Abstract
Features of crystal-orientated transformations of the rhombohedral modification of boron nitride (rBN) into dense modifications of the wurtzite (wBN) and sphalerite (spBN) types with shock compression in the range from 15 to 50 GPa are studied. Three compression schemes are used: in annular ampules (∼15 GPa); in the ampules of K. M. Rabinin (25–35 GPa); in a plane shock wave (∼50 GPa). With an increase in pressure from 15 to 50 GPa and a corresponding change in the loading scheme the degree of rBN transformation into dense modifications increases from 0 to 40%. There is a change in the rBN transformation mechanism: from longitudinal bending of layers (as a result of which wBN forms, and spBN is formed from it) to corrugation leading to spBN formation directly from rBN.
Similar content being viewed by others
References
A. V. Kurdyumov and A. N. Pilyankevich,Phase Transformations in Carbon and Boron Nitride [in Russian], Nauk. Dumka, Kiev (1979).
A. V. Kurdyumov and N. F. Ostrovskaya, “Mechnism of forming superhard phases of carbon and boron nitride at high pressure,”Fiz. Tekh. Vysokikh Davlenii,2, No. 3, 5–18 (1992).
A. Onodera, K. Inoue, H. Joshihara, et al., “Synthesis of cubic boron nitride from rhombohedral form under high static pressure,”J. Mater. Sci.,25, 4279–4284 (1990).
A. V. Kurdyumov, V. F. Britun, V. B. Zelyavskii, and I. A. Petrusha, “Formation of the wurtzite modification from rhombohedral in pyrolytic boron nitride at high pressure,”Sverkhtverd. Mater., No. 4, 28–36 (1994).
A. V. Kurdyumov, V. F. Britun, and R. A. Petrusha, “Structual mechanisms of rhombohedral BN transformations into diamond-like phases,”Diam. and Relat. Mater.,5, 1129–1235 (1996).
V. L. Solozhenko, I. A. Petrusha, and B. O. Barb’e, “Kinetic boundary of the transformation rBN→wBN with high static pressure,”Sverkhtverd. Mater., No. 6, 62–69 (1996).
M. Ueno, K. Hasegawa, R. Oshima, et al., “Room-temperature transition of rhombohedral-type boron nitride under high static pressure,”Phys. Rev. B,45, No. 18, 10226–10230 (1992).
N. Sato, T. Ishii, and N. Setaka, “Formation of cubic boron nitride from rhombohedral boron nitride by explosive shock compression,”J. Amer. Ceram. Soc.,65, No. 10, 160–162 (1982).
T. Sekine and T. Sato, “Shock induced mechanisms of phase transformations from rhombohedral BN into cubic BN,”J. Appl. Phys.,74, No. 4, 2440–2444 (1993).
A. V. Kurdyumov, V. G. Malogolovets, N. V. Novikov, et al.,Polymorphic Modifications of Carbon and Boron Nitride: Handbook [in Russian], Metallurgiya, Moscow (1994).
V. L. Solozhenko, V. A. Mukhanov, and N. V. Novikov, “Reaction of ammonia and nitrogen and its compounds at high pressures and temperatures,”Doklady Chem.,312, No. 1-3, 125–127 (1990).
V. P. Alekseevskii, N. I. Borimchuk, N. A. Fot, and V. V. Yarosh, “Physical features of methods for creating high pulsed pressure by shock compression in order to obtain phase transition in solids,” in:Hexanite and Hexanite-R and Articles Based on Them for Tool Purposes [in Russian], Inst. Probl. Materials Sci., Acad. Sci. Ukrainian SSR, Kiev (1975).
V. I. Kovtun and V. I. Trefilov, “Phase composition, structure, and properties of spBN polycrystals sintered in shock waves,”Poroshk. Metall., No. 11, 85–90 (1989).
B. N. Sharupin, A. E. Kravchik, M. M. Efremenko, et al., “Analysis of the structure of pyrolytic boron nitride,”Zhurn. Prikl. Khim.,63, No. 8, 1698–1701 (1990).
A. V. Kurdyumov, V. B. Zelyavskii, N. F. Ostrovskaya, et al., “Features of the actual structure of graphite-like BN and its transformation into the wurtzite modification with shock compression,”Poroshk. Metall., Nos. 9-10, 62–66 (1994).
L. V. Al’tshuler, “Use of shock waves in high pressure physics,”Usp. Fiz. Nauk,85, No. 2, 197–258 (1965).
Additional information
Institute for Problems of Materials Science, Ukraine National Academy of Sciences, Kiev. Translated from Poroshkovaya Metallurgiya, Nos. 9-10(409), pp. 84–88, September–October, 1999.
Rights and permissions
About this article
Cite this article
Kurdyumov, A.V., Britun, V.F., Kovtun, V.I. et al. Phase transformations of the rhombohedral modification of boron nitride with shock compression. Powder Metall Met Ceram 38, 501–504 (1999). https://doi.org/10.1007/BF02676068
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02676068