Abstract
The deformation behavior of commercially produced hot-dipped zinc and zinc-alloy coatings on steel under simple uniaxial tension has been studied. The strong basal plane texture of the hot-dipped galvanized coatings was found to be unfavorable for plastic flow and accounted for the extensive cracking observed during deformation. The eutectic structure in Galfan coatings was found to be beneficial in suppressing the formation of microcracks at low strain levels, although when grain boundary dents were present, cracks formed easily at these locations. Microcracks were observed in Galvalume coatings at all levels of strain. A technique to measure the coating plasticity has been developed to quantify the level of cracking in coatings at varying degrees of deformation.
Similar content being viewed by others
References
P.G. Partridge, The Crystallography and Deformation Modes of Hexagonal Close-Packed Metals,Mat. Metall. Rev., Vol 118, 1967,p 169
M.H. Yoo and C.T. Wei, Slip Modes of Hexagonal Close-Packed Metals,J. Appl. Phys., Vol 38, 1967, p 4317
N. Ecob and B. Ralph, Effect of Grain Size on Flow Stress of Textured Zn-Alloy,Met. Sci., Vol 17,1983, p 317
N.J. Wall, J.A. Spittle, and R.D. Jones, “The Deformation Characteristics of Zinc Coatings on Hot-Dip Galvanized Mild Steel Strip,” paper presented at the First Int. Conf. on Zinc-Coated Steel Sheet, Munich, 1985
J. Idris, S.R. Shah, J.A. Spittle, and R.D. Jones, “Cracking in Deformed Coated Strip,” paper presented at the Second Int. Conf. on Zinc-Coated Steel Sheet, Rome, 1988
R.M.S.B. Horta, W.T. Roberts, and D.V. Wilson, Texture Representation by Inverse Pole Figures,Trans. Metall. Soc. AIME, Vol 245, 1969, p 2525
J. Idris, Ph.D. thesis, University of Wales, 1989
D. Jaffrey, J.D. Browne, and T.J. Howard, The Cracking of Zinc Spangles on Hot-Dipped Galvanised Steel,Metall. Trans., Vol 11B, 1980, p 631
N.J. Wall, J.A. Spittle, and R.D. Jones, “The Crystallography of the Spangle of Hot-Dipped Galvanised Coatings on Mild Steel Strip,” paper presented at the First Int. Conf. on Zinc-Coated Steel Sheet, Munich, 1985
D. Jaffrey, J.D. Browne, and L.G. Lock-Lee, “On the Origin of Spangle Cracking,” paper presented at the Annual Conf. of the Int. Inst. of Welding, Australia, 1976
J. Pelerin, J.P. Servais, D. Coutsouradis, D.C. Herrschaft, and S.F. Radtke, Galfan: A New Zinc-Aluminum Coating,Proc. 13th Int. Galvan Conf., London, ZDA, 1982
M. Lamberigts, V. Leroy, M. Kuhn, and L. Renard, “Aluzinc Plus: A New Continuous Hot Dip 55% Al-Zn Protective Coating,” paper presented at the Second Int. Conf. on Zinc and Zinc Alloy Coated Steel Sheet (Galvatech ’92), Amsterdam, 1992
K.L. Lin, J.K. Ho, C.S. Jong, and J.T. Lee, Growth Behavior and Corrosion Resistance of 5% Al-Zn Coating,Corrosion, Vol 49 (No. 9), 1993, p 759
V. Rangarajan, N.M. Giallourakis, D.K. Matlock, and G. Krauss, The Effect of Texture and Microstructure on Deformation of Zinc Coatings,J. Mater. Shop. Technol., Vol 6, 1989, p 217
S.F. Radtke, Galfan—The Total Galvanising Alloy,Proc. Ann. Meeting Lead Ind. Assoc, Missouri, 1982, p 54
F.E. Goodwin, A.F. Skenazi, and R.F. Lynch, Corrosion Test Results and Application of Coil Coated Galfan,CIM Bull., Vol 80, 1987,p 115
G.J. Harvey, Structure and Corrosion Resistance of Zincalume Coatings,BHP Tech. Bull., Vol 25,1981, p 63
A. Humayun, “Roll-Forming of Metal Coated Sheet Steels,” paper presented at the European Coil Coating Association General Assembly, Venice, 1986
D.J. Willis, Cracking Characteristics of Zinc and Zinc-Aluminum Alloy Coatings,Proc. Int. Conf. on Zinc and Zinc-Alloy Coated Steel Sheet (Galvatech ’89), Tokyo, 1989, p 351
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shah, S., Dilewijns, J. & Jones, R. The structure and deformation behavior of zinc-rich coatings on steel sheet. JMEP 5, 601–608 (1996). https://doi.org/10.1007/BF02646089
Issue Date:
DOI: https://doi.org/10.1007/BF02646089