Abstract
The strength characteristics and microstructures of aged Ni−Mo alloys containing ordered (Ni4Mo) precipitates were studied as a function of aging time and temperature. It was found that 17 at. pct Mo alloy aged at 750°C produced a uniform dispersion of cuboidal β precipitates which coarsened with time producing a gradual increase in flow stress. The flow stress increment was found to vary in qualitative agreement with both order strengthening and coherency strain models. Both these models give over-estimates of the strengthening increment. A negative dependence of flow stress on temperature is attributed to coherency strain contributions.
Similar content being viewed by others
References
H. Gleiter and E. Hornbogen:Mater. Sci. Eng., 1968, vol. 2, p. 285.
S. M. Copley and B. H. Kear:Trans. TMS-AIME, 1967, vol. 239, p. 984.
H. Gleiter and E. Hornbogen:Z. Metallk., 1967, vol. 58, p. 157.
R. K. Ham:Proc. 3rd Bolton Landing Conf., B. H. Kear,et al., eds., p. 365. Claitors Publishing Div., Baton Rouge, La., 1970.
V. Gerold and H. Haberkorn:Phys. Status Solidi, 1966, vol. 16, p. 675.
J. M. Oblak, D. F. Paulonis, and D. S. Duvall:Met. Trans., 1974, vol. 5, p. 143.
D. F. Paulonis, J. M. Oblak, and D. S. Duvall:Trans. ASM, 1969, vol. 62, p. 611.
E. Ruedl, P. Delavignette, and S. Amelinck:Phys. Status Solidi, 1968, vol. 28, p. 305.
P. R. Okamoto and G. Thomas:Acta Met., 1971, vol. 19, p. 825.
P. V. Guthrie and E. E. Stansbury:Report ORNL-3078, Oak Ridge National Laboratory, Oak Ridge, Tenn., 1961.
V. A. Phillips:Phil. Mag., 1967, vol. 16, p. 103.
L. E. Tanner:Acta Met., 1972, vol. 20, p. 1197.
B. Chakravarti, E. A. Starke, and B. G. LeFevre:J. Mater. Sci., 1970, vol. 5, p. 394.
J. E. Spruiell and E. E. Stansbury:J. Phys. Chem. Solids, 1965, vol. 26, p. 811.
Fu-Wen Ling and E. A. Starke:Acta Met., 1971, vol. 19, p. 759.
C. K. H. Dubose and J. W. Steigler:Semi-Automatic Preparation of Specimens for TEM, ORNL-4066, 1967.
E. E. Underwood:Quantitative Stereology, Addison-Wesley Publishing Co., 1970.
L. R. Cornwell, J. D. Embur, and G. R. Purdy:Acta. Met., 1970, vol. 18, p. 1217.
M. Tamura, T. Mori, and T. Nakamura:J. Japan Inst. Metals, 1973, vol. 14, no. 5, p. 355.
I. J. Polmear:J. Aust. Inst. Metals, 1966, vol. 11, no. 4, p. 246.
A. Kelly and R. B. Nicholson:Progress in Material Science, vol. 10, no. 3, “Precipitation Hardening,” The MacMillan Co., 1963.
J. E. Spruiell: Unpublished research, University of Tennessee, Knoxville, Tenn., 1973.
A. Kelly and R. B. Nicholson:Strengthening Methods in Crystals, Elsevier Publishing Co., London, 1971.
A. J. Ardell and R. B. Nicholson:Acta. Met., 1966, vol. 14, p. 1295.
I. M. Lifshitz and V. W. Slyozov:J. Phys. Chem. Solids, 1961, vol. 19, p. 35.
B. T. Lampe: M.S. Thesis, University of Tennessee, Knoxville, Tenn., 1963.
J. W. Goodrum: Ph.D. Thesis, Georgia Institute of Technology, Atlanta, Ga., 1974.
R. K. Ham:Ref. 23,, p. 99.
W. F. Hosford and W. A. Backofen:Proc. of the 9th Sagamore Army Materials Research Conference, W. A. Backofen,et al., eds., Chapter X, Syracuse University Press, 1964.
P. B. Hirsch and F. J. Humphries:The Physics of Strength and Plasticity, A. S. Argon, ed., p. 189, MIT Press, 1969.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Goodrum, J.W., Lefevre, B.G. Strengthening by ordered precipitates in a Ni−Ni4Mo system. Metall Trans A 8, 939–943 (1977). https://doi.org/10.1007/BF02661576
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02661576