Synthesis of Er³⁺ and Er³⁺ : Yb₃₊ doped sol-gel derived silica glass and studies on their optical properties

Abstract

Er₃₊ and Er₃₊ : Yb₃₊ doped optical quality, crack and bubble free glasses for possible use in making laser material have been prepared successfully through sol-gel route. The thermal and optical, including UV-visible absorption, FTIR etc characterizations were undertaken on the samples. The absorption characteristics of Er₃₊ doped samples clearly revealed the absorption due to Er₃₊ ions. On the other hand Yb₃₊ : Er₃₊ doped samples showed enhanced absorption due to² F _7/2 →² F _5/2 transition. The absorption and emission cross-section for² F _7/2 ↔² F _5/2 of Yb³⁺ were estimated. FTIR absorption spectra have clearly shown the reduction of the absorption peak intensity with heat treatment in the range 3700–2900 cm⁻¹. The 960 cm^-1 band also showed progressive decrease in the absorption band peak intensity with heat treatment. The result of the investigations with essential discussions and conclusions have been reported in this paper.