Abstract
The substructures of thermally aged, creep deformed and fatigued 2.25 Cr-1 Mo steel have been studied using optical and transmission electron microscopy. In agreement with earlier work, the substructure of the proeutectoid ferrite was found to be very stable when exposed to thermal aging or creep deformation. This stability is explained based on the tendency of molybdenum atoms to form pairs in the ferrite matrix. Nucleation and growth of additional carbide particles during creep testing was not observed. The results of these creep tests and those of Klueh have been interpreted on the basis of Mo pair stability and the affinity between molybdenum and carbon. Fatigue tests at 866 K, however, did produce a fine Mou2C precipitate which contributed to secondary cyclic hardening in tests lasting longer than 200 h. The alloy was found to undergo early cyclic hardening followed by abrupt softening within the first tens of cycles.
Similar content being viewed by others
References
ORNL-5416, Oak Ridge National Laboratory, Oak Ridge, TN.
C. R. Brinkman, J. P. Strizak, M. K. Booker, and C. E. Jaske:J. Nucl. Mater., 1976, vol. 62, pp. 181–204.
R. L. Klueh:Mater. Sci. Eng., 1978, vol. 35, pp. 3–8.
R. G. Baker and J. Nutting:J. Iron Steel Inst., 1959, vol. 192, p. 257.
J. D. Baird and A. Jamieson:J. Iron Steel Inst., 1972, vol. 210, p. 841.
J. D. Baird and A. Jamieson:J. Iron Steel Inst., 1972, vol. 210, p. 847.
J. A. Van Den Avyle, W. B. Jones, and J. H. Gieske: Report No. SAND-77-1557, Sandia Laboratories, Albuquerque, NM, 1978.
K. F. Hale:Proceedings of the 4th Int. Conf. on Electron Microscopy, pp. 650–58, Springer-Verlag, Berlin, 1960.
K. F. Hale:Physical Metallurgy of Reactor Fuel Elements, pp. 193–201, The Metals Society, London, 1974.
R. H. Hiltz and L. H. Kirschler: Report No. MSAR69-139, MSA Research Corporation, Evans City, PA, 1969.
J. M. Leitnaker, R. L. Klueh, and W. R. Laing:Met. Trans. A, 1975, vol. 6A, p. 1949.
B. B. Argent, M. N. vanNiekerk, and G. A. Redfern:J. Iron Steel Inst., 1970, vol. 208, p. 830.
Y. Ishida and D. McLean:J. Iron Steel Inst., 1967, vol. 205, p. 88.
L. M. T. Hopkin:J. Iron Steel Inst., 1965, vol. 203, p. 583.
T. Gladman and F. B. Pickering:J. Iron Steel Inst., 1965, vol.203, p. 1212.
I. G. Ritchie and R. Rawlings:Acta Metall., 1967, vol. 15, p. 491.
R. B. Roy, B. Solly, and R. Wappling:Z. Metallkd., 1968, vol. 59, p. 563.
J.D. Baird.Jernkontorets.Ann., 1971, vol. 155, p. 311.
J. Friedet:Dislocations, p. 356, Pergamon Press, New York, 1967.
A. H. Cottrell and M. A. Jaswon:Proc. R. Soc, 1949, vol. A199, p. 104.
J. P. Hirth and J. Lothe:Theory of Dislocations, p. 605, McGraw-Hill, New York, 1968.
J. Askill:Tracer Diffusion data for Metals, Alloys, and Simple Oxides, IFI/Plenum, New York, 1970.
A. H. Cottrell:Dislocations and Plastic Flow in Crystals, p. 134, Oxford University Press, New York, 1953.
R. L. Klueh: Report No. ORNL-5219, Oak Ridge National Laboratory, Oak Ridge, TN, 1976.
J. B. Conway, R. H. Stentz, and J. T. Berling: U. S. AEC Report TID-26135, 1975.
H. Nahm, J. Moteff, and D. R. Diercks:Acta Metall., 1977, vol. 25, p. 107.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jones, W.B., Van Den Avyle, J.A. Substructure and strengthening mechanisms in 2.25 Cr-1 Mo steel at elevated temperatures. Metall Trans A 11, 1275–1286 (1980). https://doi.org/10.1007/BF02653481
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02653481