Abstract
The interface of Fe 3 Al/Q235 dissimilar materials joint, which was made by vacuum diffusion welding, combines excellently. There are Fe 3 Al, FeAl phases and α-Fe (Al) solid solution at the interface of Fe 3 Al/Q235. Aluminum content decreases from 28% to 1.5% and corresponding phase changes from Fe 3 Al with DO 3 type body centred cubic bcc structure to α-Fe (Al) solid solution with B2 type bcc structure. All phases are present in sub-grain structure level and there is no obvious brittle phases or micro-defects such as pores and cracks at the interface of Fe 3 Al/Q235 diffusion joint.
Similar content being viewed by others
References
David S A and Zacharia T 1993Welding J. 72 201
DavidS A et al 1989Welding J. 68 372
Ding Chenggang, Chen Chunhuan and Yin Yansheng 2000Welding 6 16
Fair G H and Wood J V 1994J. Mater. Res. 29 1935
Gao Dechunet al 2000Acta Metall. Sinica 36 87
He Kangsheng and Cao Xiongfu 1986Welding of dissimilar metals (Beijing: China Machine Press) p. 134
Mckameey C Get al 1991J. Mater. Res. 6 1779
Rabin B H, Wright J K, Wright R N and Sellers C H 1994J. Mater. Res. 9 1384
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Juan, W., Yajiang, L. & Huiqiang, W. Fine structure at the diffusion welded interface of Fe3Al/Q235 dissimilar materials. Bull Mater Sci 24, 639–642 (2001). https://doi.org/10.1007/BF02704013
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02704013