Abstract
High silicon-iron ribbons with 6.5 and 4.5 wt Pct silicon concentrations prepared by a rapid quenching roll technique were studied. As a result, a (100) cube-on-face texture was obtained by annealing at temperatures between 1050 °C and 1150 °C for ribbons with thickness below 130 µm. Minimum iron losses W12.5/50 obtained for 4.5 and 6.5 wt Pct ribbons were 0.51 and 0.34 W/kg, respectively.
Similar content being viewed by others
Reference
W.E. Ruder:Proc. IRE, 1942, vol. 30, p. 437.
N. Tsuya and K. I. Arai:Solid State Phys., 1978, vol. 13, p. 237 (in Japanese).
N. Tsuya and K. I. Arai:J. Appl. Phys., 1979, vol. 50, p. 1658.
K. I. Arai, N. Tsuya, and K. Ohmori:IEEE Trans. Magn., 1981, MAG- 17, p. 2857.
K.I. Arai, N. Tsuya, K. Ohmori, T. Matsuoka, and H. Shimanaka:IEEE Trans. Magn., 1982, MAG-18, p. 1418.
K. Narita, N. Teshina, Y. Mori, and M. Enokizono:IEEE Trans. Magn., 1981, MAG-17, p. 2857.
M. Wakamiya, Y. Hirota, H. Senno, and E. Hirota:Proc. 4th Int. Conf. on Rapidly Quenched Metals, Sendai, 1981, p. 1577.
J. L. Walter and C. G. Dunn:TMS-AIME, 1960, vol. 218, p. 914.
N. Tsuya and K. I. Arai:Chemistry and Physics of Rapidly Solidified Materials, TMS-AIME, 1982, p. 211.
Author information
Authors and Affiliations
Additional information
This paper is based on a presentation made at the symposium “Physical Metallurgy of Electrical Steels” held at the 1985 annual AIME meeting in New York on February 24–28, 1985, under the auspices of the TMS Ferrous Metallurgy Committee.
Rights and permissions
About this article
Cite this article
Arai, K.I., Ohmori, K. Grain growth characteristics and magnetic properties of rapidly quenched silicon steel ribbons. Metall Trans A 17, 1295–1299 (1986). https://doi.org/10.1007/BF02650110
Issue Date:
DOI: https://doi.org/10.1007/BF02650110