The change in the direction of the redox equilibrium Fe(II)=Fe(III) and S(IV)=S(VI) in glass melting upon introducing sodium silicofluoride as a melting catalyst is considered.
Similar content being viewed by others
References
H. Bach, G. K. Baukke, G. Bruckner, et al. (eds.),Types of Defects in Glass Production [in Russian], Stroiizdat, Moscow (1986).
Yu. A. Guloyan,Efficiency of Technological Processes in Production of Glass Articles [in Russian], Legkaya i Pishchevaya Prom-st’, Moscow (1982).
V. A. Barachevskii, G. I. Lashkov, and V. A. Tsekhomskii,Photochromy and Its Applications [in Russian], Khimiya, Moscow (1977).
S. P. Antonova, “The effect of accelerating additives for glass melting on spectral characteristics of tinted light filters.”Steklo Keram., No. 10, 14–15 (1987).
R. S. Zolotareva, N. I. Min’ko, V. A. Obrezan, et al., “On the effect of sodium silicofluoride in high-temperature melting of technical glass,”Steklo Keram., No. 7, 7–10 (1976).
É. K. Polokhlivets, V. I. Kiyan, and A. B. Atkarskaya, “Change in the glass composition in an operating furnace,”Steklo Keram., No. 11, 12–15 (1998).
D. S. Korzhinskii, “Acid-base interaction of the components in silicate melts and the direction of iotectic lines,”Dokl. Akad. Nauk SSSR,128(2), 383–386 (1959).
D. N. Kocharko, “The principle of chemical-bond polarity and its significance in the geochemistry of magnetism,”Geokhimiya, No. 9, 1286–1297 (1980).
Author information
Authors and Affiliations
Additional information
Translated from Steklo i Keramika, No. 3, pp. 5–7, March, 2000.
Rights and permissions
About this article
Cite this article
Kiyan, V.I., Mashir, Y.I. & Atkarskaya, A.B. Change in the redox potential of a glass melt upon introducing a melting catalyst into the glass batch. Glass Ceram 57, 78–80 (2000). https://doi.org/10.1007/BF02681512
Issue Date:
DOI: https://doi.org/10.1007/BF02681512