Properties of alumina-based coatings deposited by plasma spray and detonation gun spray processes

Abstract

Alumina, Al₂O₃ + 3 to 40 wt% TiO₂, and Al₂O₃ + 40 wt% ZrO₂ coatings were deposited by atmospheric plasma spraying (APS) and detonation gun spraying (DGS). The coatings were evaluated by optical microscopy, microhardness measurements, and X- ray diffraction. Wear resistance of the coatings was evaluated by rubber wheel sand abrasion and particle erosion test methods. Detonation gun- sprayed coatings exhibited more homogeneous microstructures and somewhat higher microhardness than corresponding plasma- sprayed coatings. Small additions of TiO₂ (3 wt%) improved both the abrasion and erosion wear resistance, whereas 40 wt% TiO₂ significantly decreased the erosion wear resistance of both APS and DGS coatings. Alumina + 40% ZrO₂ coatings exhibited the best abrasion wear resistance of both APS and DGS coatings, but the erosion wear resistance of these coatings was lower than that of the Al₂O₃ and Al₂O₃ + 3 wt% TiO₂ coatings. The best abrasion wear resistance of the coatings studied was obtained with DGS Al₂O₃ + 40 wt% ZrO₂ and Al₂O₃ + 3 to 40 wt% TiCh coatings. These coatings exhibited lower wear rates than bulk Al₂O₃. The best erosion wear resistance was obtained with the DGS Al₂O₃ + 3 wt% TiO₂ coating; however, it exhibited a higher wear rate than bulk Al₂O₃. In general, detonation gun- sprayed coatings showed significantly enhanced abrasion and erosion wear resistance than the corresponding plasma- sprayed coatings.