Abstract
This investigation of liquid Fe-Ti-S alloys has involved experimental measurements of the titanium sulfide solubility product over the temperature range 1560 °C to 1640 °C. In addition, the sulfur-titanium interaction parameter was measured and the sulfide stoichiometry was determined. Using literature values for the sulfur and titanium self-interaction parameters, the solubility product for the equilibrium sulfide, TiS, was determined to be 0.411 at 1600 °C. The sulfur-titanium interaction parameter was determined to be −0.20 at 1600 °C. Comparisons with previously reported studies are presented.
Similar content being viewed by others
References
A. M. Portevin and R. Castro:J. Iron Steel Inst., 1937, vol. 135, pp. 223–39.
C. E. Sims, H. A. Saller, and F. W. Boulger:Trans. AFS, 1949, vol. 57, pp. 233–48.
E. J. Lichy, G. C. Duderstadt, and N. L. Samways:J. Met., 1965, vol. 17, pp. 769–75.
W. P. Fishel, W. P. Roe, and J. F. Ellis:J. Met., 1951, vol. 3, pp. 674–76.
A. Ejima, K. Suzuki, N. Harada, and K. Sanbongi:Trans. ISIJ, 1977, vol. 17, pp. 349–58.
S. Ban-ya and J. Chipman:Trans. AIME, 1969, vol. 245, pp. 133–43.
Z. Buzek: inChemical Metallurgy of Iron and Steel, Iron and Steel Inst., London, 1973, pp. 173–77.
M. N. Dastur and N. A. Gokcen:Trans. AIME, 1949, vol. 185, pp. 665–67.
K. Sanbongi:Trans. ISIJ, 1979, vol. 19, pp. 1–10.
D. R. Thomerson and W. J. Price:The Analyst, 1971, vol. 96, pp. 825–34.
Recommended Equilibrium Values for Steelmaking Reactions, E. Sawamura, ed., Japan Society for Promotion of Science, Nikkan Kogyu Shinbun, Tokyo, 1968.
J. F. Elliott and M. Gleiser:Thermochemistry for Steelmaking 1, Addison-Wesley Press, Boston, MA, 1963, p. 566.
Z. Buzek and V. Schindlerova:Vysoka Skola Banska Sbronik Vedekych Praci, 1965, vol. 11, pp. 405–07.
S. Ban-ya and J. Chipman:Trans. AIME, 1968, vol. 242, pp. 940–46.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Donahue, F.M., Pehlke, R.D. Equilibrium between sulfur and titanium in liquid iron. Metall Trans B 18, 681–685 (1987). https://doi.org/10.1007/BF02672884
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02672884