Abstract
As- received 2090 Al- Li hot- rolled plate was homogenized at 482 °C for 10 h and cold worked to 95% reduction in thickness. The rolling modes were varied. One group of samples was rolled longitudinally parallel to the hot- rolling direction, the second transversely to the rolling direction, the third at 45° to the rolling direction, and the fourth in all three modes. All four groups were subsequently annealed at 456 °C for 24 h. The effect of varying the rolling mode on the ductility and strength was studied by examining the kinetics of softening as a function of the annealing time. All the groups recrystallized in less than 1 h with a coarse, elongated grain structure. Although the strengths of the different groups were similar, the ductilities varied significantly.
Similar content being viewed by others
References
F.S. Lin, S.B. Chakrabortty, and E.A. Starke, Jr., Microstructure- Property Relationships of Two Al-3Li-2Cu-0.2Zr-XCd Alloys,Metall. Trans. A, Vol 13, March 1982, p 401–410
E.A. Starke, Jr. and ES. Lin, The Influence of Grain Structure on the Ductility of the Al-Cu-Li-Mn-Cd Alloy 2020,Metall. Trans. A, Vol 13, Dec 1982, p 2259–2269
W. Wang and M. Wells, Microstructure and Mechanical Behavior of Al-Li-Zr Alloys,Proceedings of Light-Weight Alloys for Aerospace Applications 11, TMS, 1991, p 189–202
L.S. Collier, K. Ranganathan, and T.H. Sanders, Jr., Recrystalli- zation Resistance in Al-Li Alloys Containing Zirconium,Proceedings of Light-Weight Alloys for Aerospace Applications II, TMS, 1991, p 141–155
K. Lucke and H.P. Stuwe, On the Theory of Impurity Controlled Grain Boundary Migration,Acta Met., Vol 19, 1971, p 1087–1099
J. Quattrocchi, D. Johansen, M. Obrien, N. Khankan, C. Ventura, D. Raizk, K. Zakharia, M. Rajabi, R. Archilla, D. Ruhl, H. Petel, K. Shin, C. Louie, E Fisher, and O.S. Es-Said, On the Transformation Characteristics of 2090 Al-Li Alloy,Proceedings of Light-Weight Alloys for Aerospace Applications II, TMS, 1991, p 107–140
ER. Fickett, A Review of Resistive Mechanisms in Aluminum,Cryogenics, Oct 1971, p 349–367
W.A. Dean, Effects of Alloying Elements and Impurities on Properties, inAluminum: Properties, Physical Metallurgy and Phase Diagrams, Vol 1, American Society for Metals, 1967, p 174–176
O.S. Es-Said and J.G. Morris, A Method to Calculate the Resistivity of Strip Cast 3000 Series Al Alloys Based on Their Nominal Solute Content,Proceedings of Nondestructive Characterization of Materials II, Plenum Press, 1986, p 271–279
P.L. Makin and W.M. Stobbs, Comparison of Recrystallization Behavior of an Al-Li-Zr Alloy with Related Binary Systems,Proceedings of Aluminum Lithium Alloys III, Institute of Metals, 1985, p 392–401
M. Goncalves and C. M. Sellars, Static Recrystallization after Hot Working of Al-Li Alloys,J. Phys., Vol 48 (No. C3), Suppl. 9, 1987,p 171–177
O.S. Es-Said, J.G. Morris, and R.J. De-Angelis, Effect of Extended Recovery on the Recrystallization Characteristics of Flash-Annealed Strip Cast 3004 Aluminum Alloy,Mater. Charact., Vol 30, 1993, p 113–125
B. Noble, S.J. Harris, and K. Harlow, Mechanical Properties of Al-Li-Mg Alloys at Elevated Temperatures,Proceedings of Aluminum-Lithium Alloys 11, TMS-AIME, 1984, p 65–77
I.G. Palmer, W.S. Miller, D.J. Lloyd, and M.J. Bull, Effect of Grain Structure and Texture on Mechanical Properties of Al-Li Base Alloys,Proceedings of Aluminum-Lithium Alloys III, Institute of Metals, 1985, p 565–575
C.W. Cho, B.A. Cheney, D.J. Lege, and J.I. Petit, Superplasticity of 2090 SPF Sheet at Hot Rolled Gauge,J. Phys., Vol 48 (No. C3), Suppl. 9, 1987, p 277–283
J. Wadsworth, I.G. Palmer, D.D. Crooks, and R.E. Lewis, Superplastic Behavior of Aluminum-Lithium Alloys,Proceedings of Aluminum-Lithium Alloys II, TMS-AIME, 1984, p 111–135
H. Yoshida, S. Shirano, Y. Baba, T. Tsuzuku, and A. Takahashi,J Phys., Vol 48 (No. C3), Suppl. 9,1987, p 269–275
E.A. Starke, Jr., T.H. Sanders, Jr., and I.G. Palmer, New Approaches to Alloy Development in the Al-Li System,J. Met., Aug 1981, p 24–33
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Es-Said, O.S., Fisher, F., Johansen, D. et al. The Effect of the Rolling Mode on the Recrystallization Behavior of 2090 Al- Li Alloy. JMEP 3, 292–299 (1994). https://doi.org/10.1007/BF02645855
Issue Date:
DOI: https://doi.org/10.1007/BF02645855