean J. Chem. Eng.,22, 735 (2005).
Song, K. H., Hong, Y K., Yu, J. and Hong, W. H., “Influence of temperature drop by phase transition on pervaporation processes in vapor phase feed,”Korean J. Chem. Eng.,19, 290 (2002).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Choi, HS., Hong, SD., Hwang, GJ. et al. Dehydration through pervaporation from HIx solution (HI-H2O-I2 mixture) using a cation exchange membrane for thermochemical water-splitting iodine-sulfur process. Korean J. Chem. Eng. 23, 288–291 (2006). https://doi.org/10.1007/BF02705729
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02705729