Abstract
A study of grain growth in dilute cadmium and lead base alloys has revealed that there are four stages of grain growth as a function of annealing temperature and solute concentration. One of these stages, which can result in a substantial change in grain size, involves irregular grain growth or secondary recrystallization.
Similar content being viewed by others
References
C. F. Boiling and W. C. Winegard:Acta Met., 1958, vol. 6, pp. 288–92.
E. L. Holmes and W. C. Winegard:Trans. TMS-AIME, 1962, vol. 224, pp. 945–949.
P. Niessen and W. C. Winegard:J. Inst. Metals, 1966, vol. 94, pp. 31–35.
B. Taylor, E. L. Holmes, and W. C. Winegard:Can. Met. Quart., 1962, vol. 1, pp. 187–92.
E. L. Holmes and W. C. Winegard:Can. J. Phys., 1961, vol. 39, pp. 1223–26.
C. J. Simpson and W. C. Winegard:Trans. TMS-AIME, 1969, vol. 245, pp. 431–432.
P. Gordon and R. A. Vandermeer:Trans. TMS-AIME, 1962, vol. 224, pp. 917–28.
J. W. Cahn:ActaMet, 1962, vol. 10, pp. 789–98.
E. S. Machlin:Trans. TMS-AIME, 1962, vol. 224, pp. 1153–67.
K. Lücke and H. P. Stüwe:Recovery and Recrystallization of Metals, pp. 171–209, Interscience, New York, 1963.
C. J. Beingessner: Ph.D. Thesis, University of Toronto, 1966.
C. S. Smith:Metal Interfaces, ASM, Cleveland, 1951, pp. 65–108.
C. J. Simpson, K. T. Aust, and W. C. Winegard:Met. Trans., 1970, vol. 1, pp. 1782–83.
C. J. Simpson, K. T. Aust, and W. C. Winegard:Met. Trans., 1971, vol. 2, p. 993.
G. F. Boiling: Ph.D. Thesis, University of Toronto, 1957.
P. Niessen: Ph.D. Thesis, University of Toronto, 1964.
K. T. Aust:Can. Met. Quart, 1969, vol. 8, pp. 173–78.
J. P. Stark and W. R. Upthegrove:ASM Trans. Quart., 1966, vol. 59, pp. 479–90.
J. B. Hudson and R. E. Hoffman:Trans. TMS-AIME, 1961, vol. 221, pp. 761–68.
H. Gleiter:Z. Metallic., 1970, vol. 61, no. 4, pp. 282–87.
Author information
Authors and Affiliations
Additional information
Formerly Graduate Student, University of Toronto.
Rights and permissions
About this article
Cite this article
Simpson, C.J., Aust, K.T. & Winegard, W.C. The four stages of grain growth. Metall Trans 2, 987–991 (1971). https://doi.org/10.1007/BF02664229
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02664229