Abstract
Guinier-Preston (GP) zones in an Al-1.7 at. pct Cu alloy aged at 383 K for 8000 minutes were analyzed by atom-probe field ion microscopy (AP-FIM). Layer-by-layer concentration profiles in the 〈100〉 direction were obtained from several GP zones. Generally, the GP zones were found to consist of several copper-enriched layers, with the highest measured concentration of copper in any of these layers being 50 at. pct. Although some uncertainty exists as to the copper content of the GP zones, these results appear to be inconsistent with the existence of layers that approach 100 pct copper. Some GP zones showed two well-separated copper-enriched regions; others showed a broad single peak in copper concentration. Therefore, it was concluded that aging at 383 K for 8000 minutes causes a transition from GP 1 to GP 2. The present results together with the previous atom-probe data indicate that there is a distinct stage for GP 2 zones which have two separated copper-enriched layers of 200 planes.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
V. Gerold:Z. Metallkd., 1954, vol. 45, pp. 599–607.
K. Toman:Acta Crystallogr., 1955, vol. 8, pp. 587–91.
K. Toman:Acta Crystallogr., 1960, vol. 13, pp. 60–61.
K. Doi:Acta Crystallogr., 1960, vol. 13, pp. 45–49.
D.R. James and G.L. Liedl:Acta Crystallogr., 1965, vol. 18, pp. 678–81.
E. Matsubara and J.B. Cohen:Acta Metall., 1985, vol. 33, pp. 1945-55 and 1957–69.
H. Yoshida, D.J.H. Cockayne, and J.J. Whelan:Phil. Mag., 1976, vol. 34, pp. 89–100.
M. Wada, H. Kita, and T. Mori:Acta Metall., 1985, vol. 33, pp. 1631–36.
X. Auvray, P. Georgopoulos, and J.B. Cohen:Acta Metall., 1981, vol. 29, pp. 1061–75.
V.A. Phillips:Acta Metall., 1973, vol. 21, pp. 219–28.
V.A. Phillips:Acta Metall., 1975, vol. 23, pp. 751–67.
H. Yoshida, H. Hashimoto, Y. Yokota, and N. Ajikita:Trans. JIM, 1983, vol. 24, pp. 378–85.
T. Sato and T. Takahashi:Trans. JIM, 1983, vol. 24, pp. 386–95.
M.J. Casanove, D. Dorgnac, and B. Jouffrey:Institute of Physics Conference Series, No. 31, pp. 337–80.
N. Ajikita, H. Endoh, H. Hashimoto, and M. Tomita:Phil. Mag., 1985, vol. 51, pp. 729–44.
A. Fontaine, P. Lagarde, A. Naudon, D. Raoux, and D. Spanjaard:Phil. Mag. B, 1979, vol. 40, pp. 17–30.
B. Lengeler and P.M. Eisenverger:Decomposition of Alloys; the Early Stages, P. Haasen, V. Gerold, R. Wagner, and M.F. Ashby, eds., Pergamon Press, Oxford, 1984, pp. 121–26.
T. Abe, K. Miyazaki, and K. Hirano:Acta Metall., 1982, vol. 29, pp. 357–66.
K. Hono, T. Satoh, and K. Hirano:Phil. Mag. A, 1986, vol. 53, pp. 495–504.
K. Osamura, N. Ohtsuka, and Y. Murakami:Phil. Mag. B, 1982, vol. 45, pp. 583–99.
P. Prieto, B. Lengeler, and D. Schwahn:Acta Metall., 1984, vol. 32, pp. 1439–45.
V. Gerold:Scripta Metall., 1988, vol. 22, pp. 927–32.
K. Hirano and H. Iwasaki:Trans. JIM, 1964, vol. 5, pp. 162–70.
J.M. Papazian:Metall. Trans. A, 1981, vol. 12A, pp. 269–80.
Y.M. Koo, M.E. Wall, L.E. Tanner, and J.B. Cohen:Scripta Metall., 1987, vol. 21, pp. 817–20.
K. Hono, T. Hashizume, Y. Hasegawa, K. Hirano, and T. Sakurai:Scripta Metall., 1986, vol. 20, pp. 487–92.
K. Hono, T. Hashizume, Y. Hasegawa, T. Satoh, K. Hirano, and T. Sakurai : Aluminum Alloys—Physical and Mechanical Properties, E.A. Starke, Jr. and T.H. Sandars, Jr., eds., EMAS, 1986, vol. 1, pp. 635–45.
D.R. Hess: Ph.D. Thesis, The Pennsylvania State University, University Park, PA, 1985.
O. Nishikawa, K. Kurihara, M. Nachi, M. Knishi, and M. Wada:Rev. Sci. Instrum., 1981, vol. 52, pp. 810–18.
Author information
Authors and Affiliations
Additional information
Formerly Graduate Student, Department of Materials Science and Engineering, The Pennsylvania State University
Rights and permissions
About this article
Cite this article
Hono, K., Sakurai, T. & Pickering, H.W. Atom-probe analysis of GP zones in an Al-1.7 At. pct Cu alloy. Metall Trans A 20, 1585–1591 (1989). https://doi.org/10.1007/BF02663192
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02663192