Abstract
The formation of a SiO2 layer at the Ta2O5/Si interface is observed by annealing in dry O2 or N2 and the thickness of this layer increases with an increase in annealing temperature. Leakage current of thin (less than 40 nm thick) Ta2O5 films decreases as the annealing temperature increases when annealed in dry O2 or N2. The dielectric constant vs annealing temperature curve shows a maximum peak at 750 or 800° C resulting from the crystallization of Ta2O5. The effect is larger in thicker Ta2O5 films. But the dielectric constant decreases when annealed at higher temperature due to the formation and growth of a SiO2 layer at the interface. The flat band voltage and gate voltage instability as a function of annealing temperature can be explained in terms of the growth of interfacial SiO2. The electrical properties of Ta2O5 as a function of annealing conditions do not depend on the fabrication method of Ta2O5 but strongly depend on the thickness of Ta2O5 layer.
Similar content being viewed by others
References
M. M. Hukovic and M. C. Ceric, Thin Solid Films.39, 145 (1986).
G. S. Oehrein and A. Reisman, J. Appl. Phys.54, 6502 (1983).
S. Roberts, J. Ryan and L. Nesbit, J. Electrochem. Soc.133, 1405 (1986).
S. I. Kimura, Y. Nishioka, A. Shintani and K. Mukai, J. Electrochem. Soc.130, 2414 (1983).
Y. Nishiok, N. Homma, H. Shinriki, K. Mukai, K. Yamaguchi, A. Uchida, K. Higeta and K. Ogiue, IEEE Trans. Electron Devices34, 1957 (1987).
G. S. Oehrien, F. M. d’Heurle and A. Reisman, J. Appl. Phys.53, 3715 (1984).
S. Zaima, T. Furuta and Y. Yasuda, J. Electrochem. Soc.137, 1297 (1990).
H. Shinriki and M. Nakata, IEEE Trans. Electron Devices38, 455 (1991).
K. Sayyah, The Physics and Chemistry of SiO2 and Si-SiO2 interface (Plenum press, New York 1988) p. 129.
T. Kato and T. Ito, J. Electrochem. Soc.135, 2586 (1988).
J. M. Walls, Methods of Surface Analysis (Cambridge University press, New York, 1987) p. 110.
P. Fazan, M. Dutoit, C. Martin and M. Ilegems, Solid-State Electron.30, 829 (1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Park, S.W., Baek, Y.K., Lee, J.Y. et al. Effects of annealing conditions on the properties of tantalum oxide films on silicon substrates. J. Electron. Mater. 21, 635–639 (1992). https://doi.org/10.1007/BF02655432
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02655432